The effects of coagulation conditions on tensile properties of the regenerated cellulose fibers prepared by wet-spinning from NaOH/thiourea/urea(8∶6.5∶8 by weight)aqueous solvent were investigated by tensile tester,...The effects of coagulation conditions on tensile properties of the regenerated cellulose fibers prepared by wet-spinning from NaOH/thiourea/urea(8∶6.5∶8 by weight)aqueous solvent were investigated by tensile tester,X-ray diffraction(XRD),and scanning electron microscope(SEM).The results show that the tensile properties of the as-spun fibers change with the coagualtion concentration,temperature,and time.When the spinning solution is coagulated in 10% H2SO4/12.5% Na2SO4 aqueous solution,the as-spun fibers have a typical structure of cellulose II,a circular cross-section,and homogeneous morphological structure.展开更多
Two direct dyes were applied to conventional viscose(CV)and bamboo viscose(BV)fibers,which were prepared from bamboo cellulose pulps,and the dyeing kinetics of two fibers were compared.Three kinetic equations,namely C...Two direct dyes were applied to conventional viscose(CV)and bamboo viscose(BV)fibers,which were prepared from bamboo cellulose pulps,and the dyeing kinetics of two fibers were compared.Three kinetic equations,namely Chrastil,Cegarra-Puente,and Vickerstaff,were used to fit the experimental dyeing rate points,showing that the best result was obtained by the Chrastil equation.BV fibers displayed slightly higher dyeing rates and dye adsorption values at initial stages,but a bit lower dye adsorption values at equilibrium than CV fibers.Furthermore,the dyeing of BV fibers exhibited lower activation energies and higher dyeing rate constants than that of CV fibers,and therefore showed slightly lower dependence on temperature.展开更多
The regenerated cellulose fibers, made from wood pulp, have excellent physical properties like cotton fiber. Especially polynosic fibers can be mercerized by alkali, but conventional Viscose fiber can not be treated o...The regenerated cellulose fibers, made from wood pulp, have excellent physical properties like cotton fiber. Especially polynosic fibers can be mercerized by alkali, but conventional Viscose fiber can not be treated or mercerized by alkali. The paper studies on behavior of polynosic fibers treated by alkali, including physical properties, such as weight loss, tensile strength and elongation, and fiber structures properties. In this paper, on the basis of study on polynosic fibers treated by alkali, the conclusions were drawn as following. Firstly, polynosic fiber is good at alkali resistance. Secondly, the changes of fiber structure and physical properties begin declining at 5 wt% NaOH concentration and reverse changes take place at 10 wt%.展开更多
文摘The effects of coagulation conditions on tensile properties of the regenerated cellulose fibers prepared by wet-spinning from NaOH/thiourea/urea(8∶6.5∶8 by weight)aqueous solvent were investigated by tensile tester,X-ray diffraction(XRD),and scanning electron microscope(SEM).The results show that the tensile properties of the as-spun fibers change with the coagualtion concentration,temperature,and time.When the spinning solution is coagulated in 10% H2SO4/12.5% Na2SO4 aqueous solution,the as-spun fibers have a typical structure of cellulose II,a circular cross-section,and homogeneous morphological structure.
基金National Key Technology R&D Program of the Chinese Ministry of Science and Technology,China(No.2007BAE41B04)
文摘Two direct dyes were applied to conventional viscose(CV)and bamboo viscose(BV)fibers,which were prepared from bamboo cellulose pulps,and the dyeing kinetics of two fibers were compared.Three kinetic equations,namely Chrastil,Cegarra-Puente,and Vickerstaff,were used to fit the experimental dyeing rate points,showing that the best result was obtained by the Chrastil equation.BV fibers displayed slightly higher dyeing rates and dye adsorption values at initial stages,but a bit lower dye adsorption values at equilibrium than CV fibers.Furthermore,the dyeing of BV fibers exhibited lower activation energies and higher dyeing rate constants than that of CV fibers,and therefore showed slightly lower dependence on temperature.
文摘The regenerated cellulose fibers, made from wood pulp, have excellent physical properties like cotton fiber. Especially polynosic fibers can be mercerized by alkali, but conventional Viscose fiber can not be treated or mercerized by alkali. The paper studies on behavior of polynosic fibers treated by alkali, including physical properties, such as weight loss, tensile strength and elongation, and fiber structures properties. In this paper, on the basis of study on polynosic fibers treated by alkali, the conclusions were drawn as following. Firstly, polynosic fiber is good at alkali resistance. Secondly, the changes of fiber structure and physical properties begin declining at 5 wt% NaOH concentration and reverse changes take place at 10 wt%.