Synthesis and Characterization of Poly(isoprene-b-butyl methacrylate) Block Copolymer in the Presence of Rare Earth Catalyst

Poly(isoprene-b-butyl methacrylate) block copolymer with a high molecular weight was synthesized in the presence of rare earth coordination catalyst [RE(P 204 ) 3-Al( i Bu) 3 DBE]. The block copolymer was characterized by means of GPC,IR,DSC,NMR and elemental analysis. The block copolymer prepared has two glass transition temperatures: -75 6 ℃ and 32 2 ℃. The microstructure of the diblock copolymer possessed 96 8% cis 1,4 addition for the isoprene segment and a 70% syndiotacticity for the butyl methacrylate segment.

4f金属化合物催化苯乙烯和双烯烃的共聚——共聚反应的主要特征和聚合物的表征

在配位聚合反应的研究中,值得注意的研究课题之一是将稀土催化剂引入到苯乙烯和双烯烃的共聚反应。这一新课题的研究不仅对阐明4f金属配位聚合反应机理,且对开发新型稀土催化剂和共聚物,都有重要意义.例如,共聚物中顺式-1,4含量的多少,对它们的各种性能有明显的影响。

异戊二烯/甲基丙烯酸甲酯嵌段共聚物的合成与微结构研究

用稀土催化剂ＲＥ（Ｐ２０４）３（ｉＢｕ）３ＡｌＢｒＣＨ２ＣＨ２Ｂｒ（ＲＥ＝Ｎｄ，Ｐｒ，Ｙ等）合成嵌段共聚物Ｐ（ＩＰｂＭＭＡ）．系统考察了共聚合反应特征，以ＤＳＣ，１ＨＮＭＲ，１３ＣＮＭＲ技术研究了该嵌段共聚物的微结构．发现以二溴乙烷为添加剂的稀土催化体系是制备Ｐ（ＩＰｂＭＭＡ）的良好催化剂，共聚物含２个玻璃化转变温度，分别为－７５６℃和１２９℃，嵌段共聚物的结构规整，（ＩＰ）ｍ段以ｃｉｓ１，４结构为主，其含量为９７％左右，３，４结构为３％左右，链节间以头尾方式连接．（ＭＭＡ）ｎ段以间同立构为主，其含量达７４％．