PrCo5-based nanograin Pr=CO100-x （x=14-22） alloys with high coercivity were synthesized by mechanical alloying and subsequent annealing. The crystallization, phase components and magnetic properties of the alloys we...PrCo5-based nanograin Pr=CO100-x （x=14-22） alloys with high coercivity were synthesized by mechanical alloying and subsequent annealing. The crystallization, phase components and magnetic properties of the alloys were investigated systematically. The main phase of the alloy for x=14 is Pr2CO17 with rhombohedral Th2Zn17-type. The amount of the Pr2CO17 phase decreases with increasing Pr content, and a nearly single phase PrCo5 with hexagonal CaCu5-type is formed in Pr18Co81 alloy. Further increase in the Pr content leads to the formation of another magnetically hard Pr2Co7 phase with its Curie temperature about 350℃. Remanences decrease monotonously with increasing Pr content, whereas the coercivities increase, reaching a maximum of 2040 kA/m （25.6 kOe） in Pr19CO81 powders milled for 5 h and annealed at 973 K for 2 min, and then decrease for higher Pr content. The high coercivity is attributed to the high anisotropy field of the PrCo~ phase and its nanoscale grain size.展开更多
By introducing aparameter of difference in ferrite formation temperature between binary Fe-C and multicomponent system,and referring to the thermodynamic model for Fe-C binary system,a simplified thermodynamic model f...By introducing aparameter of difference in ferrite formation temperature between binary Fe-C and multicomponent system,and referring to the thermodynamic model for Fe-C binary system,a simplified thermodynamic model for pro-eutectoid ferrite formation in Fe-ΣXiC multicomponent structural steels(Xi=Mn,Si,Mo,Cr,Ni or Ti,etc)was suggested.The comparison of the calculated Ae3 temperatures with the measured data of steels 42 shows that the relative standard deviation and root-mean-square(RMS)error between them are only 0.71% and 8.92 K,respectively.However,the deviations between the same measured data and the values calculated from the superelement model are as high as 1.86% and 23.83 K,respectively.It can be concluded that the simplified thermodynamic model for pro-eutectoid ferrite formation in multicomponent structural steels is acceptable and the calculated Ae3 temperatures are in good agreement with the experimental data.展开更多
This paper is mainly about the spectral properties of a class of Jacobi operators(H_(c,b)u)(n)=c_(n)u(n+1)+c_(n-1)u(n-1)+b_(n)u(n),.where∣c_(n)−1∣=O(n^(−α))and b_(n)=O(n^(−1)).We will show that,forα≥1,the singula...This paper is mainly about the spectral properties of a class of Jacobi operators(H_(c,b)u)(n)=c_(n)u(n+1)+c_(n-1)u(n-1)+b_(n)u(n),.where∣c_(n)−1∣=O(n^(−α))and b_(n)=O(n^(−1)).We will show that,forα≥1,the singular continuous spectrum of the operator is empty.展开更多
基金This work was supported by the National Natural Science Foundation of China under Grant Nos.50331030 and 50071062 and 59725103.
文摘PrCo5-based nanograin Pr=CO100-x （x=14-22） alloys with high coercivity were synthesized by mechanical alloying and subsequent annealing. The crystallization, phase components and magnetic properties of the alloys were investigated systematically. The main phase of the alloy for x=14 is Pr2CO17 with rhombohedral Th2Zn17-type. The amount of the Pr2CO17 phase decreases with increasing Pr content, and a nearly single phase PrCo5 with hexagonal CaCu5-type is formed in Pr18Co81 alloy. Further increase in the Pr content leads to the formation of another magnetically hard Pr2Co7 phase with its Curie temperature about 350℃. Remanences decrease monotonously with increasing Pr content, whereas the coercivities increase, reaching a maximum of 2040 kA/m （25.6 kOe） in Pr19CO81 powders milled for 5 h and annealed at 973 K for 2 min, and then decrease for higher Pr content. The high coercivity is attributed to the high anisotropy field of the PrCo~ phase and its nanoscale grain size.
基金Item Sponsored by National Natural Science Foundation of China(50075053)
文摘By introducing aparameter of difference in ferrite formation temperature between binary Fe-C and multicomponent system,and referring to the thermodynamic model for Fe-C binary system,a simplified thermodynamic model for pro-eutectoid ferrite formation in Fe-ΣXiC multicomponent structural steels(Xi=Mn,Si,Mo,Cr,Ni or Ti,etc)was suggested.The comparison of the calculated Ae3 temperatures with the measured data of steels 42 shows that the relative standard deviation and root-mean-square(RMS)error between them are only 0.71% and 8.92 K,respectively.However,the deviations between the same measured data and the values calculated from the superelement model are as high as 1.86% and 23.83 K,respectively.It can be concluded that the simplified thermodynamic model for pro-eutectoid ferrite formation in multicomponent structural steels is acceptable and the calculated Ae3 temperatures are in good agreement with the experimental data.
文摘This paper is mainly about the spectral properties of a class of Jacobi operators(H_(c,b)u)(n)=c_(n)u(n+1)+c_(n-1)u(n-1)+b_(n)u(n),.where∣c_(n)−1∣=O(n^(−α))and b_(n)=O(n^(−1)).We will show that,forα≥1,the singular continuous spectrum of the operator is empty.