A free standing film of polyaniline as large as 18 cm×18cm×0.002 cm can be obtained by evaporation of a solution of the chemically synthesized base in NMP. Its structure was examined by the elemental analysi...A free standing film of polyaniline as large as 18 cm×18cm×0.002 cm can be obtained by evaporation of a solution of the chemically synthesized base in NMP. Its structure was examined by the elemental analysis, IR, U.V.-visible spectra, XPS, DSC, SEM and X-ray scattering and its conducting behavior as well as electrochemical properties were studied. Results show that the composition, structure of main chain, physical properties of the free standing film of polyanilme is similar to that of the powder. However, some differences in its electronic structure, conductivity at room temperature and potential of redox couple between the flee standing film and powder are observed, which may be due to cross-linking of the film of polyaniline.展开更多
Free-standing film of polyaniline with excellent mechanical and electrical properties has been successfully prepared by using the solution-casting method. The results show that its tensile strength, Young's modulu...Free-standing film of polyaniline with excellent mechanical and electrical properties has been successfully prepared by using the solution-casting method. The results show that its tensile strength, Young's modulus and elongation at break are about 87.9 MPa, 1563.9 MPa and 10.2%, respectively. It is essential that the soluble polyaniline should be appropriately treated in some suitable organic solvents before making a free-standing film. Films having lustrous, smooth surface, high density and good flexibility can only be doped by protonic acids of small molecular sizes, such as HCl, HClO_4 and H_2SO_4, to the metallic conducting regime (σ=6.7 S/cm). Discussions have been made in terms of doping behavior essentially affecting drawability and mechanical strengths.展开更多
High quality free-standing poly（thiophene-3-acetic acid） （PTAA）, a water-soluble polythiophene derivative, was uccessfully electrosynthesized in boron trifluoride diethyl etherate （BFEE） ＋ 25% （by volume） tri...High quality free-standing poly（thiophene-3-acetic acid） （PTAA）, a water-soluble polythiophene derivative, was uccessfully electrosynthesized in boron trifluoride diethyl etherate （BFEE） ＋ 25% （by volume） trifluoroacetic acid （TFA） at 9wer potential （0.38 V versus Pt）. The carboxyl group makes PTAA highly soluble in water, facilitating its potential pplication as a blue-light-emitting material. PTAA films with conductivity of 7 S cm-1 obtained from this medium showed ,etter redox activity and thermal stability. The structure and morphology of the polymer were studied by UV-Vis, FT-IR, H-NMR spectra and scanning electron microscopy, respectively.展开更多
文摘A free standing film of polyaniline as large as 18 cm×18cm×0.002 cm can be obtained by evaporation of a solution of the chemically synthesized base in NMP. Its structure was examined by the elemental analysis, IR, U.V.-visible spectra, XPS, DSC, SEM and X-ray scattering and its conducting behavior as well as electrochemical properties were studied. Results show that the composition, structure of main chain, physical properties of the free standing film of polyanilme is similar to that of the powder. However, some differences in its electronic structure, conductivity at room temperature and potential of redox couple between the flee standing film and powder are observed, which may be due to cross-linking of the film of polyaniline.
基金Project supported by the National Natural Science Foundation of China.
文摘Free-standing film of polyaniline with excellent mechanical and electrical properties has been successfully prepared by using the solution-casting method. The results show that its tensile strength, Young's modulus and elongation at break are about 87.9 MPa, 1563.9 MPa and 10.2%, respectively. It is essential that the soluble polyaniline should be appropriately treated in some suitable organic solvents before making a free-standing film. Films having lustrous, smooth surface, high density and good flexibility can only be doped by protonic acids of small molecular sizes, such as HCl, HClO_4 and H_2SO_4, to the metallic conducting regime (σ=6.7 S/cm). Discussions have been made in terms of doping behavior essentially affecting drawability and mechanical strengths.
基金supported by the National Natural Science Foundation of China(No.50872042)the Natural Science Foundation of Shandong Province(No.Y2008B61)the Science and Technology Development Project of Shandong Province(No.2008GG1003024)
文摘High quality free-standing poly（thiophene-3-acetic acid） （PTAA）, a water-soluble polythiophene derivative, was uccessfully electrosynthesized in boron trifluoride diethyl etherate （BFEE） ＋ 25% （by volume） trifluoroacetic acid （TFA） at 9wer potential （0.38 V versus Pt）. The carboxyl group makes PTAA highly soluble in water, facilitating its potential pplication as a blue-light-emitting material. PTAA films with conductivity of 7 S cm-1 obtained from this medium showed ,etter redox activity and thermal stability. The structure and morphology of the polymer were studied by UV-Vis, FT-IR, H-NMR spectra and scanning electron microscopy, respectively.