Polybutylacrylate (PBA)/poly(methyl methacrylate) (PMMA) core-shell elastic particles (CSEP), whose rubbery core diameter ranged from 0.08 μm to 1.38μm, were synthesized by using conventional emulsion polymerization...Polybutylacrylate (PBA)/poly(methyl methacrylate) (PMMA) core-shell elastic particles (CSEP), whose rubbery core diameter ranged from 0.08 μm to 1.38μm, were synthesized by using conventional emulsion polymerization, multi-step emulsion polymerization, and soapless polymerization. Allyl methacylate (ALMA) and ethylene glycol dimethacrylate (EGDMA) were selected as crosslinking reagents for core polymerization. Methacrylic acid (MAA) was used as functional co-monomer with methyl methacrylate as shell component. The content of vinyl groups in PBA rubbery core increased with the amount of crosslinking reagents. The core-shell ratio affected great on the morphology of the complex particles. Furthermore, the amounts of carboxyl on the surface of core-shell particles, copolymerized with acrylic acid, were determined by potentiometric titration. Results showed that methylacrylic acid was distributed mostly on the surface of particles.展开更多
文摘Polybutylacrylate (PBA)/poly(methyl methacrylate) (PMMA) core-shell elastic particles (CSEP), whose rubbery core diameter ranged from 0.08 μm to 1.38μm, were synthesized by using conventional emulsion polymerization, multi-step emulsion polymerization, and soapless polymerization. Allyl methacylate (ALMA) and ethylene glycol dimethacrylate (EGDMA) were selected as crosslinking reagents for core polymerization. Methacrylic acid (MAA) was used as functional co-monomer with methyl methacrylate as shell component. The content of vinyl groups in PBA rubbery core increased with the amount of crosslinking reagents. The core-shell ratio affected great on the morphology of the complex particles. Furthermore, the amounts of carboxyl on the surface of core-shell particles, copolymerized with acrylic acid, were determined by potentiometric titration. Results showed that methylacrylic acid was distributed mostly on the surface of particles.
基金The financial supports by the National Natural Science Foundation of China(Grant:50133020.50273047)the Team Project of the Natural Science Foundation of Guangdong.China(Grant:20003038)the Key Program of the Science and Technology Department of Guangdong,China(Grant:2001A1070201)are acknowledged.