The high temperature oxidation resistance of RE Ni W B B 4C MoS 2 composite coating, the effects of electrodeposition conditions on the morphologies of the coating and the effect of heat treatment temperature on its h...The high temperature oxidation resistance of RE Ni W B B 4C MoS 2 composite coating, the effects of electrodeposition conditions on the morphologies of the coating and the effect of heat treatment temperature on its hardness, abrasion resistance and phase structure were investigated by using scanning electron microscope(SEM), X ray diffractometer, microhardness tester and abrasion machine. The results show that the oxidation degree of RE Ni W B B 4C MoS 2 composite coating is small when the temperature is lower than 700 ℃, but it increases sharply when the temperature is higher than 700 ℃. The hardness of RE Ni W B B 4C MoS 2 composite coating increases with increasing heat treatment temperature, it comes up to the maximum value at 400 ℃,but it decreases gradually if the temperature rises continuously. The most favourable abrasion resistance was attained after RE Ni W B B 4C MoS 2 composite coating being heat treated at 400 ℃. Without heat treating, it is mainly amorphous and partially crystallized, but wholly crystallized after being heat treated at 500 ℃. RE in the composite coating is in the form of CeO 2 and additions of CeO 2 and B 4C can enhance the thermostability of RE Ni W B B 4C MoS 2 composite coating.展开更多
文摘The high temperature oxidation resistance of RE Ni W B B 4C MoS 2 composite coating, the effects of electrodeposition conditions on the morphologies of the coating and the effect of heat treatment temperature on its hardness, abrasion resistance and phase structure were investigated by using scanning electron microscope(SEM), X ray diffractometer, microhardness tester and abrasion machine. The results show that the oxidation degree of RE Ni W B B 4C MoS 2 composite coating is small when the temperature is lower than 700 ℃, but it increases sharply when the temperature is higher than 700 ℃. The hardness of RE Ni W B B 4C MoS 2 composite coating increases with increasing heat treatment temperature, it comes up to the maximum value at 400 ℃,but it decreases gradually if the temperature rises continuously. The most favourable abrasion resistance was attained after RE Ni W B B 4C MoS 2 composite coating being heat treated at 400 ℃. Without heat treating, it is mainly amorphous and partially crystallized, but wholly crystallized after being heat treated at 500 ℃. RE in the composite coating is in the form of CeO 2 and additions of CeO 2 and B 4C can enhance the thermostability of RE Ni W B B 4C MoS 2 composite coating.