The influence of pH and metallographic structure on the corrosion behavior of copper-drawn steel is studied with the simulated system.The effect of pH on the corrosion behavior of copper-drawn steel has been investiga...The influence of pH and metallographic structure on the corrosion behavior of copper-drawn steel is studied with the simulated system.The effect of pH on the corrosion behavior of copper-drawn steel has been investigated using open-circuit potential,potentiodynamic polarization,galvanic current measurement,scanning electron microscopy and scanning vibrating electrode technique techniques.The steel is corroded as anode,while the corrosion of copper plate is protected as cathode.All the results revealed that pH and metallographic structure had a significant influence on the corrosion behavior of copper-drawn steel.With the decrease in pH value from 6 to 2.4,the corrosion rate of copper-drawn steel galvanic couple(Cu-Fe GC)obviously increased in the simulated solution of acidic red soil.The electric field formed by the Cu-Fe GC changes the direction of ion migration between the copper and drawn steel electrodes,which impacts the composition and microstructure of corrosion products formed on the electrode surface.展开更多
Cerium malate (CeMal) was tested as a corrosion inhibitor for AA2024-T3 in this work. Corrosion inhibition on bare AA2024-T3 indicated that the inhibiting effect was a result of the synergistic effect of cerium cation...Cerium malate (CeMal) was tested as a corrosion inhibitor for AA2024-T3 in this work. Corrosion inhibition on bare AA2024-T3 indicated that the inhibiting effect was a result of the synergistic effect of cerium cations and maleic anions. The corrosion of AA2024-T3 was stagnated by greatly reducing the corrosion current when CeMal was present in NaCl solutions. CeMal was adsorbed on the surface of AA2024-T3 forming a protective film in the initial stage. Then, cerium cations transformed to cerium oxide/hydroxides, precipitating on the cathode sites to inhibit the further corrosion. The electrochemical impedance spectra results of the sol-gel coatings proved that CeMal was an effective corrosion inhibitor in the sol-gel coatings to provide corrosion protection for AA2024-T3.展开更多
基金financially supported by the Science and Technology Commission of Shanghai Municipality(No.19DZ2271100)。
文摘The influence of pH and metallographic structure on the corrosion behavior of copper-drawn steel is studied with the simulated system.The effect of pH on the corrosion behavior of copper-drawn steel has been investigated using open-circuit potential,potentiodynamic polarization,galvanic current measurement,scanning electron microscopy and scanning vibrating electrode technique techniques.The steel is corroded as anode,while the corrosion of copper plate is protected as cathode.All the results revealed that pH and metallographic structure had a significant influence on the corrosion behavior of copper-drawn steel.With the decrease in pH value from 6 to 2.4,the corrosion rate of copper-drawn steel galvanic couple(Cu-Fe GC)obviously increased in the simulated solution of acidic red soil.The electric field formed by the Cu-Fe GC changes the direction of ion migration between the copper and drawn steel electrodes,which impacts the composition and microstructure of corrosion products formed on the electrode surface.
基金financial support from the National Natural Science Foundation of China (Grant Nos. 51571202 and 51001109)
文摘Cerium malate (CeMal) was tested as a corrosion inhibitor for AA2024-T3 in this work. Corrosion inhibition on bare AA2024-T3 indicated that the inhibiting effect was a result of the synergistic effect of cerium cations and maleic anions. The corrosion of AA2024-T3 was stagnated by greatly reducing the corrosion current when CeMal was present in NaCl solutions. CeMal was adsorbed on the surface of AA2024-T3 forming a protective film in the initial stage. Then, cerium cations transformed to cerium oxide/hydroxides, precipitating on the cathode sites to inhibit the further corrosion. The electrochemical impedance spectra results of the sol-gel coatings proved that CeMal was an effective corrosion inhibitor in the sol-gel coatings to provide corrosion protection for AA2024-T3.