Baostrip has chosen a steel-grade weathering steel for industrial trial. By carefully designing the composition and manufacturing process,qualified weathering-steel products have been successfully produced on the Ning...Baostrip has chosen a steel-grade weathering steel for industrial trial. By carefully designing the composition and manufacturing process,qualified weathering-steel products have been successfully produced on the Ningbosteel-Baosteel strip casting industrialization demo project( NBS) production line. The industrialized practice of Baostrip shows the following: The surface microstructure of weathering-steel products is polygonal ferrite +pearlite,and that of the center is acicular ferrite. After single-stand on-line hot rolling at a 26% low pressure rate,the thickness tolerance ratio controlled within ± 25 μm reaches 99. 6%. The surface convexity and the wedge can be controlled to | C40 |< 50 μm and | W40 |< 30 μm,respectively. The mechanical properties of the strip are superior,exhibiting a yield strength range of( 430 ± 50) MPa,a tensile strength range of( 550 ± 50) MPa,and an elongation range of( 27 ± 5)%. The corrosion resistance is equivalent to that of current commercial atmospheric corrosion-resistant steels,with a relative corrosion rate of 43%. When used,the weathering steel produced by the strip-casting process meets the strict quality and usage requirements of container steel sheets.展开更多
Application of weathering and cold-formed steel in transmission lines can reduce steel consumption and environmental pollution. Some advances in the studies on the weathering and cold-formed steel in transmission towe...Application of weathering and cold-formed steel in transmission lines can reduce steel consumption and environmental pollution. Some advances in the studies on the weathering and cold-formed steel in transmission tower are introduced. Firstly, corrosion-resistant tests of weathering steel samples under different simulating technical atmospheres were carried out separately for 240 hours. It shows that the corrosion degree of joint samples is higher than that of single chip samples, and the corrosion-resistant performance of weathering steel is superior to common carbon steel. The corrosion-resistance of weathering steel meets with the requirement of transmission tower. Secondly, experiments and finite element analysis for cold-formed angles and a 220kV prototype tower were completed, and the stability coeffi-cient fitting curves as well as the modification formulas of slenderness ratio for cold-formed members were determined. According to the structural characteristics of transmission towers, four sections of cold-formed angles with different sections and slenderness ratios were selected in this study. The finite element model well predicted the buckling behav-iour of the cold-formed members. Ultimate loads calculating by the fitting curve were well agreed to the experimental values, especially for the members with small slenderness ratios. Weight of the cold-formed steel tower can be reduced by more than 5 percent after considering the strength enhancement. Cost of the weathering and cold-formed steel transmission tower is nearly equivalent to that of hot-rolled steel tower with hot galvanizing.展开更多
Alloy element and microstructure are key factors that dominate mechanical and corrosion resistant properties of weathering steel. The effect of Mo on microstructure, mechanical properties and corrosion resistant prope...Alloy element and microstructure are key factors that dominate mechanical and corrosion resistant properties of weathering steel. The effect of Mo on microstructure, mechanical properties and corrosion resistant property of depos ited metal was investigated. Experimental results show that with the increase of Mo content in deposited metals, the phase transformation temperature decreases, and the ferrite zone in CCT diagram moves rightward, resulting in en larged bainite zone and reduced ferrite and pearlite zone. The addition of 0.24 mass% Mo in deposited metal results in the increase of tensile strength, more M-A constituent and less high angle grain which reduce the low temperature toughness. It is found that Mo can raise the weathering resistance of deposited metal in industrial atmosphere. Analy sis indicates that Mo may enrich in the inner rust layer, produce MoO3, enhance the formation of compact rust film and impede the anode dissolution reaction. Granular bainite in deposited metals displays better corrosion resistance than acicular ferrite during the initial corrosion stage, but its long-term influence on the corrosion resistance is limited.展开更多
The types, morphologies and distributions of nonmetallic inclusions in Cu-P weathering steels with and without rare earth were analyzed through a quantitative image analyzer, scanning electron microscopy (SEM) and ene...The types, morphologies and distributions of nonmetallic inclusions in Cu-P weathering steels with and without rare earth were analyzed through a quantitative image analyzer, scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS) attached to SEM. Solid-soluble content of rare earth in the steels was analyzed by non-aqua electroanalysis and ICP. The results showed that rare earth modified the types and the morphologies of inclusions in the weathering steels. The small spherical rare earth oxysulfides and rare earth sulphides replaced the elongated MnS inclusions in the RE weathering steels. The rare earth inclusions dispersedly distributed and most inclusions were smaller than 2 μm in size. The optimum content of RE was 0.0065%-0.016% for 10PCuRE weathering steels containing about 0.002% oxygen and 0.004% sulfur. Solid-soluble content of rare earth in steels was (14-20)×10-6, which can act as a micro-alloying element. The corrosion resistance of 10PCuRE weathering steels and Q235 were studied by dry-wet cyclic immersion test. Their corrosion rates were obtained respectively. The polarization curves and pitting corrosion behaviors of weathering steels with and without rare earth were measured by electrochemical methods. The corrosion resistance of Cu-P weathering steels was improved by adding an appropriate amount of rare earth. Less and fewer rare earth inclusions largely decreased pitting susceptibility and rate of pit propagation. The pitting potential and the resistance against pitting corrosion of the RE weathering steel were significantly improved due to the modification of rare earth to inclusions.展开更多
The corrosion behavior and mechanism of 3Ni weathering steel in a simulated oceanic atmospheric environment are investigated in order to comprehend the impacts of La,as determined through electrochemical analysis and ...The corrosion behavior and mechanism of 3Ni weathering steel in a simulated oceanic atmospheric environment are investigated in order to comprehend the impacts of La,as determined through electrochemical analysis and rust layer characterization.The results of this study demonstrate that the addition of La enhances the corrosion resistance of 3Ni weathering steel in the marine atmospheric environment,thereby reducing the corrosion rate and improving the protection of the rust layer.The influence of La on corrosion resistance can be attributed to two primary factors.Firstly,La functions as a grain refiner,minimizing the potential difference of the micro-regions on the substrate surface,thereby significantly reducing the corrosion of bare steel in the marine environment.Secondly,La inhibits the process of Fe_(3)O_(4) oxidation back toγ-FeOOH during corrosion at the local site,thus decreasing the formation ofγ-FeOOH and enhancing the charge transfer resistance.This research work may serve as a reference for expanding the application of rare earth elements in the field of weathering steel.展开更多
基金funded by Shanghai Engineering Research Center of Strip Casting and Rolling(No.11DZ2282300)
文摘Baostrip has chosen a steel-grade weathering steel for industrial trial. By carefully designing the composition and manufacturing process,qualified weathering-steel products have been successfully produced on the Ningbosteel-Baosteel strip casting industrialization demo project( NBS) production line. The industrialized practice of Baostrip shows the following: The surface microstructure of weathering-steel products is polygonal ferrite +pearlite,and that of the center is acicular ferrite. After single-stand on-line hot rolling at a 26% low pressure rate,the thickness tolerance ratio controlled within ± 25 μm reaches 99. 6%. The surface convexity and the wedge can be controlled to | C40 |< 50 μm and | W40 |< 30 μm,respectively. The mechanical properties of the strip are superior,exhibiting a yield strength range of( 430 ± 50) MPa,a tensile strength range of( 550 ± 50) MPa,and an elongation range of( 27 ± 5)%. The corrosion resistance is equivalent to that of current commercial atmospheric corrosion-resistant steels,with a relative corrosion rate of 43%. When used,the weathering steel produced by the strip-casting process meets the strict quality and usage requirements of container steel sheets.
文摘Application of weathering and cold-formed steel in transmission lines can reduce steel consumption and environmental pollution. Some advances in the studies on the weathering and cold-formed steel in transmission tower are introduced. Firstly, corrosion-resistant tests of weathering steel samples under different simulating technical atmospheres were carried out separately for 240 hours. It shows that the corrosion degree of joint samples is higher than that of single chip samples, and the corrosion-resistant performance of weathering steel is superior to common carbon steel. The corrosion-resistance of weathering steel meets with the requirement of transmission tower. Secondly, experiments and finite element analysis for cold-formed angles and a 220kV prototype tower were completed, and the stability coeffi-cient fitting curves as well as the modification formulas of slenderness ratio for cold-formed members were determined. According to the structural characteristics of transmission towers, four sections of cold-formed angles with different sections and slenderness ratios were selected in this study. The finite element model well predicted the buckling behav-iour of the cold-formed members. Ultimate loads calculating by the fitting curve were well agreed to the experimental values, especially for the members with small slenderness ratios. Weight of the cold-formed steel tower can be reduced by more than 5 percent after considering the strength enhancement. Cost of the weathering and cold-formed steel transmission tower is nearly equivalent to that of hot-rolled steel tower with hot galvanizing.
基金Item Sponsored by International Science and Technology Cooperation Program of China(2015DFA51460)
文摘Alloy element and microstructure are key factors that dominate mechanical and corrosion resistant properties of weathering steel. The effect of Mo on microstructure, mechanical properties and corrosion resistant property of depos ited metal was investigated. Experimental results show that with the increase of Mo content in deposited metals, the phase transformation temperature decreases, and the ferrite zone in CCT diagram moves rightward, resulting in en larged bainite zone and reduced ferrite and pearlite zone. The addition of 0.24 mass% Mo in deposited metal results in the increase of tensile strength, more M-A constituent and less high angle grain which reduce the low temperature toughness. It is found that Mo can raise the weathering resistance of deposited metal in industrial atmosphere. Analy sis indicates that Mo may enrich in the inner rust layer, produce MoO3, enhance the formation of compact rust film and impede the anode dissolution reaction. Granular bainite in deposited metals displays better corrosion resistance than acicular ferrite during the initial corrosion stage, but its long-term influence on the corrosion resistance is limited.
基金Project supported by Shandong Natural Science Foundation (ZR2010EQ017)
文摘The types, morphologies and distributions of nonmetallic inclusions in Cu-P weathering steels with and without rare earth were analyzed through a quantitative image analyzer, scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS) attached to SEM. Solid-soluble content of rare earth in the steels was analyzed by non-aqua electroanalysis and ICP. The results showed that rare earth modified the types and the morphologies of inclusions in the weathering steels. The small spherical rare earth oxysulfides and rare earth sulphides replaced the elongated MnS inclusions in the RE weathering steels. The rare earth inclusions dispersedly distributed and most inclusions were smaller than 2 μm in size. The optimum content of RE was 0.0065%-0.016% for 10PCuRE weathering steels containing about 0.002% oxygen and 0.004% sulfur. Solid-soluble content of rare earth in steels was (14-20)×10-6, which can act as a micro-alloying element. The corrosion resistance of 10PCuRE weathering steels and Q235 were studied by dry-wet cyclic immersion test. Their corrosion rates were obtained respectively. The polarization curves and pitting corrosion behaviors of weathering steels with and without rare earth were measured by electrochemical methods. The corrosion resistance of Cu-P weathering steels was improved by adding an appropriate amount of rare earth. Less and fewer rare earth inclusions largely decreased pitting susceptibility and rate of pit propagation. The pitting potential and the resistance against pitting corrosion of the RE weathering steel were significantly improved due to the modification of rare earth to inclusions.
基金G.Niu,R.Yuan,H.B.Wu,C.J.Shang,and X.P.Mao appreciate the support from the National Key R&D Program of China(No.2021YFB3701700)G.Niu appreciates the support from the National Natural Science Foundation of China(No.52304389)the China Postdoctoral Science Foundation(No.2022M720402).
文摘The corrosion behavior and mechanism of 3Ni weathering steel in a simulated oceanic atmospheric environment are investigated in order to comprehend the impacts of La,as determined through electrochemical analysis and rust layer characterization.The results of this study demonstrate that the addition of La enhances the corrosion resistance of 3Ni weathering steel in the marine atmospheric environment,thereby reducing the corrosion rate and improving the protection of the rust layer.The influence of La on corrosion resistance can be attributed to two primary factors.Firstly,La functions as a grain refiner,minimizing the potential difference of the micro-regions on the substrate surface,thereby significantly reducing the corrosion of bare steel in the marine environment.Secondly,La inhibits the process of Fe_(3)O_(4) oxidation back toγ-FeOOH during corrosion at the local site,thus decreasing the formation ofγ-FeOOH and enhancing the charge transfer resistance.This research work may serve as a reference for expanding the application of rare earth elements in the field of weathering steel.