The acoustic emission(AE)characteristics from the fatigue crack propagation in SM50B-Zc steel were strongly affected by the environment me- dium.The AE feature from the fatigue process both in air and in 3.5% NaCl aqu...The acoustic emission(AE)characteristics from the fatigue crack propagation in SM50B-Zc steel were strongly affected by the environment me- dium.The AE feature from the fatigue process both in air and in 3.5% NaCl aqueous solution mani- fested a periodicity which indicated the fatigue ex- tension was discontinuous.The fatigue striation and secondary cracking were the main AE sources during the fatigue crack growth in air.In contrast, AE during the fatigue crack propagation in 3.5% NaCl solution was released from the intergranular fracture and quasicleavage cracking.展开更多
Based on theoretical analysis about local strain,strain rate and dissolving rate at crack tip, the corrosion fatigue crack growth rate of steels ZG20SiMn and SM50B-Zc in fresh water and 3.5% NaCl solution were measure...Based on theoretical analysis about local strain,strain rate and dissolving rate at crack tip, the corrosion fatigue crack growth rate of steels ZG20SiMn and SM50B-Zc in fresh water and 3.5% NaCl solution were measured experimentally,and the PH and electrode potential within crack were also measured continuously along with crack propagating.It showed that the increase of crack growth rate,caused by both decreasing frequency and raising stress ratio,was mainly accelerated by hydrogen embrittlement.展开更多
文摘The acoustic emission(AE)characteristics from the fatigue crack propagation in SM50B-Zc steel were strongly affected by the environment me- dium.The AE feature from the fatigue process both in air and in 3.5% NaCl aqueous solution mani- fested a periodicity which indicated the fatigue ex- tension was discontinuous.The fatigue striation and secondary cracking were the main AE sources during the fatigue crack growth in air.In contrast, AE during the fatigue crack propagation in 3.5% NaCl solution was released from the intergranular fracture and quasicleavage cracking.
文摘Based on theoretical analysis about local strain,strain rate and dissolving rate at crack tip, the corrosion fatigue crack growth rate of steels ZG20SiMn and SM50B-Zc in fresh water and 3.5% NaCl solution were measured experimentally,and the PH and electrode potential within crack were also measured continuously along with crack propagating.It showed that the increase of crack growth rate,caused by both decreasing frequency and raising stress ratio,was mainly accelerated by hydrogen embrittlement.