Pr^（3＋）-doped transparent oxyfluoride glass-ceramic containing tetragonal LiYF_4 nanocrystals has been synthesized by melting-quenching method and subsequent thermal treatment and spectroscopic properties of Pr^（...Pr^（3＋）-doped transparent oxyfluoride glass-ceramic containing tetragonal LiYF_4 nanocrystals has been synthesized by melting-quenching method and subsequent thermal treatment and spectroscopic properties of Pr^（3＋） ions were investigated. The crystalline phase and microstructure of the LiYF_4 nanocrystals were studied by X-ray diffraction（XRD） and transmission electron microscopy（TEM）, respectively. Compared with those of Pr^（3＋）-doped glass（Pr^（3＋）：PG）, the sharp absorption and emission bands of Pr^（3＋）-doped glass-ceramic（Pr^（3＋）：GC） reveal parts of Pr^（3＋） ions are incorporated into LiYF_4 nanocrystals. The peak absorption cross-section at 443 nm（~3H_4 → ~3P_2） adds to 110% and the full width at half maximum（FWHM） for the band around 443 nm reduces from 22 to 14 nm after crystallization. The fluorescence lifetime of the ~3P_0 multiplet of Pr^（3＋） ions increases from 5.35 to 11.14 μs after crystallization. The results indicate that this glass-ceramic is promising to be a visible laser material.展开更多
基金supported by the Strategic Priority Research Program of the Chinese Academy of Sciences(No.XDB20000000)
文摘Pr^（3＋）-doped transparent oxyfluoride glass-ceramic containing tetragonal LiYF_4 nanocrystals has been synthesized by melting-quenching method and subsequent thermal treatment and spectroscopic properties of Pr^（3＋） ions were investigated. The crystalline phase and microstructure of the LiYF_4 nanocrystals were studied by X-ray diffraction（XRD） and transmission electron microscopy（TEM）, respectively. Compared with those of Pr^（3＋）-doped glass（Pr^（3＋）：PG）, the sharp absorption and emission bands of Pr^（3＋）-doped glass-ceramic（Pr^（3＋）：GC） reveal parts of Pr^（3＋） ions are incorporated into LiYF_4 nanocrystals. The peak absorption cross-section at 443 nm（~3H_4 → ~3P_2） adds to 110% and the full width at half maximum（FWHM） for the band around 443 nm reduces from 22 to 14 nm after crystallization. The fluorescence lifetime of the ~3P_0 multiplet of Pr^（3＋） ions increases from 5.35 to 11.14 μs after crystallization. The results indicate that this glass-ceramic is promising to be a visible laser material.