The flexural strengths and oxidative resistant properties of the ceramics derived from polycarbosilane and active fillers (Ti, TiH 2, TiB 2, Cr, and CrSi 2) were measured and characterized. The introduction of acti...The flexural strengths and oxidative resistant properties of the ceramics derived from polycarbosilane and active fillers (Ti, TiH 2, TiB 2, Cr, and CrSi 2) were measured and characterized. The introduction of active fillers enhances slightly the flexural strengths, and further densification is required to obtain higher strengths. The oxidative resistant behaviors of the specimens with active fillers are, by means of weight gain in air, poorer compared with those without active fillers.展开更多
The yttrium as a sintering aid was introduced into polycarbosilane（PCS） to prepare yttrium-containing PCS（PYCS）.Two types of yttrium-containing SiC fibres,the SiC（OY） fibres and the SiC（Y） fibres,were fabricat...The yttrium as a sintering aid was introduced into polycarbosilane（PCS） to prepare yttrium-containing PCS（PYCS）.Two types of yttrium-containing SiC fibres,the SiC（OY） fibres and the SiC（Y） fibres,were fabricated with PYCS.The structural evolution and the associated properties on changing from SiC（OY） to SiC（Y） fibres during the sintering process were studied.The chemical composition of the SiC（OY） fibres is SiC1.53O0.22Y0.005 with an amorphous structure.The composition of SiC（Y） fibres is SiC1.23O0.05Y0.005.The fibres are composed of a large number of β-SiC crystallites with a size of 50 nm and a small amount of α-SiC crystalline.The tensile strength and fracture toughness of the SiC（OY） fibres are 2.25 GPa and 2.37 MPa·m1/2,respectively,and 1.61 GPa,1.91 MPa·m1/2,respectively for SiC（Y） fibres.The SiC（Y） fibres have a higher thermal stability than the SiC（OY） fibres.展开更多
文摘The flexural strengths and oxidative resistant properties of the ceramics derived from polycarbosilane and active fillers (Ti, TiH 2, TiB 2, Cr, and CrSi 2) were measured and characterized. The introduction of active fillers enhances slightly the flexural strengths, and further densification is required to obtain higher strengths. The oxidative resistant behaviors of the specimens with active fillers are, by means of weight gain in air, poorer compared with those without active fillers.
基金Projects (51175444,50532010) supported by the National Natural Science Foundation of ChinaProject (2011121002) supported by the Fundamental Research Funds for the Central Universities, ChinaProject (2009J1009) supported by Scientific and Technological Innovation Platform of Fujian Province,China
文摘The yttrium as a sintering aid was introduced into polycarbosilane（PCS） to prepare yttrium-containing PCS（PYCS）.Two types of yttrium-containing SiC fibres,the SiC（OY） fibres and the SiC（Y） fibres,were fabricated with PYCS.The structural evolution and the associated properties on changing from SiC（OY） to SiC（Y） fibres during the sintering process were studied.The chemical composition of the SiC（OY） fibres is SiC1.53O0.22Y0.005 with an amorphous structure.The composition of SiC（Y） fibres is SiC1.23O0.05Y0.005.The fibres are composed of a large number of β-SiC crystallites with a size of 50 nm and a small amount of α-SiC crystalline.The tensile strength and fracture toughness of the SiC（OY） fibres are 2.25 GPa and 2.37 MPa·m1/2,respectively,and 1.61 GPa,1.91 MPa·m1/2,respectively for SiC（Y） fibres.The SiC（Y） fibres have a higher thermal stability than the SiC（OY） fibres.