The present study is an attempt to find out the effect of environmental corrosion on the commonly used pearlitic rail steel. The cases of corrosion of rail under Indian environment have been studied. It has been found...The present study is an attempt to find out the effect of environmental corrosion on the commonly used pearlitic rail steel. The cases of corrosion of rail under Indian environment have been studied. It has been found that in marine environment both the yield strength and tensile strength decreases with increasing corrosion rate. In acidic environment yield strength increased with increasing corrosion rate, although the tensile strength decreases with increasing corrosion rate.展开更多
An experimental study of dwell and normal cyclic fatigue behaviours was carried out using specimens from a Ti60 forging with a bimodal microstructure. Apparent decrease in the fatigue life was found under dwell fatigu...An experimental study of dwell and normal cyclic fatigue behaviours was carried out using specimens from a Ti60 forging with a bimodal microstructure. Apparent decrease in the fatigue life was found under dwell fatigue condition as compared to that under normal cyclic condition. Strain produced in each cycle in dwell fatigued specimens was observed larger than that in its normal cyclic-fatigued counterparts. Interior crack initiation was found in most dwell fatigued specimens as compared to the subsurface crack initiation under normal cyclic fatigue condition. Flat and bright facets were found at crack initiation sites in both cases. The facet density is higher in dwell condition, which is consistent with the crystal orientation and Schmid factors analysis of α grains around secondary cracks using electron back-scattered diffraction （EBSD） methods. Dwell loading favours cleavage in α grains with their basal plane normals aligned no more than 15° to the loading axis, which may account for its lower fatigue life according to the present study.展开更多
文摘The present study is an attempt to find out the effect of environmental corrosion on the commonly used pearlitic rail steel. The cases of corrosion of rail under Indian environment have been studied. It has been found that in marine environment both the yield strength and tensile strength decreases with increasing corrosion rate. In acidic environment yield strength increased with increasing corrosion rate, although the tensile strength decreases with increasing corrosion rate.
文摘An experimental study of dwell and normal cyclic fatigue behaviours was carried out using specimens from a Ti60 forging with a bimodal microstructure. Apparent decrease in the fatigue life was found under dwell fatigue condition as compared to that under normal cyclic condition. Strain produced in each cycle in dwell fatigued specimens was observed larger than that in its normal cyclic-fatigued counterparts. Interior crack initiation was found in most dwell fatigued specimens as compared to the subsurface crack initiation under normal cyclic fatigue condition. Flat and bright facets were found at crack initiation sites in both cases. The facet density is higher in dwell condition, which is consistent with the crystal orientation and Schmid factors analysis of α grains around secondary cracks using electron back-scattered diffraction （EBSD） methods. Dwell loading favours cleavage in α grains with their basal plane normals aligned no more than 15° to the loading axis, which may account for its lower fatigue life according to the present study.
