The structural and magnetic properties of Pr0.1CexTb0.9-xFe1.9 alloys were investigated by using X-ray diffraction, AC susceptibility, VSM and standard strain gauge techniques. The lattice parameter exhibits positive ...The structural and magnetic properties of Pr0.1CexTb0.9-xFe1.9 alloys were investigated by using X-ray diffraction, AC susceptibility, VSM and standard strain gauge techniques. The lattice parameter exhibits positive deviation from Vegard’s law with the increasing Ce content in the range of 0.40.6. Curie temperature decreases linearly with increasing Ce content. The saturation magnetization and magnetostriction decrease when 0.2≤x<0.4 and x>0.6, while abnormally increase with Ce content increasing from 0.4 to 0.6. These abnormal changes of （lattice） parameter, saturation magnetization and magnetostriction can be attributed to the valence fluctuation of Ce （ions.）展开更多
通过扫描电镜/能谱、X射线衍射以及金相分析,针对含0.3%Fe(质量分数)的Al Mg Si Cu铝合金,研究了Mn含量对其结晶相的影响。研究表明:合金在铸造过程中形成的结晶相为Al1.9CuMg4.1Si3.3,Al5(FeMn)Si,Al8(FeMn)2Si以及少量的Mg2Si;增大含M...通过扫描电镜/能谱、X射线衍射以及金相分析,针对含0.3%Fe(质量分数)的Al Mg Si Cu铝合金,研究了Mn含量对其结晶相的影响。研究表明:合金在铸造过程中形成的结晶相为Al1.9CuMg4.1Si3.3,Al5(FeMn)Si,Al8(FeMn)2Si以及少量的Mg2Si;增大含Mn量,合金中AlFeMnSi型结晶相数量增多;对合金进行均匀化处理时,Al1.9CuMg4.1Si3.3相完全溶解,发生Al5(FeMn)Si向Al8(FeMn)2Si相的转变;对合金进行轧制及最终热处理后,结晶相碎化且沿轧向呈纤维状分布,但结晶相的类型不变。展开更多
In this paper,the evolutions of microstructure and mechanical properties of Cu-l.9Be-0.3Ni-0.15Co alloy were studied.The alloys in the condition of the solution treated（soft state） and 37% cold rolled（hard state） ...In this paper,the evolutions of microstructure and mechanical properties of Cu-l.9Be-0.3Ni-0.15Co alloy were studied.The alloys in the condition of the solution treated（soft state） and 37% cold rolled（hard state） were aged at 320 ℃for different time,respectively.The mechanical properties,electrical conductivity and microstructure of the alloy aged for different time were analyzed.Additionally,the precipitation kinetics of Cu-1.9Be-0.3Ni-0.15Co alloys was investigated.X-ray diffraction and transmission electron microscopy results reveal that both continuous precipitation and discontinuous precipitation existed in the hard-state Cu-l.9Be-0.3Ni-0.15Co alloy during the whole aging process;the sequence of continuous precipitation is G.P.zone →γ″→γ′→γ.Furthermore,the precipitation transformation mechanism of softstate alloy is homogeneous nucleation,while hard-state alloy shows the heterogeneous nucleation（interface nucleation）with the nucleation rate of both states decaying rapidly to zero during aging at 320 ℃.展开更多
基金Project(50271023) supported by the National Natural Foundation Science Foundation of China Project(02017) suppor ted by Key Foundation of Education Ministry
文摘The structural and magnetic properties of Pr0.1CexTb0.9-xFe1.9 alloys were investigated by using X-ray diffraction, AC susceptibility, VSM and standard strain gauge techniques. The lattice parameter exhibits positive deviation from Vegard’s law with the increasing Ce content in the range of 0.40.6. Curie temperature decreases linearly with increasing Ce content. The saturation magnetization and magnetostriction decrease when 0.2≤x<0.4 and x>0.6, while abnormally increase with Ce content increasing from 0.4 to 0.6. These abnormal changes of （lattice） parameter, saturation magnetization and magnetostriction can be attributed to the valence fluctuation of Ce （ions.）
文摘通过扫描电镜/能谱、X射线衍射以及金相分析,针对含0.3%Fe(质量分数)的Al Mg Si Cu铝合金,研究了Mn含量对其结晶相的影响。研究表明:合金在铸造过程中形成的结晶相为Al1.9CuMg4.1Si3.3,Al5(FeMn)Si,Al8(FeMn)2Si以及少量的Mg2Si;增大含Mn量,合金中AlFeMnSi型结晶相数量增多;对合金进行均匀化处理时,Al1.9CuMg4.1Si3.3相完全溶解,发生Al5(FeMn)Si向Al8(FeMn)2Si相的转变;对合金进行轧制及最终热处理后,结晶相碎化且沿轧向呈纤维状分布,但结晶相的类型不变。
基金supported by Materials Forming Processing Control and Simulation Laboratory in University of Science and Technology BeijingCNMC Ningxia Orient Group Co.,Ltd.
文摘In this paper,the evolutions of microstructure and mechanical properties of Cu-l.9Be-0.3Ni-0.15Co alloy were studied.The alloys in the condition of the solution treated（soft state） and 37% cold rolled（hard state） were aged at 320 ℃for different time,respectively.The mechanical properties,electrical conductivity and microstructure of the alloy aged for different time were analyzed.Additionally,the precipitation kinetics of Cu-1.9Be-0.3Ni-0.15Co alloys was investigated.X-ray diffraction and transmission electron microscopy results reveal that both continuous precipitation and discontinuous precipitation existed in the hard-state Cu-l.9Be-0.3Ni-0.15Co alloy during the whole aging process;the sequence of continuous precipitation is G.P.zone →γ″→γ′→γ.Furthermore,the precipitation transformation mechanism of softstate alloy is homogeneous nucleation,while hard-state alloy shows the heterogeneous nucleation（interface nucleation）with the nucleation rate of both states decaying rapidly to zero during aging at 320 ℃.