To improve oil quality,ZSM-22/SAPO-11 composite molecular sieves were synthesized by adding ZSM-22 into a synthetic gel of SAPO-11 for n-decane hydroisomerization.The mass ratios of ZSM-22/(ZSM-22+SAPO-11)in the compo...To improve oil quality,ZSM-22/SAPO-11 composite molecular sieves were synthesized by adding ZSM-22 into a synthetic gel of SAPO-11 for n-decane hydroisomerization.The mass ratios of ZSM-22/(ZSM-22+SAPO-11)in the composite molecular sieves were optimized and the optimal ZSM-22/SAPO-11 composite(ZS-9)was obtained.The electrostatic repulsions between the ZSM-22 precursors and the SAPO-11 crystalline nuclei produced small ZSM-22 and SAPO-11 crystallites in ZS-9,which increased the specific surface area and mesopore volume and thereby exposed more acid sites.In comparison with conventional SAPO-11,ZSM-22 and their mechanical mixture,ZS-9 with smaller crystallites and the optimal medium and strong Brønsted acid centers(MSBAC)content displayed a higher yield of branched C_(10) isomers(81.6%),lower cracking selectivity(11.9%)and excellent stability.The correlation between the i-C_(10) selectivity and the MSBAC density of molecular sieves indicated that the selectivity for branched C_(10) isomers first increased and then decreased with increasing MSBAC density on the molecular sieves,and the maximum selectivity(87.7%)occurred with a density of 9.6×10^(−2)μmol m^(−2).展开更多
A SAPO-11 silicoaluminophosphate molecular sieve with stable crystal structure was synthesized for the first time. After removing template by calcination, its crystal space group still retains Icm2 which the as-synthe...A SAPO-11 silicoaluminophosphate molecular sieve with stable crystal structure was synthesized for the first time. After removing template by calcination, its crystal space group still retains Icm2 which the as-synthesized has. The catalyst deriving from the present SAPO-11 materials shows higher isomerization selectivity and higher paraffin hydroisomerization yield than those reported elsewhere.展开更多
Silicoaluminophosphate（SAPO） molecular sieves doped with cobalt（Co-SAPO-5） were synthesized hydrothermally with different concentrations of Co.Each sample was characterized by X-ray diffraction,N2 adsorption-desor...Silicoaluminophosphate（SAPO） molecular sieves doped with cobalt（Co-SAPO-5） were synthesized hydrothermally with different concentrations of Co.Each sample was characterized by X-ray diffraction,N2 adsorption-desorption,scanning electron microscopy,ultraviolet-visible spectroscopy,temperature-programmed desorption of NH3（NH3-TPD）,and infrared spectrascopy of adsorbed pyridine（Py-IR）.The results showed that Co was highly dispersed in the Co-SAPO-5 samples.In addition,a part of the Co content had been incorporated into the SAPO-5 framework,while the remainder existed on the surface as extra-framework Co.The surface areas of the Co-SAOP-5 samples were similar to the SAPO-5 sample.However,the pore volumes of the Co-SAOP-5 samples were lower than that of the SAOP-5 sample.As the concentration of Co increased,the pore volume gradually decreased because extra-framework cobalt oxide was present on the catalyst surface.NH3-TPD and Py-IR results revealed that the amount of Br（？）nsted acid and the total amount of acid for the Co-SAPO-5 samples were higher than that for the SAPO-5 sample.These values were also higher for samples with higher Co content.The catalytic activity of the Co-SAPO-5 samples was evaluated for the oxidation of cyclohexane with molecular oxygen.When Co was added to the SAPO-5 catalyst,the catalytic activity of the Co-SAPO-5 catalysts improved.In addition,the conversion of cyclohexane increased as the Co content in the Co-SAPO-5 catalysts increased.However,with a high conversion of cyclohexane（6.30%）,the total selectivity of cyclohexanone（K） and cyclohexanol（A） decreased sharply.The K/A ratio ranged from 1.15 to 2.47.The effects of reaction conditions（i.e.,reaction temperature,reaction time,initial oxygen pressure,and the catalyst amount） on the performance of the Co-SAPO-5 catalysts have also been measured.Furthermore,the stability of the Co-SAPO-5 catalyst was explored and found to be good for the selective oxidation of cyclohexane by molecular oxygen.展开更多
CoAPO11 molecular sieve with a high crystallinity was prepared by hydrothermal synthesis from a nonaqueous system(EG)in the presence of Et2NH or iPr2NH as a structuredirecting agent.The Xray diffraction(XRD)patterns a...CoAPO11 molecular sieve with a high crystallinity was prepared by hydrothermal synthesis from a nonaqueous system(EG)in the presence of Et2NH or iPr2NH as a structuredirecting agent.The Xray diffraction(XRD)patterns and scanning electron micrographs(SEM)revealed that the product powder was pure and homogenous in particlesize.The Xray powder diffraction data,compositional analysis,thermal stability analysis and UVVis diffuse reflectance spectroscopic analysis showed that Co()ions were incorporated in the aluminophosphate framework and tetrahedrally coordinated in the lattice of asprepared samples.展开更多
A TAPO-11 molecular sieve with the space group lcm2 was synthesized successfully. The samples with different space group were controlled simply only by adjusting the crystallization temperature （CT） in the hydrother...A TAPO-11 molecular sieve with the space group lcm2 was synthesized successfully. The samples with different space group were controlled simply only by adjusting the crystallization temperature （CT） in the hydrothermal system. In the system of gel with a molar composition of 0.7R- xTiO2： P2O5： Al2O3： 30H2O, where x is 0.01-0.10 and the R is a mixture of di-n-propylamine and diisopropylamine as templates. When CT was between 150-160℃, the calcined sample showed the space group of Icm^2, while it showed Pna21 at CT larger than 190℃. The characterizations of UV-Vis and FT-IR confirmed that Ti was incorporated into the AEL framework successfully.展开更多
MAPO-11 molecular sieves were synthesized by hydrothermal methods. The influence of precursor of magnesium, Mg/Al ratio, synthesis temperature, synthesis time and the type of template on the formation and properties o...MAPO-11 molecular sieves were synthesized by hydrothermal methods. The influence of precursor of magnesium, Mg/Al ratio, synthesis temperature, synthesis time and the type of template on the formation and properties of MAPO-11 molecular sieves was examined. The samples were characterized by the techniques of X-ray diffraction (XRD), scanning electron microscopy (SEM), thermogravimetric/differential thermogravimetric analysis (TG-DGA), etc. The results show that the shape and size of crystal were influenced by the precursor of Mg, the Mg/Al ratio and the type of template, and the TG-DGA analysis shows that MAPO-11 molecular sieves as-synthesized have poor thermal stability.展开更多
在水热条件下改变合成参数合成了系列SAPO-11分子筛，采用XRD和^29Si MAS NMR等手段对样品进行表征，并考察了合成参数对SAPO-11分子筛性能的影响。结果表明，合成条件对SAPO-11分子筛的骨架Si分布有很大影响。延长晶化时间、升高晶化...在水热条件下改变合成参数合成了系列SAPO-11分子筛，采用XRD和^29Si MAS NMR等手段对样品进行表征，并考察了合成参数对SAPO-11分子筛性能的影响。结果表明，合成条件对SAPO-11分子筛的骨架Si分布有很大影响。延长晶化时间、升高晶化温度、降低硅／铝比（n（SiO2）／n（Al2O3））或控制初始溶胶pH值为5．0～5．4都可以促进骨架Si的均匀分布，得到具有较高Si分散度的SAPO-11分子筛。展开更多
基金The authors gratefully acknowledge the financial support of Science Foundation of China University of Petroleum,Beijing(Grant No.KYJJ2012-03-03).
文摘To improve oil quality,ZSM-22/SAPO-11 composite molecular sieves were synthesized by adding ZSM-22 into a synthetic gel of SAPO-11 for n-decane hydroisomerization.The mass ratios of ZSM-22/(ZSM-22+SAPO-11)in the composite molecular sieves were optimized and the optimal ZSM-22/SAPO-11 composite(ZS-9)was obtained.The electrostatic repulsions between the ZSM-22 precursors and the SAPO-11 crystalline nuclei produced small ZSM-22 and SAPO-11 crystallites in ZS-9,which increased the specific surface area and mesopore volume and thereby exposed more acid sites.In comparison with conventional SAPO-11,ZSM-22 and their mechanical mixture,ZS-9 with smaller crystallites and the optimal medium and strong Brønsted acid centers(MSBAC)content displayed a higher yield of branched C_(10) isomers(81.6%),lower cracking selectivity(11.9%)and excellent stability.The correlation between the i-C_(10) selectivity and the MSBAC density of molecular sieves indicated that the selectivity for branched C_(10) isomers first increased and then decreased with increasing MSBAC density on the molecular sieves,and the maximum selectivity(87.7%)occurred with a density of 9.6×10^(−2)μmol m^(−2).
文摘A SAPO-11 silicoaluminophosphate molecular sieve with stable crystal structure was synthesized for the first time. After removing template by calcination, its crystal space group still retains Icm2 which the as-synthesized has. The catalyst deriving from the present SAPO-11 materials shows higher isomerization selectivity and higher paraffin hydroisomerization yield than those reported elsewhere.
基金supported by the National Basic Research Program of China(2010CB732300)the National Natural Science Foundation of China(21103048)~~
文摘Silicoaluminophosphate（SAPO） molecular sieves doped with cobalt（Co-SAPO-5） were synthesized hydrothermally with different concentrations of Co.Each sample was characterized by X-ray diffraction,N2 adsorption-desorption,scanning electron microscopy,ultraviolet-visible spectroscopy,temperature-programmed desorption of NH3（NH3-TPD）,and infrared spectrascopy of adsorbed pyridine（Py-IR）.The results showed that Co was highly dispersed in the Co-SAPO-5 samples.In addition,a part of the Co content had been incorporated into the SAPO-5 framework,while the remainder existed on the surface as extra-framework Co.The surface areas of the Co-SAOP-5 samples were similar to the SAPO-5 sample.However,the pore volumes of the Co-SAOP-5 samples were lower than that of the SAOP-5 sample.As the concentration of Co increased,the pore volume gradually decreased because extra-framework cobalt oxide was present on the catalyst surface.NH3-TPD and Py-IR results revealed that the amount of Br（？）nsted acid and the total amount of acid for the Co-SAPO-5 samples were higher than that for the SAPO-5 sample.These values were also higher for samples with higher Co content.The catalytic activity of the Co-SAPO-5 samples was evaluated for the oxidation of cyclohexane with molecular oxygen.When Co was added to the SAPO-5 catalyst,the catalytic activity of the Co-SAPO-5 catalysts improved.In addition,the conversion of cyclohexane increased as the Co content in the Co-SAPO-5 catalysts increased.However,with a high conversion of cyclohexane（6.30%）,the total selectivity of cyclohexanone（K） and cyclohexanol（A） decreased sharply.The K/A ratio ranged from 1.15 to 2.47.The effects of reaction conditions（i.e.,reaction temperature,reaction time,initial oxygen pressure,and the catalyst amount） on the performance of the Co-SAPO-5 catalysts have also been measured.Furthermore,the stability of the Co-SAPO-5 catalyst was explored and found to be good for the selective oxidation of cyclohexane by molecular oxygen.
文摘CoAPO11 molecular sieve with a high crystallinity was prepared by hydrothermal synthesis from a nonaqueous system(EG)in the presence of Et2NH or iPr2NH as a structuredirecting agent.The Xray diffraction(XRD)patterns and scanning electron micrographs(SEM)revealed that the product powder was pure and homogenous in particlesize.The Xray powder diffraction data,compositional analysis,thermal stability analysis and UVVis diffuse reflectance spectroscopic analysis showed that Co()ions were incorporated in the aluminophosphate framework and tetrahedrally coordinated in the lattice of asprepared samples.
基金This work was supported by the National Natural Science Foundation of China （No. 20473027） Science and Technology Commission of Shanghai Municipality （No. 05dz22306）Pujiang project （No. 05PJ14041）.
文摘A TAPO-11 molecular sieve with the space group lcm2 was synthesized successfully. The samples with different space group were controlled simply only by adjusting the crystallization temperature （CT） in the hydrothermal system. In the system of gel with a molar composition of 0.7R- xTiO2： P2O5： Al2O3： 30H2O, where x is 0.01-0.10 and the R is a mixture of di-n-propylamine and diisopropylamine as templates. When CT was between 150-160℃, the calcined sample showed the space group of Icm^2, while it showed Pna21 at CT larger than 190℃. The characterizations of UV-Vis and FT-IR confirmed that Ti was incorporated into the AEL framework successfully.
文摘MAPO-11 molecular sieves were synthesized by hydrothermal methods. The influence of precursor of magnesium, Mg/Al ratio, synthesis temperature, synthesis time and the type of template on the formation and properties of MAPO-11 molecular sieves was examined. The samples were characterized by the techniques of X-ray diffraction (XRD), scanning electron microscopy (SEM), thermogravimetric/differential thermogravimetric analysis (TG-DGA), etc. The results show that the shape and size of crystal were influenced by the precursor of Mg, the Mg/Al ratio and the type of template, and the TG-DGA analysis shows that MAPO-11 molecular sieves as-synthesized have poor thermal stability.
文摘在水热条件下改变合成参数合成了系列SAPO-11分子筛，采用XRD和^29Si MAS NMR等手段对样品进行表征，并考察了合成参数对SAPO-11分子筛性能的影响。结果表明，合成条件对SAPO-11分子筛的骨架Si分布有很大影响。延长晶化时间、升高晶化温度、降低硅／铝比（n（SiO2）／n（Al2O3））或控制初始溶胶pH值为5．0～5．4都可以促进骨架Si的均匀分布，得到具有较高Si分散度的SAPO-11分子筛。