The effect of catalyst properties on residue oil hydroconversion was studied at moderate operating conditions(at a temperature of 400 ℃, an initial hydrogen pressure of 10 MPa, and a reaction time of 4 h) in a batch ...The effect of catalyst properties on residue oil hydroconversion was studied at moderate operating conditions(at a temperature of 400 ℃, an initial hydrogen pressure of 10 MPa, and a reaction time of 4 h) in a batch mode slurry phase with different catalyst samples. The results showed that the catalyst acidity had a good effect on residue conversion and MCR(micro carbon residue) conversion but brought about higher coke yield. Residue conversion was thermally induced but the catalyst acidity changed its conversion route. A catalyst with higher metal loading, higher hydrogenation activity and appropriate pore size had higher sulfur and metal removal rate, higher MCR conversion and also a lower coke formation. The activity of spent commercial catalyst AS1 and DS1 was slightly lower than the corresponding fresh ones but was still high enough for residue oil hydroconversion. It assumes that the role of the catalyst is to activate hydrogen species toward reaction with an aromatic carbon radical to yield a cyclohexadienyl type intermediate which will turn into liquid and also to absorb the mesophase which can easily aggregate to form coke.展开更多
Isotactic poly（butene-1） （iPB） with spherical morphology was synthesized successfully with bulk precipitation polymerization without post-treatment of the products. The bulk precipitation polymerization process ma...Isotactic poly（butene-1） （iPB） with spherical morphology was synthesized successfully with bulk precipitation polymerization without post-treatment of the products. The bulk precipitation polymerization process made it possible for iPB to be used as general plastic due to the acceptable decreased cost compared with the solution polymerization process. The influence of catalyst residues on the aging and thermal stability of iPB synthesized by bulk precipitation polymerization method was investigated by gel permeation chromatography, mechanical performance testing, thermogravimetric analysis and infrared spectroscopic analysis. Commercial iPB and the lab-made iPB with varied catalyst residue contents were studied. The results demonstrated that the catalyst residues played an important role in the aging process of the iPB. A possible mechanism of aging promotion by catalyst residues was proposed.展开更多
文摘The effect of catalyst properties on residue oil hydroconversion was studied at moderate operating conditions(at a temperature of 400 ℃, an initial hydrogen pressure of 10 MPa, and a reaction time of 4 h) in a batch mode slurry phase with different catalyst samples. The results showed that the catalyst acidity had a good effect on residue conversion and MCR(micro carbon residue) conversion but brought about higher coke yield. Residue conversion was thermally induced but the catalyst acidity changed its conversion route. A catalyst with higher metal loading, higher hydrogenation activity and appropriate pore size had higher sulfur and metal removal rate, higher MCR conversion and also a lower coke formation. The activity of spent commercial catalyst AS1 and DS1 was slightly lower than the corresponding fresh ones but was still high enough for residue oil hydroconversion. It assumes that the role of the catalyst is to activate hydrogen species toward reaction with an aromatic carbon radical to yield a cyclohexadienyl type intermediate which will turn into liquid and also to absorb the mesophase which can easily aggregate to form coke.
基金financially supported by the National Key Technology R&D Program of China(No.2011BAE26B05)
文摘Isotactic poly（butene-1） （iPB） with spherical morphology was synthesized successfully with bulk precipitation polymerization without post-treatment of the products. The bulk precipitation polymerization process made it possible for iPB to be used as general plastic due to the acceptable decreased cost compared with the solution polymerization process. The influence of catalyst residues on the aging and thermal stability of iPB synthesized by bulk precipitation polymerization method was investigated by gel permeation chromatography, mechanical performance testing, thermogravimetric analysis and infrared spectroscopic analysis. Commercial iPB and the lab-made iPB with varied catalyst residue contents were studied. The results demonstrated that the catalyst residues played an important role in the aging process of the iPB. A possible mechanism of aging promotion by catalyst residues was proposed.