A bifunctional catalyst Pt/HY-β was prepared from a bimicroporous composite zeolite Y-β. Characterization results showed that the specific surface area, pore volume, and acid amount of the catalyst Pt/HY-β all decr...A bifunctional catalyst Pt/HY-β was prepared from a bimicroporous composite zeolite Y-β. Characterization results showed that the specific surface area, pore volume, and acid amount of the catalyst Pt/HY-β all decreased compared to the original zeolite. The catalytic performance of this catalyst in n-octane hydroisomerization was investigated in a fixed bed stainless steel tubular reactor. The results showed that at a hydrogen/n-octane volume ratio of 1000, pressure of 0.6 MPa, temperature of 230 ℃ and LHSV of 3 h^-1, the conversion of n-octane, yield of liquid, hydrocracking rate and yield of iso-octane were 52.32%, 88.66%, 12.60%, 39.51%, respectively.展开更多
基金sponsored by China Petroleumand Chemical Corporation(No.:090701)
文摘A bifunctional catalyst Pt/HY-β was prepared from a bimicroporous composite zeolite Y-β. Characterization results showed that the specific surface area, pore volume, and acid amount of the catalyst Pt/HY-β all decreased compared to the original zeolite. The catalytic performance of this catalyst in n-octane hydroisomerization was investigated in a fixed bed stainless steel tubular reactor. The results showed that at a hydrogen/n-octane volume ratio of 1000, pressure of 0.6 MPa, temperature of 230 ℃ and LHSV of 3 h^-1, the conversion of n-octane, yield of liquid, hydrocracking rate and yield of iso-octane were 52.32%, 88.66%, 12.60%, 39.51%, respectively.