Red mud is a type of highly alkaline waste residue produced in the process of alumina smelting by the Bayer process.Based on the idea of medium calcium content,solid wastes such as red mud and fly ash were used to pre...Red mud is a type of highly alkaline waste residue produced in the process of alumina smelting by the Bayer process.Based on the idea of medium calcium content,solid wastes such as red mud and fly ash were used to prepare non-burnt bricks;and the mass ratio of CaO/SiO2 was selected in the range of 0.88–1.42.Mechanical properties and durability were investigated with a compressive strength test.X-ray diffractometry(XRD),scanning electron microscope(SEM),and Fourier transform infrared spectroscopy(FTIR)techniques were used to characterize the hydration characteristic.The environmental performance was analyzed by Inductively Coupled Plasma Mass Spectrometry(ICP).The results indicated that the mechanical properties and the durability were optimal when the mass ratio of CaO/SiO2 was 1.23.The hydration products were mostly C–S–H gel,ettringite,Na4Ca(Si10All6)O32·12H2O and Ca3Al2(SiO4)(OH)8.They were responsible for the strength development,and the CaO/SiO2 mass ratio of 1.23 had the best polymerized structure.The results of an environmental performance test showed that the heavy metals in the raw materials were well-solidified in the brick.Therefore,this paper provides an effective solution for use of solid wastes in building material.展开更多
Low-dimensional nanomaterials such as graphene can be used as a reinforcing agent in building materials to enhance the strength and durability. Common building materials burnt red soil bricks and fly ash bricks were r...Low-dimensional nanomaterials such as graphene can be used as a reinforcing agent in building materials to enhance the strength and durability. Common building materials burnt red soil bricks and fly ash bricks were reinforced with various amounts of graphene, and the effect of graphene on the strength of these newly developed nanocomposites was studied. The fly ash brick nanocomposite samples were cured as per their standard curing time, and the burnt red soil brick nanocomposite samples were merely dried in the sun instead of being subjected to the traditional heat treatment for days to achieve sufficient strength. The water absorption ability of the fly ash bricks was also discussed. The compressive strength of all of the graphene-reinforced nanocomposite samples was tested, along with that of some standard (without graphene) composite samples with the same dimensions, to evaluate the effects of the addition of various amounts of graphene on the compressive strength of the bricks.展开更多
基金the financial support from the National Natural Science Foundation of China (No.51574024)Fundamental Research Funds for the Central Universities (FRF-TP-18-005B1)Technological Research and Development Programs of China Railways Corporation (No.2017G006-J)
文摘Red mud is a type of highly alkaline waste residue produced in the process of alumina smelting by the Bayer process.Based on the idea of medium calcium content,solid wastes such as red mud and fly ash were used to prepare non-burnt bricks;and the mass ratio of CaO/SiO2 was selected in the range of 0.88–1.42.Mechanical properties and durability were investigated with a compressive strength test.X-ray diffractometry(XRD),scanning electron microscope(SEM),and Fourier transform infrared spectroscopy(FTIR)techniques were used to characterize the hydration characteristic.The environmental performance was analyzed by Inductively Coupled Plasma Mass Spectrometry(ICP).The results indicated that the mechanical properties and the durability were optimal when the mass ratio of CaO/SiO2 was 1.23.The hydration products were mostly C–S–H gel,ettringite,Na4Ca(Si10All6)O32·12H2O and Ca3Al2(SiO4)(OH)8.They were responsible for the strength development,and the CaO/SiO2 mass ratio of 1.23 had the best polymerized structure.The results of an environmental performance test showed that the heavy metals in the raw materials were well-solidified in the brick.Therefore,this paper provides an effective solution for use of solid wastes in building material.
文摘Low-dimensional nanomaterials such as graphene can be used as a reinforcing agent in building materials to enhance the strength and durability. Common building materials burnt red soil bricks and fly ash bricks were reinforced with various amounts of graphene, and the effect of graphene on the strength of these newly developed nanocomposites was studied. The fly ash brick nanocomposite samples were cured as per their standard curing time, and the burnt red soil brick nanocomposite samples were merely dried in the sun instead of being subjected to the traditional heat treatment for days to achieve sufficient strength. The water absorption ability of the fly ash bricks was also discussed. The compressive strength of all of the graphene-reinforced nanocomposite samples was tested, along with that of some standard (without graphene) composite samples with the same dimensions, to evaluate the effects of the addition of various amounts of graphene on the compressive strength of the bricks.