Microstructure and toughness of thick-gauge pipeline steel joint via double-sided friction stir welding combined with preheating

Fusion welding easily causes microstructural coarsening in the heat-affected zone(HAZ) of a thick-gauge pipeline steel joint. This is most significant in the inter-critically coarse-grained HAZ(ICCGHAZ), which considerably deteriorates the toughness of the joint. In the present work, 11-mm thick pipeline steel was joined by preheating and double-sided friction stir welding(FSW). A comparative study on the microstructure and toughness in the ICCGHAZs for FSW and gas metal arc welding(GMAW) was performed. The toughness in the ICCGHAZ for FSW was improved significantly than that in the ICCGHAZ for GMAW. Generally, the nugget zone(NZ) has a coarse microstructure in the FSW steel joint formed at the highest peak temperature. However, in the current study, the microstructure in the one-pass NZ was remarkably refined owing to the static recrystallization of ferrite. An excellent toughness was achieved in the NZ of the pipeline steel joint that employed FSW.

Effect of H_2S concentration on the corrosion behavior of pipeline steel under the coexistence of H_2S and CO_2

The effect of H2S concentration on H2S/CO2 corrosion of API-X60 steel was studied by scanning electron microscopy, a weight-loss method, potentiodynamic polarization tests, and the electrochemical impedance spectroscopy technique. It is found that the cor-rosion process of the steel in an environment where H2S and CO2 coexist at different H2S concentrations is related to the morphological structure and stability of the corrosion product film. With the addition of a small amount of H2S, the size of the anode reaction region is de-creased due to constant adsorption and separation of more FeS sediment or more FeHS＋ions on the surface of the steel. Meanwhile, the dou-ble-layer capacitance is diminished with increasing anion adsorption capacity. Therefore, the corrosion process is inhibited. The general cor-rosion rate of the steel rapidly decreases after the addition of a small amount of H2S under the coexistence of H2S and CO2. With a further increase in H2S concentration, certain parts of the corrosion product film become loose and even fall off. Thus, the protection provided by the corrosion product film worsens, and the corrosion rate tends to increase.

Effect of hydrogen on the stress corrosion cracking behavior of X80 pipeline steel in Ku'erle soil simulated solution

Hydrogen was a key factor resulting in stress corrosion cracking （SCC） of X80 pipeline steel in Ku＇erle soil simulated solution. In this article, the effect of hydrogen on the SCC susceptibility of X80 steel was investigated further by slow strain rate tensile test, the surface fractures were observed using scanning electron microscopy （SEM）, and the fracture mechanism of SCC was discussed. The results indicate that hydrogen increases the SCC susceptibility. The SEM micrographs of hydrogen precharged samples presents a brittle quasi-cleavage feature, and pits facilitate the transgranular crack initiation. In the electrochemical impedance spectroscopy （EIS） measurement, the decreased polarization resistance and the pitting resistance of samples with hydrogen indicate that hydrogen increases the dissolution rate and deteriorates the pitting corrosion resistance. The potentiodynamic polarization curves present that hydrogen also accelerates the dissolution rate of the crack tip.

Microstructure and Property of Coarse Grain HAZ X80 Pipeline Steel

The coarse grain HAZ microstructure and property of X80 pipeline steel with different carbon content was investigated. The weld thermal simulation test was carried out on Gleeble 1500 thermal mechanical test machine. The Charpy tests were completed at --20 ℃ for evaluating the toughness of coarse grain heat affected zone （CGHAZ）. The microstructure was examined by optical microscope （OM） and transmission electron microscopy （TEM）, and the austenite constituent was quantified by X-ray diffraction. The results showed that the ultra-low carbon can improve the toughness of CGHAZ by suppressing the formation of carbide, decreasing the martensite austenite （M-A） constituent and increasing the residual austenite in the M A.

Inclusion variations and calcium treatment optimization in pipeline steel production

SiCa line and SiCaBaFe alloy were injected into liquid pipeline steel at the end of LF refining as calcium treatment,and samples were taken from the ladles,mould,and slabs.Analysis of Ca content and inclusions shows that Ca content in steel decreases obviously in the following process after calcium treatment;the compositions,morphology,and sizes of inclusions also vary much in the production;primary inclusions in the ladles prior to calcium treatment are mainly Al2O3 inclusions,but they turn to fine irregular CaS-CaO-Al2O3 compound inclusions after the treatment,then become fine globular CaO-Al2O3 inclusions in the mould,and finally change to a few larger irregular CaS-CaO-Al2O3 complex inclusions in the slabs.Thermodynamic study reveals that inclusion variations are related with the preferential reactions among Ca,Al2O3,and S and the precipitation of S in CaO-Al2O3 inclusions with high sulfur capacity.New evaluation standards for calcium treatment in high-grade pipeline steel were put forward according to the inclusion variations and requirements of pipeline steel on inclusion controlling,and the calcium process was studied and optimized.

Effects of precipitates and inclusions on the fracture toughness of hot rolling X70 pipeline steel plates

In order to investigate the fracture toughness, crack tip opening displacement （CTOD） experiments were conducted on two X70 pipeline steel plates with different rolling processes. Atter the experiments, optical microscopy （OM）, scanning electron microscopy （SEM） and transmission electron microscopy （TEM） were employed to observe the microstructure and fracture morphology. The effects of precipi- tates on the fracture toughness and the crack initiation mechanism induced by inclusions were analyzed. The CTOD result shows that the steel with a lower finishing cooling temperature has a higher fracture toughness. Inchisiom with different shapes and two kinds of precipi- tates with different sizes were observed. It can be concluded that precipitates with different sizes have different effects and mechanisms on the fracture toughness. Distinguished fi＇om the earlier researches, inclusions enriched in silicon can be also served as the crack initiation.

STUDY OF THE X70 PIPELINE STEEL CORRODING IN 3.0wt% NaCl SOLUTION USING ELECTROCHEMICAL IMPEDANCE SPECTROSCOPY TECHNIQUE

The corrosion process of the X70 pipeline steel in 3.0wt% NaCl solution were studied using polarization method, and the chronological characteristics during the entire polarization plot were investigated in detail using EIS technique. In the active region of X70 steel, such as 20mV potential bias applied on open circuit potential (OCP), the impedance spectra was comprised of three parts: a high-frequency capacitive loop, a middle-frequency capacitive loop and a low-frequency inductive component. When positive polarization potential increased, the capacitive loops at high and middle frequency range merged, and the inductive component at low frequency shrunk. At high positive polarization potential bias (500-800mV vs. OCP), the high-frequency capacitive loop and the low-frequency inductive loop exhibited as disheveled points due to the synergism of the inhomogeneity of the corroding material and the localized corrosion. The results were fitted utilizing the equivalent circuits to simulate the impedance spectra and to interpret the electrochemical features shown during the experiments.

Experimental study on 830 MPa grade pipeline steel containing chromium

The diversity of microstructure and properties of 830 MPa grade pipeline steel containing chromium was investigated by optical microscope and transmission electron microscopy. The main microstructures were multiple configurations, containing lath bainite and granule bainitc. Mechanical properties test results showed that the yield strength and tensile strength improved with increasing chromium content. The toughness and elongation decreased at the same time, so temper process was introduced. Appling proper temper parameters, the values of toughness and elongation were improved dramatically, and the strength decreased slightly.

Influences of microstructure and texture on crack propagation path of X70 acicular ferrite pipeline steel

The aspects of two pipeline steels with different technologies were investigated by using transmission electron microscopy （TEM） and electron back-scattered diffraction （EBSD）. The microstructure presents a typical acicular ferrite characteristic with fine particles of martensite/austenite （M/A） constituent, which distributes in grains and at grain boundaries. The bulk textures of the pipeline steel plate are {112}〈110〉 and 〈111〉 fibers, respectively, and the {112}〈110〉 component is the favorable texture benefiting for drop weight tear test. Moreover, low angle boundaries and low coincidence site lattice boundaries are inactive and more resistant to fracture than high energy random boundaries.

Passivation process of X80 pipeline steel in bicarbonate solutions

The passivation process of X80 pipeline steel in bicarbonate solutions was investigated using potentiodynamic, dynamic electro-chemical impedance spectroscopy （DEIS）, and Mott-Schottky measurements. The results show that the shape of polarization curves changes with concentration. The critical ＇passive＇ concentration is 0.009 mol/L for X80 pipeline steel in bicarbonate solutions. No anodic current peak exists in solutions when the concentration is lower than 0.009 mol/L, whereas there are one and two anodic current peaks when the concentration ranges from 0.009 to 0.05 mol/L and is higher than 0.1 mol/L, respectively. DEIS measurements show that there exist active dissolution range, transition range, pre-passive range, passive layer formation range, passive range, and trans-passive range for X80 pipeline steel in the 0.1 mol/L solutions. The results of DEIS measurements are in complete agreement with the potentiodynamic diagram. An equivalent circuit containing three sub-layers is used to explain the Nyquist plots in the passive range. Analyses are well made for explaining the corresponding fitted capacitance and impedance. The Mott-Schottky plots show that the passive film of X80 pipeline steel is an n-type semiconductor, and capacitance measurements are in good accordance with the results of DEIS experiment.

Effects of welding wire composition and welding process on the weld metal toughness of submerged arc welded pipeline steel

The effects of alloying elements in welding wires and submerged arc welding process on the microstructures and low-temperature impact toughness of weld metals have been investigated. The results indicate that the optimal contents of alloying elements in welding wires can improve the low-temperature impact toughness of weld metals because the proeutectoid ferrite and bainite formations can be suppressed, and the fraction of acicular ferrite increases. However, the contents of alloying elements need to vary along with the welding heat input. With the increase in welding heat input, the contents of alloying elements in welding wires need to be increased accordingly. The microstructures mainly consisting of acicular ferrite can be obtained in weld metals after four-wire submerged arc welding using the wires with a low carbon content and appropriate contents of Mn, Mo, Ti-B, Cu, Ni, and RE, resulting in the high low-temperature impact toughness of weld metals.

Stress corrosion cracking of X80 pipeline steel exposed to high pH solutions with different concentrations of bicarbonate

Susceptibilities to stress corrosion cracking （SCC） of X80 pipeline steel in high pH solutions with various concentrations of HC03 at a passive potential of-0.2 V vs. SCE were investigated by slow strain rate tensile （SSRT） test. The SCC mechanism and the effect of HC03 were discussed with the aid of electrochemical techniques. It is indicated that X80 steel shows enhunced susceptibility to SCC with the concentration of HCO3 increasing from 0.15 to 1.00 mol/L, and the susceptibility can be evaluated in terms of current density at -0.2 V vs. SCE. The SCC behavior is controlled by the dissolution-based mechanism in these circumstances. Increasing the concentration of HCO3 not only increases the risk of rupture of passive films but also promotes the anodic dissolution of crack tips. Besides, little susceptibility to SCC is found in dilute solution containing 0.05 mol/L HCO3 for X80 steel. This can be attributed to the inhibited repassivation of passive films, manifesting as a more intensive dissolution in the non-crack tip areas than at the crack tips.

Hydrogen induced cracking of X80 pipeline steel

The hydrogen-induced cracking （HIC） behavior of X80 pipeline steel was studied by means of electrochemical charging, hydrogen permeation tests, tension test, and scanning electron microscopy （SEM）. The experimental results indicate that the increase of charging time and charging current density or the decrease of the solution pH value leads to an increase of the hydrogen content in X80 steel, which plays a key role in the initiation and propagation of HIC. It is found that the majority of macro-inclusions within the as-used X80 steel do not constitute a direct threat to HIC except aluminum oxides, which directly or indirectly lead to HIC. The hydrogen trap density at room temperature is estimated to be pretty high, and this is an essential reason why the steel is sensitive to HIC. After hydrogen charging, the elongation loss rate and area reduction of X80 steel decline obviously, taking a noticeable sign of hydrogen-induced plasticity damages. It is demonstrated that the losses of these plastic parameters have a linear relation to the fracture size due to hydrogen.

Precipitation behaviors of X80 acicular ferrite pipeline steel

The precipitation behaviors of X80 acicular ferrite pipeline steel were investigated by using transmission electron microscopy （TEM） and energy dispersive spectroscopy （EDS）. The results show that dendritic precipitates in the as-cast steel slabs precipitate mainly in grain boundaries, and these dendritic precipitates dissolve and re-precipitate to two kinds of carbonitrides： Ti- and Nb-rich （Ti, Nb）（C, N） carbonitrides during reheating. Four types of precipitates mainly exist in the hot rolled plate： Ti-rich carbonitrides resulted from the dendritic carbonitrides undissolved during the reheating process; Ti-rich carbonitrides re-precipitated along austenite grain boundaries during the re-heating process; NbC carbides mainly heterogeneously nucleated on the small pre-existing Nb-rich carbonitrides in the hot rolling process; and NbC carbides precipitated on dislocations during hot rolling.

Effect of Ca^(2+) on CO_2 corrosion properties of X65 pipeline steel

The effect of Ca^2＋ on CO2 corrosion to X65 pipeline steel was investigated in the simulated stratum water of an oil field containing different concentrations of Ca^2＋. It is found that Ca^2＋ can enhance the corrosion rate, especially in the Ca^2＋ concentration from 256 to 512 mg/L, which can be attributed to the growing grain size and loosing structure of corrosion scales with increasing Ca^2＋ concentration. X-ray diffraction （XRD） and X-ray photoelectron spectroscopy （XPS） investigations reveal that a complex carbonate （Fe, Ca）CO3 forms at high Ca^2＋ concentration due to the gradual replacement of Fe^2＋ in FeCO3 by Ca^2＋.

Effects of alternating current interference on corrosion of X60 pipeline steel

With rapid economic development in China, demand for energy and transportation is growing. Due to the limitations of factors such as terrain and traffic, a large number of buried oil and gas pipelines are parallel to high- voltage transmission lines and electrified railways over long distances. Alternating pipelines is very serious in laboratory experiments were current （AC） corrosion of such cases. In this work, carried out with an electrochemical method in a simulated soil solution at various AC current densities from 0 to 200 A]m2 and AC frequencies from 10 to 200 Hz. Experimental results indicated that with an increase in the AC current density, the corrosion po- tential of an X60 steel electrode shifted negatively, the anodic current density increased significantly, and the corrosion rate increased. Moreover, with an increase in the AC frequency, the corrosion potential of the X60 electrode shifted positively and the anodic current density decreased, which led to a decrease in the corrosion rate. Furthermore, the morphology of X60 electrodes indicated that uniform corrosion occurred at a low AC current density; while corrosion pits were found on the X60 electrode surface at a high AC current density, and deep corrosion pits seriously damaged the pipelines and might lead to leakage.

Effect of cooling temperature on the microstructure and corrosion behavior of X80 pipeline steel

Dual-phase accelerated cooling(DPAC) was applied to X80 pipeline steel to obtain its microstructure with different amounts of bainite and ferrite. The microstructure, hardness, and polarization behaviors of the steel, cooled to different temperatures, were investigated. Results showed that, with decreasing cooling temperature, the amount of polygon ferrite(PF) increased while that of acicular ferrite(AF) decreased. The amount of bainite correspondingly decreased, except when cooled to 760°C. Moreover, the grain size of ferrite increased. The corrosion behaviors of different phases were distinct. Martensite/austenite(M/A) islands presented at the grain boundary of the PF phase caused small pits. Numerous micro-corrosion cells were formed in the AF and bainite phases, where micropores were prone to form. X80 pipeline steel cooled to 700°C had the best corrosion resistance in the simulated seawater. The decreased amount of the PF phase reduced the area of cathode, resulting in slight corrosion. About 40 vol% of the bainite phase provided strength while the PF phase provided adequate ductility to the X80 steel. It was concluded that the appropriate cooling temperature was 700°C for ideal corrosion resistance and mechanical properties.

Precipitation behaviors of X70 acicular ferrite pipeline steel

The morphology, structure, and chemical composition of precipitates in the final microstructure of Nb-V-Ti microalloyed X70 acicular ferrite pipeline steel were investigated using transmission electron microscopy （TEM） and energy dispersive X-ray spectroscopy （EDS）. Precipitates observed by TEM can be classified into two groups. The large precipitates are complex compounds that comprise square-shaped TiN precipitate as core with fine Nb-containing precipitate nucleated on pre-existing TiN precipitate as caps on one or more faces at high temperature. In contrast, the fine and spherical Nb carbides and/or carbonitrides precipitate heterogeneously on dislocations and sub-boundaries at low temperature. From the analysis in terms of thermodynamics, EDS and chemical cornposition of the steel, NbC precipitation is considered to be the predominant precipitation behavior in the tested steel under the processing conditions of this research.

Effect of Nb on the dynamic recrystallization behavior of high-grade pipeline steels

The dynamic recrystallization （DRX） behavior of high-grade X80/X100 pipeline steels with different Nb contents was investi- gated through single pass compression experiment using a Gleeble 1500 thermomechanical simulator. By the regression of stress-sWain data obtained in the experiment, the deformation activation energy of DRX was identified, and the critical strain was calculated with the Po- liak-Jonas （P-J） method. Based on the analysis, the occurrence condition and kinetics of DRX were determined. The results show that as the Nb content increases from 0.08wt% to 0.095wt%, the activation energy of recrystallization raises from 365 to 395 kJ/mol. The critical swain of DRX can be determined more accurately by the P-J method, and the ratios of critical swain to peak sWain of XS0 and X100 pipeline steels are 0.51 and 0.49, respectively, which are similar to the results achieved by other researchers and calculated with empirical formulae.

Effects of laser heat treatment on the fracture morphologies of X80 pipeline steel welded joints by stress corrosion

The surfaces of X80 pipeline steel welded joints were processed with a CO2 laser, and the effects of laser heat treatment （LHT） on H2S stress corrosion in the National Association of Corrosion Engineers （NACE） solution were analyzed by a slow strain rate test. The fracture morphologies and chemical components of corrosive products before and after LHT were analyzed by scanning electron microscopy and energy-dispersive spectroscopy, respectively, and the mechanism of LHT on stress corrosion cracking was discussed. Results showed that the fracture for welded joints was brittle in its original state, while it was transformed to a ductile fracture after LHT. The tendencies of hydrogen-induced corrosion were reduced, and the stress corrosion sensitivity index decreased from 35.2% to 25.3%, indicating that the stress corrosion resistance of X80 pipeline steel welded joints has been improved by LHT.