Due to traffic and wave actions, cast steel joints are subjected to variable-amplitude fatigue loading, which may cause fatigue problems. The ratio of the minimum strain to the maximum strain(strain ratio)can be emplo...Due to traffic and wave actions, cast steel joints are subjected to variable-amplitude fatigue loading, which may cause fatigue problems. The ratio of the minimum strain to the maximum strain(strain ratio)can be employed to analyze the influence of variable-amplitude fatigue both in the elastic and plastic ranges. To evaluate the effect of the strain ratio on G20Mn5 QT cast steel, the fatigue tests of smooth specimens were carried out at the strain ratio of 0.1. The cyclic deformation and the relationships between the strain amplitude, the stress amplitude, the Smith, Watson and Topper(SWT)parameter and fatigue life were studied and compared with those at the strain ratio of-1. Compared with other methods, Basquin formula and Solonberg formula provide reliable and appropriate ranges of S-N curve and fatigue limit at different strain ratios respectively. The SWT parameter can be used to predict the fatigue life at other strain ratios accurately.展开更多
本文主要介绍了采用熔模铸造工艺实现铸态性能达成抗拉强度≥800MPa,延伸率≥5%,主要的技术措施是:1、利用合金元素Mn和Cu等合金强化基体组织;2、通过采用低镁低稀土球化剂Fe Si Mg6Re2,包内孕育采用75Si Fe,倒包孕育采用4-8mm的钡硅铁...本文主要介绍了采用熔模铸造工艺实现铸态性能达成抗拉强度≥800MPa,延伸率≥5%,主要的技术措施是:1、利用合金元素Mn和Cu等合金强化基体组织;2、通过采用低镁低稀土球化剂Fe Si Mg6Re2,包内孕育采用75Si Fe,倒包孕育采用4-8mm的钡硅铁孕育剂,三次型内孕育采用2-4mm的钡硅铁孕育剂;3、球铁原铁液化学成分控制为:W(C):3.3%-3.5%W(Si):2.3%-2.5%,W(Mn):0.8%-1.0%W(Cu):0.7%-0.9%。试验结果表明,,,基体组织中珠光体含量≥85%,球化等级≤2级,力学性能能够满足要求。展开更多
基金Supported by the National Natural Science Foundation of China(No.51178307 and No.51525803)
文摘Due to traffic and wave actions, cast steel joints are subjected to variable-amplitude fatigue loading, which may cause fatigue problems. The ratio of the minimum strain to the maximum strain(strain ratio)can be employed to analyze the influence of variable-amplitude fatigue both in the elastic and plastic ranges. To evaluate the effect of the strain ratio on G20Mn5 QT cast steel, the fatigue tests of smooth specimens were carried out at the strain ratio of 0.1. The cyclic deformation and the relationships between the strain amplitude, the stress amplitude, the Smith, Watson and Topper(SWT)parameter and fatigue life were studied and compared with those at the strain ratio of-1. Compared with other methods, Basquin formula and Solonberg formula provide reliable and appropriate ranges of S-N curve and fatigue limit at different strain ratios respectively. The SWT parameter can be used to predict the fatigue life at other strain ratios accurately.
文摘本文主要介绍了采用熔模铸造工艺实现铸态性能达成抗拉强度≥800MPa,延伸率≥5%,主要的技术措施是:1、利用合金元素Mn和Cu等合金强化基体组织;2、通过采用低镁低稀土球化剂Fe Si Mg6Re2,包内孕育采用75Si Fe,倒包孕育采用4-8mm的钡硅铁孕育剂,三次型内孕育采用2-4mm的钡硅铁孕育剂;3、球铁原铁液化学成分控制为:W(C):3.3%-3.5%W(Si):2.3%-2.5%,W(Mn):0.8%-1.0%W(Cu):0.7%-0.9%。试验结果表明,,,基体组织中珠光体含量≥85%,球化等级≤2级,力学性能能够满足要求。