Inl this investigation the different tests were carried out on the butt joints of several kinds of steels to study the effects of weldmatching on the fracture initiation under statie and dynamic loading, on the fractu...Inl this investigation the different tests were carried out on the butt joints of several kinds of steels to study the effects of weldmatching on the fracture initiation under statie and dynamic loading, on the fracture propagating arresting properties, on the fatigue behavior and finally on the residual stress distribution, The testing results show that overmatching of metal increases the possibility of having a general yieleding and may help to enlarge the tolerate of weld defects for crack initiation under dynamic or static loading. In the propagating and arresting cases the beneficial effct of overmatching of weld metal was found .However non significant effect of the weldmatch mg on the propagation thresholds △Kth and da'dN was found.展开更多
文摘Inl this investigation the different tests were carried out on the butt joints of several kinds of steels to study the effects of weldmatching on the fracture initiation under statie and dynamic loading, on the fracture propagating arresting properties, on the fatigue behavior and finally on the residual stress distribution, The testing results show that overmatching of metal increases the possibility of having a general yieleding and may help to enlarge the tolerate of weld defects for crack initiation under dynamic or static loading. In the propagating and arresting cases the beneficial effct of overmatching of weld metal was found .However non significant effect of the weldmatch mg on the propagation thresholds △Kth and da'dN was found.