Zinc(Zn)is considered a promising biodegradable metal for implant applications due to its appropriate degradability and favorable osteogenesis properties.In this work,laser powder bed fusion(LPBF)additive manufacturin...Zinc(Zn)is considered a promising biodegradable metal for implant applications due to its appropriate degradability and favorable osteogenesis properties.In this work,laser powder bed fusion(LPBF)additive manufacturing was employed to fabricate pure Zn with a heterogeneous microstructure and exceptional strength-ductility synergy.An optimized processing window of LPBF was established for printing Zn samples with relative densities greater than 99%using a laser power range of 80∼90 W and a scanning speed of 900 mm s−1.The Zn sample printed with a power of 80 W at a speed of 900 mm s−1 exhibited a hierarchical heterogeneous microstructure consisting of millimeter-scale molten pool boundaries,micrometer-scale bimodal grains,and nanometer-scale pre-existing dislocations,due to rapid cooling rates and significant thermal gradients formed in the molten pools.The printed sample exhibited the highest ductility of∼12.1%among all reported LPBF-printed pure Zn to date with appreciable ultimate tensile strength(∼128.7 MPa).Such superior strength-ductility synergy can be attributed to the presence of multiple deformation mechanisms that are primarily governed by heterogeneous deformation-induced hardening resulting from the alternative arrangement of bimodal Zn grains with pre-existing dislocations.Additionally,continuous strain hardening was facilitated through the interactions between deformation twins,grains and dislocations as strain accumulated,further contributing to the superior strength-ductility synergy.These findings provide valuable insights into the deformation behavior and mechanisms underlying exceptional mechanical properties of LPBF-printed Zn and its alloys for implant applications.展开更多
Grain growth of magnesium(Mg)and its hydride is one of the main reasons for kinetic and capacity degradation during the hydrogen absorption and desorption cycles.To solve this problem,herein we propose a novel method ...Grain growth of magnesium(Mg)and its hydride is one of the main reasons for kinetic and capacity degradation during the hydrogen absorption and desorption cycles.To solve this problem,herein we propose a novel method involving synergistic effect of inside embedded metals and outside coated graphene to limit the growth of Mg and its hydride grains.The graphene coated Mg-Y-Al alloys were selected as a model system for demonstrating this positive effect where the Mg_(91)Y_(3)Al_(6)alloy was first prepared by rapidly solidified method and then high-pressure milled with 5 wt%graphene upon 5 MPa hydrogen gas for obtaining in-situ formed YAl_(2)and YH_(3)embedded in the MgH_(2)matrix with graphene shell(denoted as MgH_(2)-Y-Al@GR).In comparison to pure MgH_(2),the obtained MgH_(2)-Y-Al@GR composites deliver much better kinetics and more stable cyclic performance.For instance,the MgH_(2)-Y-Al@GR can release about 6.1 wt%H_(2)within 30 min at 300℃ but pure MgH_(2)only desorbs∼1.5 wt%H_(2).The activation energy for desorption of MgH_(2)-Y-Al@GR samples is calculated to be 75.3±9.1 kJ/mol that is much lower than approximately 160 kJ/mol for pure MgH_(2).Moreover,its capacity retention is promoted from∼57%of pure MgH_(2)to∼84%after 50th cycles without obvious particle agglomeration and grain growth.The synergistic effect of outside graphene coating with inside embedded metals which could provide a huge number of active sites for catalysis as well as inhibit the grain growth of Mg and its hydride is believed to be responsible for these.展开更多
Ni-Fe-based oxides are among the most promising catalysts developed to date for the bottleneck oxygen evolution reaction(OER)in water electrolysis.However,understanding and mastering the synergy of Ni and Fe remain ch...Ni-Fe-based oxides are among the most promising catalysts developed to date for the bottleneck oxygen evolution reaction(OER)in water electrolysis.However,understanding and mastering the synergy of Ni and Fe remain challenging.Herein,we report that the synergy between Ni and Fe can be tailored by crystal dimensionality of Ni,Fe-contained Ruddlesden-Popper(RP)-type perovskites(La_(0.125)Sr_(0.875))n+1(Ni_(0.25)Fe_(0.75))nO3n+1(n=1,2,3),where the material with n=3 shows the best OER performance in alkaline media.Soft X-ray absorption spectroscopy spectra before and after OER reveal that the material with n=3 shows enhanced Ni/Fe-O covalency to boost the electron transfer as compared to those with n=1 and n=2.Further experimental investigations demonstrate that the Fe ion is the active site and the Ni ion is the stable site in this system,where such unique synergy reaches the optimum at n=3.Besides,as n increases,the proportion of unstable rock-salt layers accordingly decreases and the leaching of ions(especially Sr^(2+))into the electrolyte is suppressed,which induces a decrease in the leaching of active Fe ions,ultimately leading to enhanced stability.This work provides a new avenue for rational catalyst design through the dimensional strategy.展开更多
Au sites supported on Ti-containing materials(Au/Ti-containing catalyst)are currently considered as a promising catalyst for the propylene epoxidation owing to the synergistic effect that hydrogen peroxide species for...Au sites supported on Ti-containing materials(Au/Ti-containing catalyst)are currently considered as a promising catalyst for the propylene epoxidation owing to the synergistic effect that hydrogen peroxide species formed on Au sites diffuses to the Ti sites to form the Ti-hydroperoxo intermedi-ates and contributes to the formation of propylene oxide(PO).In principle,thermal treatment will significantly affect the chemical and physical structures of Ti-containing materials.Consequently,the synergy between tailored Ti sites with different surface properties and Au sites is highly expected to enhance the catalytic performance for the reaction.Herein,we systematically studied the intrinsic effects of different microenvironments around Ti sites on the PO adsorption/desorption and conversion,and then effectively improved the catalytic performance by tailoring the number of surface hydroxyl groups.The Ti^(Ⅵ) material with fewer hydroxyls stimulates a remarkable enhancement in PO selectivity and H_(2) efficiency compared to the Ti^(Ⅵ) material that possessed more hydroxyls,offering a 7-fold and 4-fold increase,respectively.As expected,the Ti^(Ⅵ+Ⅳ) and Ti^(Ⅳ) materials also exhibit a similar phenomenon to the Ti^(Ⅵ) materials through the same thermal treatment,which strongly supports that the Ti sites microenvironment is an important factor in suppressing PO con-version and enhancing catalytic performance.These insights could provide guidance for the rational preparation and optimization of Ti-containing materials synergizing with Au catalysts for propylene epoxidation.展开更多
基金National Natural Science Foundation of China (52305358)the Fundamental Research Funds for the Central Universities (2023ZYGXZR061)+3 种基金Guangdong Basic and Applied Basic Research Foundation (2022A1515010304)Science and Technology Program of Guangzhou (202201010362)Young Elite Scientists Sponsorship Program by CAST . (2023QNRC001)Young Talent Support Project of Guangzhou (QT-2023-001)
文摘Zinc(Zn)is considered a promising biodegradable metal for implant applications due to its appropriate degradability and favorable osteogenesis properties.In this work,laser powder bed fusion(LPBF)additive manufacturing was employed to fabricate pure Zn with a heterogeneous microstructure and exceptional strength-ductility synergy.An optimized processing window of LPBF was established for printing Zn samples with relative densities greater than 99%using a laser power range of 80∼90 W and a scanning speed of 900 mm s−1.The Zn sample printed with a power of 80 W at a speed of 900 mm s−1 exhibited a hierarchical heterogeneous microstructure consisting of millimeter-scale molten pool boundaries,micrometer-scale bimodal grains,and nanometer-scale pre-existing dislocations,due to rapid cooling rates and significant thermal gradients formed in the molten pools.The printed sample exhibited the highest ductility of∼12.1%among all reported LPBF-printed pure Zn to date with appreciable ultimate tensile strength(∼128.7 MPa).Such superior strength-ductility synergy can be attributed to the presence of multiple deformation mechanisms that are primarily governed by heterogeneous deformation-induced hardening resulting from the alternative arrangement of bimodal Zn grains with pre-existing dislocations.Additionally,continuous strain hardening was facilitated through the interactions between deformation twins,grains and dislocations as strain accumulated,further contributing to the superior strength-ductility synergy.These findings provide valuable insights into the deformation behavior and mechanisms underlying exceptional mechanical properties of LPBF-printed Zn and its alloys for implant applications.
基金financially supported by the Key Program for International S&T Cooperation Projects of China(No.2017YFE0124300)National Natural Science Foundation of China(No.52171205,51971002 and 52171197)+1 种基金Scientific Research Foundation of Anhui Provincial Education Department(Nos.KJ2020ZD26,KJ2021A0360)Anhui Provincial Natural Science Foundation for Excellent Youth Scholars(No.2108085Y16).
文摘Grain growth of magnesium(Mg)and its hydride is one of the main reasons for kinetic and capacity degradation during the hydrogen absorption and desorption cycles.To solve this problem,herein we propose a novel method involving synergistic effect of inside embedded metals and outside coated graphene to limit the growth of Mg and its hydride grains.The graphene coated Mg-Y-Al alloys were selected as a model system for demonstrating this positive effect where the Mg_(91)Y_(3)Al_(6)alloy was first prepared by rapidly solidified method and then high-pressure milled with 5 wt%graphene upon 5 MPa hydrogen gas for obtaining in-situ formed YAl_(2)and YH_(3)embedded in the MgH_(2)matrix with graphene shell(denoted as MgH_(2)-Y-Al@GR).In comparison to pure MgH_(2),the obtained MgH_(2)-Y-Al@GR composites deliver much better kinetics and more stable cyclic performance.For instance,the MgH_(2)-Y-Al@GR can release about 6.1 wt%H_(2)within 30 min at 300℃ but pure MgH_(2)only desorbs∼1.5 wt%H_(2).The activation energy for desorption of MgH_(2)-Y-Al@GR samples is calculated to be 75.3±9.1 kJ/mol that is much lower than approximately 160 kJ/mol for pure MgH_(2).Moreover,its capacity retention is promoted from∼57%of pure MgH_(2)to∼84%after 50th cycles without obvious particle agglomeration and grain growth.The synergistic effect of outside graphene coating with inside embedded metals which could provide a huge number of active sites for catalysis as well as inhibit the grain growth of Mg and its hydride is believed to be responsible for these.
基金Guangdong Basic and Applied Basic Research Foundation,Grant/Award Number:2023A1515012878Natural Science Foundation of Anhui Province,Grant/Award Number:2008085ME134+2 种基金Australian Research Council Discovery Projects,Grant/Award Numbers:ARC DP200103315,ARC DP200103332Major Special Science and Technology Project of Anhui Province,Grant/Award Number:202103a07020007Key Research and Development Program of Anhui Province,Grant/Award Number:202104a05020057。
文摘Ni-Fe-based oxides are among the most promising catalysts developed to date for the bottleneck oxygen evolution reaction(OER)in water electrolysis.However,understanding and mastering the synergy of Ni and Fe remain challenging.Herein,we report that the synergy between Ni and Fe can be tailored by crystal dimensionality of Ni,Fe-contained Ruddlesden-Popper(RP)-type perovskites(La_(0.125)Sr_(0.875))n+1(Ni_(0.25)Fe_(0.75))nO3n+1(n=1,2,3),where the material with n=3 shows the best OER performance in alkaline media.Soft X-ray absorption spectroscopy spectra before and after OER reveal that the material with n=3 shows enhanced Ni/Fe-O covalency to boost the electron transfer as compared to those with n=1 and n=2.Further experimental investigations demonstrate that the Fe ion is the active site and the Ni ion is the stable site in this system,where such unique synergy reaches the optimum at n=3.Besides,as n increases,the proportion of unstable rock-salt layers accordingly decreases and the leaching of ions(especially Sr^(2+))into the electrolyte is suppressed,which induces a decrease in the leaching of active Fe ions,ultimately leading to enhanced stability.This work provides a new avenue for rational catalyst design through the dimensional strategy.
文摘Au sites supported on Ti-containing materials(Au/Ti-containing catalyst)are currently considered as a promising catalyst for the propylene epoxidation owing to the synergistic effect that hydrogen peroxide species formed on Au sites diffuses to the Ti sites to form the Ti-hydroperoxo intermedi-ates and contributes to the formation of propylene oxide(PO).In principle,thermal treatment will significantly affect the chemical and physical structures of Ti-containing materials.Consequently,the synergy between tailored Ti sites with different surface properties and Au sites is highly expected to enhance the catalytic performance for the reaction.Herein,we systematically studied the intrinsic effects of different microenvironments around Ti sites on the PO adsorption/desorption and conversion,and then effectively improved the catalytic performance by tailoring the number of surface hydroxyl groups.The Ti^(Ⅵ) material with fewer hydroxyls stimulates a remarkable enhancement in PO selectivity and H_(2) efficiency compared to the Ti^(Ⅵ) material that possessed more hydroxyls,offering a 7-fold and 4-fold increase,respectively.As expected,the Ti^(Ⅵ+Ⅳ) and Ti^(Ⅳ) materials also exhibit a similar phenomenon to the Ti^(Ⅵ) materials through the same thermal treatment,which strongly supports that the Ti sites microenvironment is an important factor in suppressing PO con-version and enhancing catalytic performance.These insights could provide guidance for the rational preparation and optimization of Ti-containing materials synergizing with Au catalysts for propylene epoxidation.