The novel polyoxometalate, 32[Mo8ⅣMo4ⅤV2ⅣO38(PO4)], was synthesized and characterized by elementary analysis, EPR, IR spectra and X ray diffraction. The compoundcrystallizes in triclinic system, space group with a=...The novel polyoxometalate, 32[Mo8ⅣMo4ⅤV2ⅣO38(PO4)], was synthesized and characterized by elementary analysis, EPR, IR spectra and X ray diffraction. The compoundcrystallizes in triclinic system, space group with a= 1.41999(2)nm, b=1.43467(2)nm, c=1.694610(10)nm, α=95.7250(10)°, β=92.2110(10)°, γ=92.6060(10)°, V=3.42829(7)nm3, Z=2, Dc=2.388g·cm-3, Mr=2465.10g·mol-1, μ=2.489mm-1, F(000)=2388, R1=0.0584, wR2=0.1461, S=1.164. The heteropolyanion is a bi capped pseudo Keggin complex. CCDC: 186645.展开更多
The thermal behavior of the complex Pr[(C5H8NS2)3(C12H8N2)] in a dry nitrogen flow was examined by TG-DTG analysis. The TG-DTG investigations indicated that Pr[(C5H8NS2)3-(C12H8N2)] was decomposed into Pr2S3 and depos...The thermal behavior of the complex Pr[(C5H8NS2)3(C12H8N2)] in a dry nitrogen flow was examined by TG-DTG analysis. The TG-DTG investigations indicated that Pr[(C5H8NS2)3-(C12H8N2)] was decomposed into Pr2S3 and deposited carbon in one step where Pr2S3 predominated in the final products. The results of non-isothermal kinetic calculations showed that the decomposition stage was the random nucleation and subsequent growth mechanism (n =nential constant In[A/s] was 7.8697. The empirical kinetics model equation was proposed as f(α) =3/2(1-α)[-ln(1-α)]1/3. The X-ray powder diffraction patterns of the thermal decomposition products at 800℃ under N2 atmosphere show that the product can be indexed to the cubic Pr2S3 phase. The transmission electron microscopy (TEM) of the final product reveals the particle appearance of a diameter within 40 nm. The experimental results show that the praseodymium sulfide nanocrystal can be prepared from thermal decomposition of Pr[(C5H8NS2)3(C12H8N2)].展开更多
文摘The novel polyoxometalate, 32[Mo8ⅣMo4ⅤV2ⅣO38(PO4)], was synthesized and characterized by elementary analysis, EPR, IR spectra and X ray diffraction. The compoundcrystallizes in triclinic system, space group with a= 1.41999(2)nm, b=1.43467(2)nm, c=1.694610(10)nm, α=95.7250(10)°, β=92.2110(10)°, γ=92.6060(10)°, V=3.42829(7)nm3, Z=2, Dc=2.388g·cm-3, Mr=2465.10g·mol-1, μ=2.489mm-1, F(000)=2388, R1=0.0584, wR2=0.1461, S=1.164. The heteropolyanion is a bi capped pseudo Keggin complex. CCDC: 186645.
基金supported by the National Natural Science Foundation of China(Grant No.20171036)Education Committee of Shannxi Province(No.01JK229)
文摘The thermal behavior of the complex Pr[(C5H8NS2)3(C12H8N2)] in a dry nitrogen flow was examined by TG-DTG analysis. The TG-DTG investigations indicated that Pr[(C5H8NS2)3-(C12H8N2)] was decomposed into Pr2S3 and deposited carbon in one step where Pr2S3 predominated in the final products. The results of non-isothermal kinetic calculations showed that the decomposition stage was the random nucleation and subsequent growth mechanism (n =nential constant In[A/s] was 7.8697. The empirical kinetics model equation was proposed as f(α) =3/2(1-α)[-ln(1-α)]1/3. The X-ray powder diffraction patterns of the thermal decomposition products at 800℃ under N2 atmosphere show that the product can be indexed to the cubic Pr2S3 phase. The transmission electron microscopy (TEM) of the final product reveals the particle appearance of a diameter within 40 nm. The experimental results show that the praseodymium sulfide nanocrystal can be prepared from thermal decomposition of Pr[(C5H8NS2)3(C12H8N2)].