Nanosized Gd2(1–x)Eu2xTi2O7:yV5+ phosphors were prepared via sol-gel method and characterized with X-ray diffraction,Raman spectroscopy,diffuse reflectance spectra and photoluminescence spectra.Their PL properties we...Nanosized Gd2(1–x)Eu2xTi2O7:yV5+ phosphors were prepared via sol-gel method and characterized with X-ray diffraction,Raman spectroscopy,diffuse reflectance spectra and photoluminescence spectra.Their PL properties were investigated as functions of the Eu3+ doping concentration and annealing temperature.The results indicated that the as-prepared samples showed a strong emission of Eu3+ under the irradiation of 303 nm.For Eu3+-doped Gd2Ti2O7,the orange emission at 586 nm was the strongest,which was correspond...展开更多
Ca2-xSrxZn4Ti15O36∶Pr red long decay phosphor was synthesized by high temperature solid state reaction. Photoluminescence property and crystalline and unit cell parameters of the orthorhombic were investigated by flu...Ca2-xSrxZn4Ti15O36∶Pr red long decay phosphor was synthesized by high temperature solid state reaction. Photoluminescence property and crystalline and unit cell parameters of the orthorhombic were investigated by fluorescence spectrophotometer and by powder X-ray diffraction, respectively. The emission intensity at 618 nm changes sharply when the concentration of Sr2+ （x） is less than 0.1 and the emission intensity reaches the maximum when x is equal to 0.007. There is an obviously broad excitation band at 270 nm when x is equal to 0.003 and it disappears gradually when x is over 0.01. The unit cell a parameter of Ca2-xSrxZn4Ti15O36∶Pr decreases while c parameter increases with the increases of the concentration of the doped Sr2+. When x is over 0.1 the value of the unit cell parameters a and c become stable. TL peaks of Ca2Zn4Ti15O36∶Pr, Ca1.993Sr0.007Zn4Ti15O36∶0.002Pr3+, 0.002Na+, are located at 62 ℃, 88 ℃, respectively, which indicates that there are deeper traps in Ca1.993Sr0.007Zn4 Ti15O36∶0.002Pr3+, 0.002Na+.展开更多
基金supported by Cultivating Innovative Talents for Colleges & Universities of Henan Province (2002006)Open Research Foundation of Henan University
文摘Nanosized Gd2(1–x)Eu2xTi2O7:yV5+ phosphors were prepared via sol-gel method and characterized with X-ray diffraction,Raman spectroscopy,diffuse reflectance spectra and photoluminescence spectra.Their PL properties were investigated as functions of the Eu3+ doping concentration and annealing temperature.The results indicated that the as-prepared samples showed a strong emission of Eu3+ under the irradiation of 303 nm.For Eu3+-doped Gd2Ti2O7,the orange emission at 586 nm was the strongest,which was correspond...
文摘Ca2-xSrxZn4Ti15O36∶Pr red long decay phosphor was synthesized by high temperature solid state reaction. Photoluminescence property and crystalline and unit cell parameters of the orthorhombic were investigated by fluorescence spectrophotometer and by powder X-ray diffraction, respectively. The emission intensity at 618 nm changes sharply when the concentration of Sr2+ （x） is less than 0.1 and the emission intensity reaches the maximum when x is equal to 0.007. There is an obviously broad excitation band at 270 nm when x is equal to 0.003 and it disappears gradually when x is over 0.01. The unit cell a parameter of Ca2-xSrxZn4Ti15O36∶Pr decreases while c parameter increases with the increases of the concentration of the doped Sr2+. When x is over 0.1 the value of the unit cell parameters a and c become stable. TL peaks of Ca2Zn4Ti15O36∶Pr, Ca1.993Sr0.007Zn4Ti15O36∶0.002Pr3+, 0.002Na+, are located at 62 ℃, 88 ℃, respectively, which indicates that there are deeper traps in Ca1.993Sr0.007Zn4 Ti15O36∶0.002Pr3+, 0.002Na+.