Pr_(83)Cu_(17)(wt%) grain boundary reconstruction was applied to prepare sintered NdFeB magnets. The effects of addition amount and annealing on the bending strength were investigated. The results show that Pr_(83)Cu_...Pr_(83)Cu_(17)(wt%) grain boundary reconstruction was applied to prepare sintered NdFeB magnets. The effects of addition amount and annealing on the bending strength were investigated. The results show that Pr_(83)Cu_(17) can not only effectively enhance the bending strength, but also change the mechanical anisotropy in two directions parallel and perpendicular to c-axis. The bending strength perpendicular to c-axis reaches 404 MPa in 10 wt% addition magnet, higher than 348 MPa along parallel direction. This change is attributed to the preferred distribution of boundary phases, i.e., ductile(Nd,Pr)-Fe-Cu phase along perpendicular direction to c-axis and(Nd,Pr)-Fe phase along parallel direction. Moreover, the Cu migration during 480 ℃ annealing is found to be related to this boundary phase distribution.展开更多
基金supported by National Natural Science Foundation of China(51401021)the State Key Laboratory Advanced Metals and Materials(20162-14)
文摘Pr_(83)Cu_(17)(wt%) grain boundary reconstruction was applied to prepare sintered NdFeB magnets. The effects of addition amount and annealing on the bending strength were investigated. The results show that Pr_(83)Cu_(17) can not only effectively enhance the bending strength, but also change the mechanical anisotropy in two directions parallel and perpendicular to c-axis. The bending strength perpendicular to c-axis reaches 404 MPa in 10 wt% addition magnet, higher than 348 MPa along parallel direction. This change is attributed to the preferred distribution of boundary phases, i.e., ductile(Nd,Pr)-Fe-Cu phase along perpendicular direction to c-axis and(Nd,Pr)-Fe phase along parallel direction. Moreover, the Cu migration during 480 ℃ annealing is found to be related to this boundary phase distribution.