This paper reports the fabrication and test of a high-Tc SQUID planar gradiometer which is patterned from YBCO thin film deposited on a SrTiO3 bicrystal substrate. The measurement of noise spectrum at 77K shows that t...This paper reports the fabrication and test of a high-Tc SQUID planar gradiometer which is patterned from YBCO thin film deposited on a SrTiO3 bicrystal substrate. The measurement of noise spectrum at 77K shows that the white noise at 200 Hz is about 1×10^-4 φ0/√Hz. The minimal magnetic gradient is measured and the results suggest that the minimal magnetic gradient is 94 pT/m. The planar gradiometer is used in non-destructive evaluation （NDE） experiments to detect the artifacts in conducting aluminium plates by performing eddy current testing in an unshielded environment. The effect of the exciting coil dimension on the NDE results is investigated. By mapping out the induced field distribution, flaws about 10mm below the plate surface can be clearly identified.展开更多
基金Project supported by Ministry of Science and Technology of China （Grant Nos 2006CB601007 and 2002AA306412 ）, National Nature Science Foundation of China （Grant No 10221002） and Chinese Academy of Sciences and National Center for Nanoscience and Technology, China.
文摘This paper reports the fabrication and test of a high-Tc SQUID planar gradiometer which is patterned from YBCO thin film deposited on a SrTiO3 bicrystal substrate. The measurement of noise spectrum at 77K shows that the white noise at 200 Hz is about 1×10^-4 φ0/√Hz. The minimal magnetic gradient is measured and the results suggest that the minimal magnetic gradient is 94 pT/m. The planar gradiometer is used in non-destructive evaluation （NDE） experiments to detect the artifacts in conducting aluminium plates by performing eddy current testing in an unshielded environment. The effect of the exciting coil dimension on the NDE results is investigated. By mapping out the induced field distribution, flaws about 10mm below the plate surface can be clearly identified.