S-doped Sb_2O_3 nanocrystals were synthesized using SbCl3 and thioacetamide(TAA) as starting materials by a hydrothermal method and the effects of TAA dosage on the composition and properties of resultant nanocrysta...S-doped Sb_2O_3 nanocrystals were synthesized using SbCl3 and thioacetamide(TAA) as starting materials by a hydrothermal method and the effects of TAA dosage on the composition and properties of resultant nanocrystals were determined.Their photocatalytic performance was evaluated using the degradation of methyl orange(MO) as a model reaction.The results suggest that TAA dosage can affect the preferential growth direction of Sb_2O_3,and further influences its photocatalytic activity.S doping can extend the optical absorption edge of Sb_2O_3 to the visible light religion,and thus endows its ability to photocatalyze the degradation of MO under visible light illumination.Based on these results,the correlations between the photocatalytic activity of S-doped Sb_2O_3 and the ratio between exposed facets,specific surface area and crystallographic defects were discussed.展开更多
基金supported by the National Natural Science Foundation of China(21307012)Educational Commission of Fujian Province(JK2013007,2014J01035,JA15138)
文摘S-doped Sb_2O_3 nanocrystals were synthesized using SbCl3 and thioacetamide(TAA) as starting materials by a hydrothermal method and the effects of TAA dosage on the composition and properties of resultant nanocrystals were determined.Their photocatalytic performance was evaluated using the degradation of methyl orange(MO) as a model reaction.The results suggest that TAA dosage can affect the preferential growth direction of Sb_2O_3,and further influences its photocatalytic activity.S doping can extend the optical absorption edge of Sb_2O_3 to the visible light religion,and thus endows its ability to photocatalyze the degradation of MO under visible light illumination.Based on these results,the correlations between the photocatalytic activity of S-doped Sb_2O_3 and the ratio between exposed facets,specific surface area and crystallographic defects were discussed.