Effects of Nd on microstructure and mechanical properties of as-cast Mg-8Li-3Al alloy were investigated by OM,X-ray diffraction（XRD）,EPMA,scanning electron microscopy（SEM） and energy dispersive spectroscopy（EDS）...Effects of Nd on microstructure and mechanical properties of as-cast Mg-8Li-3Al alloy were investigated by OM,X-ray diffraction（XRD）,EPMA,scanning electron microscopy（SEM） and energy dispersive spectroscopy（EDS）.The results showed that the dendrites sizes of α phase were decreased by the Nd addition.When the amount of addition Nd was 1.6 wt.%,the alloy with the smallest α phase was obtained.The refining mechanism mainly owed to the increasing constitutional supercooling at the solidification front.Furthermore,the compound Al 2 Nd generated by the reaction of Al and Nd,which distributed at the phase boundary and inside β phase,could also restrain the growth of α phase.Nd could improve the tensile strength and elongation of Mg-8Li-3Al alloy,however,excessive Al 2 Nd might also become crack source and decrease the elongation.展开更多
基金supported by the National High Technology Research and Development Program ("863" Program) of China (2009AA03Z525)the Program of New Century Excellent Talents of the Ministry of Education of China (NCET-08-0080)+1 种基金the Science and Technology Fund of Dalian City (2009J21DW003)the Fundamental Research Funds for the Central Universities (DUT11ZD115)
文摘Effects of Nd on microstructure and mechanical properties of as-cast Mg-8Li-3Al alloy were investigated by OM,X-ray diffraction（XRD）,EPMA,scanning electron microscopy（SEM） and energy dispersive spectroscopy（EDS）.The results showed that the dendrites sizes of α phase were decreased by the Nd addition.When the amount of addition Nd was 1.6 wt.%,the alloy with the smallest α phase was obtained.The refining mechanism mainly owed to the increasing constitutional supercooling at the solidification front.Furthermore,the compound Al 2 Nd generated by the reaction of Al and Nd,which distributed at the phase boundary and inside β phase,could also restrain the growth of α phase.Nd could improve the tensile strength and elongation of Mg-8Li-3Al alloy,however,excessive Al 2 Nd might also become crack source and decrease the elongation.