Semi-solid Casting of High Speed Steel Ingots Using Inclined Slope Pre-crystallization Method 被引量:1
1
作者 和优锋 《Journal of Wuhan University of Technology(Materials Science)》 SCIE EI CAS 2009年第5期750-752,共3页
Semi-solid casting of M2 high speed steel ingots was investigated by inclined slope pre-crystallization method. Effects of casting temperature and slope length on the microstructure of M2 HSS ingots were investigated.... Semi-solid casting of M2 high speed steel ingots was investigated by inclined slope pre-crystallization method. Effects of casting temperature and slope length on the microstructure of M2 HSS ingots were investigated. M2 cast ingots of non-dendritic primary austenite and fine eutectic ledeburite network carbide structure were obtained, with the casting temperature, slope length and angle of 1480 ℃, 500 mm and 60° respectively. Meanwhile, the microstructure of cast samples was quantitatively assessed by Image tool software. Results show that optimum mean equivalent diameter of primary austenite crystal grain is 50.8 μm, shape factor is 0.83, and mean thickness of network carbide is 5.21 μm. 展开更多
关键词 M2 high speed steel SEMI-SOLID pre-crystalLIZATION inclined slope
下载PDF
Microstructure and magnetic properties of hot-deformed anisotropic Nd–Fe–B magnets prepared from amorphous precursors with different crystallization proportions 被引量:6
2
作者 Wei Zhao Ying Liu +2 位作者 Jun Li Ren-Quan Wang Yu-Chong Qiu 《Rare Metals》 SCIE EI CAS CSCD 2017年第4期268-276,共9页
Anisotropic magnets were obtained by hot deformation with the partial crystallized precursor prepared via spark-plasma sintering (SPS). Amorphous powders with the nominal composition of Nd_28.72Fe_balCo_5.66 Ga_0.59... Anisotropic magnets were obtained by hot deformation with the partial crystallized precursor prepared via spark-plasma sintering (SPS). Amorphous powders with the nominal composition of Nd_28.72Fe_balCo_5.66 Ga_0.59B_0.92 (wt%) were used as the starting material. The results show that the amorphous powders would suffer varying degrees of crystallization even below the crystal- lization point during the SPS process under high pressure. And the pre-crystallized grains in precursors have great impacts on the microstructure and magnetic properties of the hot-deformed magnets. The final obtained anisotropic magnets exhibit homogeneous microstructure consisting of well-aligned and platelet-shaped Nd_2Fe_14B grains without abnormal growth. It can be found that a reasonable pro- portion of pre-crystallized gains could promote the pref- erential orientation in the magnet, leading to the achievement of optimal magnetic properties among the magnets with identical composition and best magnetic performance is achieved in the magnet hot deformed from the 490 ℃ high-pressure hot-pressed precursor. 展开更多
关键词 Nd-Fe-B magnets Amorphous precursors pre-crystallized grains Hot deformation MICROSTRUCTURE