MECHANICAL PROPERTIES OF SMC WHISKER REINFORCED HIGH DENSITY POLYETHYLENE COMPOSITES

A new type of SiO_2-MgO-CaO (SMC) whisker was used to modify high density polyethylene (HDPE).The melting behavior and crystallinity were investigated by differential scanning calorimetry (DSC).The dispersion of whiskers and interfacial adhesion in the prepared HDPE/SMC whisker composites were investigated by scanning electron microscopy (SEM).The mechanical properties were evaluated by mechanical tests and dynamic mechanical analysis (DMA).DSC data indicated that the melting temperature and the crystallini...

SMC晶须在丁苯橡胶中的应用

对硅镁钙晶须(SMC晶须)在丁苯橡胶(SBR)中的应用进行了研究,考察了晶须用量(0～50phr)对胶料的硫化特性和硫化胶的力学性能的影响,并与常用的填料白炭黑(WCB)和碳酸钙(CaCO3)进行了比较。实验结果表明:SMC晶须对SBR有促进硫化作用;SMC晶须对SBR具有一定的补强作用,拉伸强度随着晶须用量的增加而增大;用量相同时,SMC晶须填充的复合材料硬度和撕裂强度与WCB填充的相当,300%定伸应力比WCB填充的高,拉伸永久变形比WCB小得多;SMC晶须补强效果远优于CaCO3。

SMC晶须增强尼龙6复合材料的性能研究

通过注射成型的方法制备了SMC增强尼龙6复合材料,然后对复合材料的力学性能、热性能及其它物理性能进行了测试,研究了SMC晶须含量对SMC/nylon复合材料性能的影响规律。结果表明,SMC晶须对尼龙6的力学性能、耐热性能及形状尺寸稳定有明显的增强作用,晶须含量越高增强效果越好,但晶须对尼龙6的冲击性能及加工性能产生了不利的影响。

SMC晶须增强高密度聚乙烯复合材料的拉伸性能

采用一种新型SMC晶须纤维增强HDPE制备出SH复合材料,并运用扫描电镜(SEM)、动态机械力学分析(DMA)等方法对复合材料的拉伸性能进行了研究,并在此基础上进一步研究了材料在高温下的长期拉伸蠕变性能。结果表明:与纯HDPE相比,随着晶须含量的增加,SH复合材料的拉伸强度、模量有大幅的提高,这些改善归因于晶须纤维与基体材料之间良好的兼容性及两者之间的界面强度增强;晶须对HDPE增强的同时还提高了SH复合材料的长期耐蠕变性能,随着晶须含量的增加,复合材料表现出更多的线性力学性能。

SMC晶须/高密度聚乙烯复合材料的多层结晶结构

研究了SMC晶须/高密度聚乙烯复合材料的结晶结构,着重对比了静态注射样品和动态保压注射样品的多层结晶结构和形貌。静态注射样品具有皮层和芯层2层结构,而动态保压注射样品则存在皮层、剪切层和芯层3层结构。示差扫描量热分析(DSC)结果表明:SMC晶须对高密度聚乙烯结晶具有促进作用,样品各层的结晶度都随着晶须含量的增加而变大,在剪切力最强的剪切层这种促进作用更为明显。广角衍射(WAXD)和小角散射(SAXS)结果表明剪切层具有很高的取向度。剪切层的高结晶度和高取向度的特点使动态注射样品具有更优异的力学性能。

基于SMC晶须改性高密度聚乙烯蠕变研究的检查井寿命预测

用SMC晶须增强高密度聚乙烯制备出一种新型复合材料(WPE),对WPE材料进行了拉伸、弯曲及压缩蠕变研究,并采用一种线性外推的方法来处理蠕变数据,拟合得到实验温度下的材料失效时间与蠕变强度关系式。在分析检查井各受力部位的应力状况基础上,结合时温等效原理对WPE塑料检查井的寿命进行了预测。结果表明:处理材料非线性蠕变数据的外推方法适于预测WPE检查井长期工作性能,计算显示检查井在使用31.42 a后达到其允许应变,说明用SMC改性高密度聚乙烯材料制备的检查井是可靠的。

SMC晶须/聚丙烯复合材料的性能研究

通过注射成型的方法制备了SMC/PP复合材料,然后对复合材料的力学性能及热性能进行了分析,研究了SMC晶须含量对SMC/PP复合材料力学及热性能的影响规律,并对此进行了合理的解释。