The process of emulsifier-free copolymerization of the Styrene-Butyl Acrylate-K_sS_sO_s-water in the presence of Barium Sulfate(BS)powder was investigated under varied conditions within the range of BS powder quantity...The process of emulsifier-free copolymerization of the Styrene-Butyl Acrylate-K_sS_sO_s-water in the presence of Barium Sulfate(BS)powder was investigated under varied conditions within the range of BS powder quantity,initiator concentration and reaction temperature.Experimental results showed that the rate of polymerization is proportional to 0.3-power of the BS quantity and 1.3-power of the initiator concentration.There is a linear relationship of 2/3-power for the conversion and time.A process for the polymerization is propose to explain the experimental results.展开更多
Binary monomers of maleic acid and vinyl acetate are grafted onto poly(vinylidene fluoride) (PVDF) powder by pre-irradiation induced graft polymerization technique in emulsion solution. The co-grafting of binary monom...Binary monomers of maleic acid and vinyl acetate are grafted onto poly(vinylidene fluoride) (PVDF) powder by pre-irradiation induced graft polymerization technique in emulsion solution. The co-grafting of binary monomers is successfully proved by FT-IR spectroscopy analysis. The influences of the absorbed dose, reaction temperature, reaction time, total concentration of monomers, and feed ratio of binary monomers on the degree of grafting are investigated. The thermal property of grafted PVDF powder was characterized by differential scanning calorimetry (DSC) and thermo-gravimetry analysis (TGA).展开更多
An acrylic acid/kaoline powder superabsorbent composite with a water absorbency of the superabsorbent composite about 1/800 was synthesized by inverse\|suspending polymerization reaction between acrylic acid monomer a...An acrylic acid/kaoline powder superabsorbent composite with a water absorbency of the superabsorbent composite about 1/800 was synthesized by inverse\|suspending polymerization reaction between acrylic acid monomer and kaoline ultrafine powder. The influence of the dispersant agent on the configuration of the products in the inverse suspension polymerization is investigated. The influences of the kaoline powder,cross\|linker,initiator,neutralization degree and the volume ratio of oil to water phase on the water absorbency of the superabsorbent composites are discussed in the paper.展开更多
The emulsion polymerization of highly shear-stable copolymer dispersions of methyl methacrylate and butyl acrylate were carried out using poly （vinyl alcohol） with a thiol end group （PVA-SH） as protective colloid....The emulsion polymerization of highly shear-stable copolymer dispersions of methyl methacrylate and butyl acrylate were carried out using poly （vinyl alcohol） with a thiol end group （PVA-SH） as protective colloid. The dispersions can be transformed into corresponding redispersible powder via a spray dryingcooling process. On-line FT-IR monitoring shows that grafting polymer of PVA-g-PMMA was formed mainly at the stage-1 of the emulsion polymerization. TEM images show, the PVA-SH shell was fragmentary when adding SDS at initial stage and integrated when adding at particle growing or final stage. The particle size turns to be smaller when delayed adding SDS surfactant. Triethanolamine, a co-regulator of PVA-SH, controlled the M to 50 000-70 000 and reduced the PDI to 1.5-1.7. The acrylic dispersions with 0.8wt%-1.5wt% PVA-SH1 can be spray-dried into super dispersible polymer powder （SDPP）, which can easily disperse in water and form recon- stituted dispersions with an average particle size smaller than 1 micron.展开更多
Proton exchange membranes(PEMs)were prepared in three steps:grafting of polystyrene onto PVDF powder using pre-irradiation graft polymerization technique,processing the grafted PVDF powder into membranes of around 50-...Proton exchange membranes(PEMs)were prepared in three steps:grafting of polystyrene onto PVDF powder using pre-irradiation graft polymerization technique,processing the grafted PVDF powder into membranes of around 50-μm thickness,and sulfonating them with cholorosulfonic acid to form poly(vinylidene fluoride)-g-poly(styrene sulfonic acid)membranes.Kinetics of the graft polymerization was studied.The existing of polystyrene side-chains in the grafted PVDF powders,and PSSA groups in PEMs,were proved by FT-IR.Properties of the PEMs,i.e.the ion exchange capacity,water uptake,proton conductivity,thermal property and oxidative stability, were characterized.Dependence of properties on the degree of grafting was investigated,too.展开更多
文摘The process of emulsifier-free copolymerization of the Styrene-Butyl Acrylate-K_sS_sO_s-water in the presence of Barium Sulfate(BS)powder was investigated under varied conditions within the range of BS powder quantity,initiator concentration and reaction temperature.Experimental results showed that the rate of polymerization is proportional to 0.3-power of the BS quantity and 1.3-power of the initiator concentration.There is a linear relationship of 2/3-power for the conversion and time.A process for the polymerization is propose to explain the experimental results.
基金Supported by National Natural Science Foundation of China (11175234, 11105210)Knowledge Innovation Program of Chinese Academy of Sciences (KJCX2-YW-N49, XDA02040300)Shanghai Municipal Commission for Science and Technology (10ZR1436700, 11ZR1445400)
文摘Binary monomers of maleic acid and vinyl acetate are grafted onto poly(vinylidene fluoride) (PVDF) powder by pre-irradiation induced graft polymerization technique in emulsion solution. The co-grafting of binary monomers is successfully proved by FT-IR spectroscopy analysis. The influences of the absorbed dose, reaction temperature, reaction time, total concentration of monomers, and feed ratio of binary monomers on the degree of grafting are investigated. The thermal property of grafted PVDF powder was characterized by differential scanning calorimetry (DSC) and thermo-gravimetry analysis (TGA).
文摘An acrylic acid/kaoline powder superabsorbent composite with a water absorbency of the superabsorbent composite about 1/800 was synthesized by inverse\|suspending polymerization reaction between acrylic acid monomer and kaoline ultrafine powder. The influence of the dispersant agent on the configuration of the products in the inverse suspension polymerization is investigated. The influences of the kaoline powder,cross\|linker,initiator,neutralization degree and the volume ratio of oil to water phase on the water absorbency of the superabsorbent composites are discussed in the paper.
文摘The emulsion polymerization of highly shear-stable copolymer dispersions of methyl methacrylate and butyl acrylate were carried out using poly （vinyl alcohol） with a thiol end group （PVA-SH） as protective colloid. The dispersions can be transformed into corresponding redispersible powder via a spray dryingcooling process. On-line FT-IR monitoring shows that grafting polymer of PVA-g-PMMA was formed mainly at the stage-1 of the emulsion polymerization. TEM images show, the PVA-SH shell was fragmentary when adding SDS at initial stage and integrated when adding at particle growing or final stage. The particle size turns to be smaller when delayed adding SDS surfactant. Triethanolamine, a co-regulator of PVA-SH, controlled the M to 50 000-70 000 and reduced the PDI to 1.5-1.7. The acrylic dispersions with 0.8wt%-1.5wt% PVA-SH1 can be spray-dried into super dispersible polymer powder （SDPP）, which can easily disperse in water and form recon- stituted dispersions with an average particle size smaller than 1 micron.
基金Supported by National Natural Science Foundation of China(No.10875164 and No.10805070)Knowledge Innovation Program of the Chinese Academy of Sciences
文摘Proton exchange membranes(PEMs)were prepared in three steps:grafting of polystyrene onto PVDF powder using pre-irradiation graft polymerization technique,processing the grafted PVDF powder into membranes of around 50-μm thickness,and sulfonating them with cholorosulfonic acid to form poly(vinylidene fluoride)-g-poly(styrene sulfonic acid)membranes.Kinetics of the graft polymerization was studied.The existing of polystyrene side-chains in the grafted PVDF powders,and PSSA groups in PEMs,were proved by FT-IR.Properties of the PEMs,i.e.the ion exchange capacity,water uptake,proton conductivity,thermal property and oxidative stability, were characterized.Dependence of properties on the degree of grafting was investigated,too.