As the basic protective element, steel plate had attracted world-wide attention because of frequent threats of explosive loads. This paper reports the relationships between microscopic defects of Q345 steel plate unde...As the basic protective element, steel plate had attracted world-wide attention because of frequent threats of explosive loads. This paper reports the relationships between microscopic defects of Q345 steel plate under the explosive load and its macroscopic dynamics simulation. Firstly, the defect characteristics of the steel plate were investigated by stereoscopic microscope(SM) and scanning electron microscope(SEM). At the macroscopic level, the defect was the formation of cave which was concentrated in the range of 0-3.0 cm from the explosion center, while at the microscopic level, the cavity and void formation were the typical damage characteristics. It also explains that the difference in defect morphology at different positions was the combining results of high temperature and high pressure. Secondly, the variation rules of mechanical properties of steel plate under explosive load were studied. The Arbitrary Lagrange-Euler(ALE) algorithm and multi-material fluid-structure coupling method were used to simulate the explosion process of steel plate. The accuracy of the method was verified by comparing the deformation of the simulation results with the experimental results, the pressure and stress at different positions on the surface of the steel plate were obtained. The simulation results indicated that the critical pressure causing the plate defects may be approximately 2.01 GPa. On this basis, it was found that the variation rules of surface pressure and microscopic defect area of the Q345 steel plate were strikingly similar, and the corresponding mathematical relationship between them was established. Compared with Monomolecular growth fitting models(MGFM) and Logistic fitting models(LFM), the relationship can be better expressed by cubic polynomial fitting model(CPFM). This paper illustrated that the explosive defect characteristics of metal plate at the microscopic level can be explored by analyzing its macroscopic dynamic mechanical response.展开更多
Sorbitol,triethanolamine,sodium benzoate,boric acid,and sodium carbonate were mixed to prepare a waterborne rust inhibitor.A temperature and humidity accelerated corrosion test was applied to investigate the corrosion...Sorbitol,triethanolamine,sodium benzoate,boric acid,and sodium carbonate were mixed to prepare a waterborne rust inhibitor.A temperature and humidity accelerated corrosion test was applied to investigate the corrosion behaviour of waterborne rust inhibitor coated Q235 steel and original Q235 steel,which was carried out in a temperature and humidity test chamber(WSHW-1000)at a temperature of 80℃and humidity of 95%.Compared with the original Q235,waterborne rust inhibitor coated Q235 has better resistance to corrosion in hot and humid ambient conditions.Electrochemical impedance spectroscopy and potentiodynamic polarization were measured with a three-electrode cell in 3.5%NaCl aqueous solution on a CHI760E potentiostat/galvanostat.Molecular dynamics was simulated to verify the synergistic corrosion inhibitory mechanism of sodium carbonate and triethanolamine.The test shows that the prepared waterborne rust inhibitor can reduce the tendency of Q235 to corrosion and can also effectively reduce the corrosion rate.展开更多
Since it has excellent tensile strength, the quenching and partitioning （Q ＆ P） treated steel has been widely acclaimed. Some researched is currently being conducted on Q ＆ P steel, but Q ＆ P techniques and relat...Since it has excellent tensile strength, the quenching and partitioning （Q ＆ P） treated steel has been widely acclaimed. Some researched is currently being conducted on Q ＆ P steel, but Q ＆ P techniques and related mechanisms have been mostly research based on conventional transformation-induced plasticity （TRIP） steel. This study researches the effect of Mn on the properties of Q ＆P sheet steel. Two kinds of steel sheet with different levels of Mn content （1.46% Mn and 2.75% Mn） are investigated. After being fully annealed, the steel sheets were quenched to a temperature between Ms and Mr. Allocation treatment then caused the carbon to be partitioned into the remaining austenite.The microstructure and tensile properties were analyzed. The results show that the increment of Mn content can increase the stability of the steel and decrease the sensitivity of the quenching temperature （QT）. The results also indicate that increasing the level of Mn can effectively suppress the formation of bainite.展开更多
基金Science and Technology Project of Fire Rescue Bureau of Ministry of Emergency Management(Grant No.2022XFZD05)S&T Program of Hebei(Grant No.22375419D)National Natural Science Foundation of China(Grant No.11802160).
文摘As the basic protective element, steel plate had attracted world-wide attention because of frequent threats of explosive loads. This paper reports the relationships between microscopic defects of Q345 steel plate under the explosive load and its macroscopic dynamics simulation. Firstly, the defect characteristics of the steel plate were investigated by stereoscopic microscope(SM) and scanning electron microscope(SEM). At the macroscopic level, the defect was the formation of cave which was concentrated in the range of 0-3.0 cm from the explosion center, while at the microscopic level, the cavity and void formation were the typical damage characteristics. It also explains that the difference in defect morphology at different positions was the combining results of high temperature and high pressure. Secondly, the variation rules of mechanical properties of steel plate under explosive load were studied. The Arbitrary Lagrange-Euler(ALE) algorithm and multi-material fluid-structure coupling method were used to simulate the explosion process of steel plate. The accuracy of the method was verified by comparing the deformation of the simulation results with the experimental results, the pressure and stress at different positions on the surface of the steel plate were obtained. The simulation results indicated that the critical pressure causing the plate defects may be approximately 2.01 GPa. On this basis, it was found that the variation rules of surface pressure and microscopic defect area of the Q345 steel plate were strikingly similar, and the corresponding mathematical relationship between them was established. Compared with Monomolecular growth fitting models(MGFM) and Logistic fitting models(LFM), the relationship can be better expressed by cubic polynomial fitting model(CPFM). This paper illustrated that the explosive defect characteristics of metal plate at the microscopic level can be explored by analyzing its macroscopic dynamic mechanical response.
基金Funded by Key Scientific Research Projects Plan of Henan Higher Education Institutions(No.19A460025)National Natural Science Foundation of China(No.51809127)。
文摘Sorbitol,triethanolamine,sodium benzoate,boric acid,and sodium carbonate were mixed to prepare a waterborne rust inhibitor.A temperature and humidity accelerated corrosion test was applied to investigate the corrosion behaviour of waterborne rust inhibitor coated Q235 steel and original Q235 steel,which was carried out in a temperature and humidity test chamber(WSHW-1000)at a temperature of 80℃and humidity of 95%.Compared with the original Q235,waterborne rust inhibitor coated Q235 has better resistance to corrosion in hot and humid ambient conditions.Electrochemical impedance spectroscopy and potentiodynamic polarization were measured with a three-electrode cell in 3.5%NaCl aqueous solution on a CHI760E potentiostat/galvanostat.Molecular dynamics was simulated to verify the synergistic corrosion inhibitory mechanism of sodium carbonate and triethanolamine.The test shows that the prepared waterborne rust inhibitor can reduce the tendency of Q235 to corrosion and can also effectively reduce the corrosion rate.
文摘Since it has excellent tensile strength, the quenching and partitioning （Q ＆ P） treated steel has been widely acclaimed. Some researched is currently being conducted on Q ＆ P steel, but Q ＆ P techniques and related mechanisms have been mostly research based on conventional transformation-induced plasticity （TRIP） steel. This study researches the effect of Mn on the properties of Q ＆P sheet steel. Two kinds of steel sheet with different levels of Mn content （1.46% Mn and 2.75% Mn） are investigated. After being fully annealed, the steel sheets were quenched to a temperature between Ms and Mr. Allocation treatment then caused the carbon to be partitioned into the remaining austenite.The microstructure and tensile properties were analyzed. The results show that the increment of Mn content can increase the stability of the steel and decrease the sensitivity of the quenching temperature （QT）. The results also indicate that increasing the level of Mn can effectively suppress the formation of bainite.