Ternary Pb-Sn-Cd alloy nanoparticles were prepared b y the sonochemical dispersion method. The nanoparticles were found to be about 40 —60 nm and coated with an amorphous layer of surfactant dioctadecyldithiophosph a...Ternary Pb-Sn-Cd alloy nanoparticles were prepared b y the sonochemical dispersion method. The nanoparticles were found to be about 40 —60 nm and coated with an amorphous layer of surfactant dioctadecyldithiophosph ate(DDP).The formation and constituent of the as-prepared nanoalloy were charac terized by transmission electron microscopy (TEM), high resolution transmission electron microscopy (HRTEM), X-ray diffraction (XRD), differential thermal anal ysis and thermogravimetry (DTA-TG), and Fourier transform infrared (FT-IR) spe ctrophotometer.It was also found that the powder showed excellent antiwear prope rty by tribological test results.展开更多
基金Project(50774061) supported by the National Natural Science Foundation of ChinaProject(28-TP-2009) supported by the Research Fund of State Key Laboratory of Solidification Processing(NWPU),China
文摘Ternary Pb-Sn-Cd alloy nanoparticles were prepared b y the sonochemical dispersion method. The nanoparticles were found to be about 40 —60 nm and coated with an amorphous layer of surfactant dioctadecyldithiophosph ate(DDP).The formation and constituent of the as-prepared nanoalloy were charac terized by transmission electron microscopy (TEM), high resolution transmission electron microscopy (HRTEM), X-ray diffraction (XRD), differential thermal anal ysis and thermogravimetry (DTA-TG), and Fourier transform infrared (FT-IR) spe ctrophotometer.It was also found that the powder showed excellent antiwear prope rty by tribological test results.