Magnetocaloric properties of phenolic resin bonded La(Fe,Si)13-based plates and its use in a hybrid magnetic refrigerator

We present a simple hot press-based method for processing La(Fe,Si)13-based compounds consisting of La–Fe–Co–Si–C particles and phenolic resin. The magnetic entropy change △S per unit mass for the La Fe_(10.87)Co_(0.63)Si_(1.5)C_(0.2)/phenolic resin compounds have nearly the same magnitude with the base materials. With the content of phenolic resin of 5.0 wt%, the compound conductivity is 3.13 W·m^(-1)·K^(-1). In order to measure the cooling performance of La(Fe,Si)13-based compounds,the La(Fe_(11.6-x)Co_(x))Si_(1.4)C_(0.15)(x =0.60, 0.65, 0.75, 0.80, 0.85)/phenolic resin compounds were pressed into thin plates and tested in a hybrid refrigerator that combines the active magnetic refrigeration effect with the Stirling cycle refrigeration effect. The test results showed that a maximum cooling power of 41 W was achieved over a temperature span of 30 K.

Magnetic and magnetocaloric effect of Er_(20)Ho_(20)Dy_(20)Cu_(20)Ni_(20)high-entropy metallic glass

Er_(20)Ho_(20)Dy_(20)Cu_(20)Ni_(20)high-entropy metallic glass exhibited excellent magnetic refrigeration material with a wide temperature range and high refrigeration capacity(RC)was reported.Er_(20)Ho_(20)Dy_(20)Cu_(20)Ni_(20)high-entropy metallic glass was observed with typical spin glass behavior around 15.5 K.In addition,we find that the magnetic entropy change(-△S_(M))originates from the sample undergoing a ferromagnetic(FM)to paramagnetic(PM)transition around 20 K.Under a field change from 0 T to 7 T,the value of maximum magnetic entropy change(-△S_(M)^(max))reaches 12.5 J/kg·K,and the corresponding value of RC reaches 487.7 J/kg in the temperature range from 6 K to 60 K.The large RC and wide temperature range make the Er_(20)Ho_(20)Dy_(20)Cu_(20)Ni_(20)high-entropy metallic glass be a promising material for application in magnetic refrigerators.

Development of permanent magnetic refrigerator at room temperature

A reciprocating magnetic refrigerator was developed based on the active magnetic regeneration technology. Rare earth metal Gd and intermetallic compound LaFe11.2Co0.7Si1.1 were used as the magnetic operating materials in the machine. The particles of the magnetic operating materials, with diameter of 0.5-2 mm and total mass of 950 g, were mounted in the cooling bed. A magnetic field was assembled using NdFeB rare earth permanent magnets. It had the magnetic field space of Φ 34×200 and the magnetic induction of 1.5 T. The water at pH=10 is used as a heat transfer fluid. When the ambient temperature is 296 K, a temperature span of 18 K was achieved after operation of 45 min at a frequency of 0.178 Hz. The temperature span and the output power increase significantly with the increasing velocity of heat transfer.

Structure, magnetism and magnetocaloric effects in Er_(5)Si_(3)B_(x)(x=0.3,0.6) compounds

We investigate the structure, magnetic properties, magnetic phase transitions and magnetocaloric effects(MCEs) of Er5Si3Bx(x=0.3,0.6) compounds. The Er5Si3Bx(x = 0.3, 0.6) compounds crystalize in a Mn5Si3type hexagonal structure(space group: P63/cm) and exhibit a successive complicated magnetic phase transition. The extensive magnetic phase transitions contribute to the broad temperature range of MCEs exhibiting in Er_(5)Si_(3)B_(x)(x=0.3,0.6) compounds, with maximum magnetic entropy change(-ΔSM_(max)) and refrigeration capacity of 10.2 J·kg^(-1)·K^(-1), 356.3 J/kg and 11.5 J·kg^(-1)·K^(-1),393.3 J/kg under varying magnetic fields 0–5 T, respectively. Remarkably, the δTFWHMvalues(the temperature range corresponding to 1/2×|-ΔSM_(max)|) of Er5Si3Bx(x=0.3,0.6) compounds were up to 41.8 K and 39.6 K, respectively. Thus, the present work provides a potential magnetic refrigeration material with a broad temperature range MCEs for applications in cryogenic magnetic refrigerators.

Effect of surface microstructure of aluminum coating on corrosion properties of magnetic refrigerant gadolinium

AI coatings with different microstructures were prepared on the surface of Gd using the magnetron sputtering technique to improve its corrosion resistance. The corrosion behaviors for the pure Gd and Gd with Al coating in distilled water were studied using the mass loss and electrochemical performance. As a result, pure Gd without coating shows a certain amount of surface cracks under water flow conditions, whereas the polygonal Al coating decreases the path of the corrosive medium to body due to the existence of eroding pits structure. Compared with the polygonal structure Al coating and pure Gd, the lamellar structure of Al coating exhibits a higher electrochemical protection performance （e.g., a lower corrosion current and higher self-corrosion potential） and no occurrence of pitting corrosion. Due to an effective physical shield, the formation of the lamellar structure protected the inner Gd part from being corroded, and prolonged the duration of cathodic protection.

Rare Earths and Magnetic Refrigeration

Magnetic refrigeration is a revolutionary, efficient, environmentally friendly cooling technology, which is on the threshold of commercialization. The magnetic rare earth materials are utilized as the magnetic refrigerants in most cooling devices, and for many cooling application the Nd2Fe14B permanent magnets are employed as the source of the magnetic field. The status of the near room temperature magnetic cooling was reviewed.

Nanocrystalline and Nanocomposite Magnetic Materials and Their Applications

Nanocrystalline materials can possess bulk properties quite different from those commonly associated with conventional large-grained materials. Nanocomposites, a subset of nanocrystalline materials, in addition have been found to possess magnetic properties which are similar to, but different from, the properties of the individual constituents. New magnetic phenomena, unusual property combinations, and both enhanced and diminished magnetic property values are just some of the changes observed in magnetic nanocomposites from conventional magnetic materials. Here, a description will be presented of some of the exciting new properties discovered in nanomaterials and the magnetic applications envisioned for them.

Magnetic entropy change and magnetic properties of LaFe_(11.5)Si_(1.5) after controlling the Curie temperature by partial substitution of Mn and hydrogenation

Magnetic properties and magnetic entropy changes of La（Fe_（1-x）Mn_x）_（11.5）Si_（1.5）H_y compounds are investigated. Their Curie temperatures are adjusted to room temperature by partial Mn substitution for Fe and hydrogen absorption in 1-atm（1 atm = 1.01325×10~5Pa） hydrogen gas. Under a field change from 0 T to 2 T, the maximum magnetic entropy change for La（Fe_（0.99）Mn_（0.01））_（11.5）Si_（1.5）H_（1.61）is-11.5 J/kg. The suitable Curie temperature and large value of ？S_m make it an attractive potential candidate for the room temperature magnetic refrigeration application.

Magnetic properties of Fe_(3(1-x))Cr_(3x)C alloys

The magnetic properties of Fe3（1-x）Cr3xC alloys with x=0.05, 0.1, 0.15, and 0.2, which crystallize in the cementite Fe3C-type structure with space group Pnma, were investigated by means of magnetization measurements. These alloys show temperature-induced second-order magnetic phase transitions. The Curie temperature （Tc） of these alloys decreases with increasing x. The isothermal magnetic-entropy changes of these alloys were derived from the magnetic isotherms measured with increasing temperature and increasing field. The maximum values of the magnetic-entropy change are about 0.9 and 3.6 J·kg^-1·K^-1 at Tc =360 K for x = 0.05 in a magnetic field change from 0 to 1 T and 0 to 5 T, respectively.

Magnetocaloric Effect in Colossal Magnetoresistance Material (La_(0.6)Dy_(0.1))Sr_(0.3)MnO_3

The magnetocaloric effect in the A-site doping colossal magnetoresistance material (La_(0.6)Dy_(0.1))Sr_(0.3)MnO_3 was studied. From the measurement and calculation of isothermal magnetization (M-H) curves under various temperatures, a large magnetocaloric effect with ferromagnetic-paramagnetic transition, additional magnetism exchange action introduces additional magnetic entropy change was discovered. This result suggests that (La_(0.6)Dy_(0.1))Sr_(0.3)MnO_3 is a suitable candidate as working substance at room temperature in magnetic refrigeration technology.

Influence of Sn substitution for Co in RCo_2 (R= Gd,Tb,Dy) alloys on the structure and magnetocaloric effect

The phases and the magnetocaloric effect in the alloys R（Co1-xSnx）2 with X = 0, 0.025, 0.050, 0.075, and 0.100 were investigated by X-ray diffraction analysis and magnetization measurement. The substitution of Sn in RCo2 is limited. The cubic MgCu2-type structure for the alloys of RCo2 was confirmed by X-ray powder diffraction and the remaining alloys mainly consisted of the RCo2 phase, along with some RCo3 and R5Sn3 impurity phases. The impurity phases increase with the increase of Sn content. The Tc of the alloys is not very sensitive to the Sn substitution for Dy（Co1-xSnx）2 and Tb（Co1-xSnx）2, whereas in Gd（Co1-xSnx）2, the Curie temperatures significantly increase. The maximum magnetic entropy changes in the alloys Dy（Co1-xSnx）2 （x = 0, 0.025, 0.050, 0.075） are 5.78, 5.43, 3.88, and 2.98 J·kg^-1·K^-1, respectively, and those in the Tb（Co1-xSnx）2 （x = 0, 0.025） are 3.44, and 2.29 J·kg^-1·K^-1 respectively in the applied field change of 0-2.0 T.

Magnetocaloric effect of (Gd_(1-x)Nd_x)Co_2 alloys in low magnetic field

The phases and magnetocaloric effect in the alloys （Gd1-xNdx）Co2 with x = 0, 0.1, 0.2, 0.3, and 0.4 were investigated by X-ray diffraction analysis and magnetization measurement. The samples are single phase with a cubic MgCu2-type structure. The To decreases obviously with increasing Nd content from 404 K of the alloy with x = 0 to 272 K of the alloy with x = 0.4; forx = 0.3, the To is 296 K, which is near room temperature. In the samples （Gd1-xNdx）Co2 with x = 0.0, 0.1, 0.2, 0.3, and 0.4, the maximum magnetic entropy change is 1.471, 1.228, 1.280, 1.381 and 1.610 J·kg^-1·K^-1, respectively, in the applied field range of 0-2.0 T. The results of Arrott plots confirmed that the transition type were second order magnetic transition forx = 0, 0.3, and 0.4.

Magnetocaloric Properties of (Gd_(1-x)Tb_x)_3Al_2 Compounds Near Room Temperature

Magnetic and thermal properties of the (Gd 1- x Tb x ) 3Al 2 compounds were studied as potential magnetic refrigerant materials which are used in magnetic refrigeration near room temperature at low magnetic field. The compounds (Gd 1- x Tb x ) 3Al 2 with x =0, 0.1, 0.2 and 0 3 exhibit a second order magnetic transition. Curie temperature varies from 255 K for x =0.3 to 280 K for x =0. The maximum of the isothermal magnetic entropy change Δ S increases by substituting Tb element for Gd element. Δ S max =18.9 kJ·m -3 ·K -1 for x =0.1 by changing the magnetic field from 0 to 1 T.

Magnetic hysteresis and refrigeration capacity of Ni-Mn-Ga alloys near Martensitic transformation

This paper studies the magnetic hysteresis and refrigeration capacity of Ni-Mn-Ga alloys in detail during heating and cooling isothermal magnetisation processes. The Ni-Mn-Ga alloys show larger magnetic hysteresis when they trans-form from austenite to martensite, but smaller magnetic hysteresis when they transform from martensite to austenite. This behaviour is independent of either the pure Ni-Mn-Ga alloys or the alloys doped with other elements. Because of the existence of the magnetic hysteresis, the relation between the magnetic entropy change and refrigeration capacity is not simply linear. For practical consideration, magnetocaloric effect of Ni-Mn-Ga alloys should be investigated both on cooling and heating processes.

Effects of Pr substitution on the hydrogenating process and magnetocaloric properties of La1-xPrxFe11.4Si1.6Hy hydrides

In this paper, we study the effects of Pr substitution on the hydrogenating process and magnetocaloric properties of La（1-x）PrxFe11.4Si1.6Hy hydrides. The powder x-ray diffraction patterns of the La1-xPrxFe11.4Si1.6 and its hydrides show that each of the alloys is crystallized into the single phase of cubic Na Zn13-type structure. There are hydrogen-absorbing plateaus under 0.4938 MPa and 0.4882 MPa in the absorbing curves for the La0.8Pr0.2Fe11.4Si1.6 and La0.6Pr0.4Fe11.4Si1.6 compounds. The releasing processes lag behind the absorbing process, which is obviously different from the coincidence between absorbing and releasing curves of the La Fe11.4Si1.6 compound. The remnant hydrogen content for La0.6Pr0.4Fe11.4Si1.6 is significantly more than that for La0.8Pr0.2Fe11.4Si1.6 after hydrogen desorption, indicating that more substitutions of Pr for La are beneficial to retaining more hydrogen atoms in the alloys. The values of maximum magnetic entropy change are 14.91 J/kg·K and 17.995 J/kg·K for La0.8Pr0.2Fe11.4Si1.6H0.13 and La0.6Pr0.4Fe11.4Si1.6H0.87,respectively.

Table-like shape magnetocaloric effect and large refrigerant capacity in dual-phase HoNi/HoNi2 composite

Nowadays,magnetic cooling(MC) technology by using the magnetocaloric effect(MCE) has attracted extensive research interest for its promising practical applications.A constant large/giant MCE covers wide refrigeration temperatures(denote as table-like shape) is beneficial for obtaining high efficiency performance for MC.In this paper,the HoNi/HoNi2 composite was successfully synthesized by arc-melting method and proved to be composed of HoNi and HoNi2 crystalline phases with weight ratios of 52.4 wt.% and 47.6 wt.%,respectively.The maximum magnetic entropy change(-ΔSMmax)is 18.23 J/(kg·K),and the refrigerant capacity values RC1,RC2,and RC3 are 867.9 J/kg,676.4 J/kg,and 467.8 J/kg with ΔH=0-70 kOe,respectively.The table-like shape MCE and large refrigerant capacity values make the composite attractive for cryogenic MC using the Ericsson cycle.

Machine learning technique for prediction of magnetocaloric effect in La(Fe,Si/Al)_(13)-based materials

Data-mining techniques using machine learning are powerful and efficient for materials design, possessing great potential for discovering new materials with good characteristics. Here, this technique has been used on composition design for La（Fe,Si/Al）（13）-based materials, which are regarded as one of the most promising magnetic refrigerants in practice. Three prediction models are built by using a machine learning algorithm called gradient boosting regression tree（GBRT） to essentially find the correlation between the Curie temperature（TC）, maximum value of magnetic entropy change（（？SM）（max））,and chemical composition, all of which yield high accuracy in the prediction of TC and（？SM）（max）. The performance metric coefficient scores of determination（R^2） for the three models are 0.96, 0.87, and 0.91. These results suggest that all of the models are well-developed predictive models on the challenging issue of generalization ability for untrained data, which can not only provide us with suggestions for real experiments but also help us gain physical insights to find proper composition for further magnetic refrigeration applications.

Magnetic properties and magnetocaloric effect in RE_(55)Co_(30)Al_(10)Si_(5)(RE=Er and Tm)amorphous ribbons

The magnetic and magnetocaloric effects(MCE)of the amorphous RE_(55)Co_(30)Al_(10)Si_(5)(RE=Er and Tm)ribbons were systematically investigated in this paper.Compounds with R=Er and Tm undergo a second-order magnetic phase transition from ferromagnetic(FM)to paramagnetic(PM)around Curie temperature T_(C)~9.3 K and 3 K,respectively.For Er_(55)Co_(30)Al_(10)Si_(5) compound,an obvious magnetic hysteresis and thermal hysteresis were observed at low field below 6 K,possibly due to spin-glass behavior.Under the field change of 0 T–5 T,the maximum values of magnetic entropy change(-△S_(M)^(max))reach as high as 15.6 J/kg·K and 15.7 J/kg·K for Er_(55)Co_(30)Al_(10)Si_(5) and Tm_(55)Co_(30)Al_(10)Si_(5) compounds,corresponding refrigerant capacity(RC)values are estimated as 303 J/kg and 189 J/kg,respectively.The large MCE makes amorphous RE_(55)Co_(30)Al_(10)Si_(5)(RE=Er and Tm)alloys become very attractive magnetic refrigeration materials in the low-temperature region.

Study on Gd-Al-Dy System Magnetic Refrigeration Materials

d-Al-Dy system materials were prepared by the technique of powder sintering. Twolayers gradient function materials with compositions of (Gd_0.9Dy_0.1)_3Al_2 and Gd_3Al_2 respectively were studied. The results show that the Curie temperature (Tc) of the monolayer material decreases with the increment of Dy content. The Tc values of the twolayer gradient function material agree well with the layer numbers and corresponding to Dy content. For the Tc gradiently changed twolayers Gd-Al-Dy system material, its ΔSm changes smoothly with temperature. Therefore, the magnetic refrigeration is improved.

Thermodynamical Evaluation on Magnetocaloric Effect of Magnetic Refrigerating Materials Near Room Temperature

The relationship between isothermal magnetic entropy change DELTA S andadiabatic temperature change DELTA T_(ad) was deduced according to the principles of thermodynamics.The MCE and the engineering application were discussed for Gd and several new kinds of magneticrefrigerating materials near room temperature, Gd_5Si_2Ge_2, MnFeP_(0.45)As_(0.55) and LaFe_(11.2)Co_(0.7)Si_(1.1). Isothermal entropy change is proportional to adiabatic temperature change with afactor of T/C (T is temperature, C is heat capacity). When the comparison of magnetacoloric effectis made for two different materials, we should consider isothermal entropy change as well asadiabatic temperature change.