Tin/tin oxide materials are key electrocatalysts for selective conversion of CO;to formate/formic acid.Herein we report a tin oxide material with nitrogen doping by using ammonia treatment at elevated temperature. The...Tin/tin oxide materials are key electrocatalysts for selective conversion of CO;to formate/formic acid.Herein we report a tin oxide material with nitrogen doping by using ammonia treatment at elevated temperature. The N doped material demonstrated enhanced electrocatalytic CO;reduction activity, showing high Faradaic efficiency（90%） for formate at -0.65 V vs. RHE with partial current density of 4 mA/cm;.The catalysis was contributed to increased electron negativity of N atom compared to O atom. Additionally, the N-doped catalyst demonstrates sulfur tolerance with retained formate selectivity. The analysis after electrolysis shows that the catalyst structure partially converts to metallic Sn, and thus the combined Sn/N-SnO;is the key for the active CO;catalysis.展开更多
Tin oxide（SnO2） and fluorine doped tin oxide（FTO） films were prepared on glass substrates by sol-gel spin-coating using SnCl4 and NH4F precursors.Fluorine doping concentration was fixed at 4 at%and 20 at%by contro...Tin oxide（SnO2） and fluorine doped tin oxide（FTO） films were prepared on glass substrates by sol-gel spin-coating using SnCl4 and NH4F precursors.Fluorine doping concentration was fixed at 4 at%and 20 at%by controlling precursor sol composition.Films exhibited the tetragonal rutile-type crystal structure regardless of fluorine concentration.Uniform and highly transparent FTO films,with more than 85%of optical transmittance,were obtained by annealing at 600℃.Florine doping of films was verified by analyzing the valence band region obtained by XPS.It was found that the fluorine doping affects the shape of valence band of SnO2 films.In addition,it was observed that the band gap of SnO2 is reduced as well as the Fermi level is upward shifted by the effect of fluorine doping.展开更多
High transparent and conductive thin films of zinc doped tin oxide （ZTO） were deposited on quartz substrates by the radio-frequency （RF） magnetron sputtering using a 12 wt% ZnO doped with 88 wt% SnO2 ceramic targe...High transparent and conductive thin films of zinc doped tin oxide （ZTO） were deposited on quartz substrates by the radio-frequency （RF） magnetron sputtering using a 12 wt% ZnO doped with 88 wt% SnO2 ceramic target.The effect of substrate temperature on the structural,electrical and optical performances of ZTO films has been studied.X-ray diffraction （XRD） results show that ZTO films possess tetragonal rutile structure with the preferred orientation of （101）.The surface morphology and roughness of the films was investigated by the atomic force microscope （AFM）.The electrical characteristic （including carrier concentration,Hall mobility and resistivity） and optical transmittance were studied by the Hall tester and UV- VIS,respectively.The highest carrier concentration of -1.144×1020 cm-3 and the Hall mobility of 7.018 cm2（V ·sec）-1 for the film with an average transmittance of about 80.0% in the visible region and the lowest resistivity of 1.116×10-2 Ω·cm were obtained when the ZTO films deposited at 250 oC.展开更多
Antimony-doped tin hydroxide colloid precipitates were prepared by hydrolysis of SnCl4·5H2O and SbCl3 ethanol solutions. Isoamyl acetate was selected as azeotropic drying solvent and was compared with the most co...Antimony-doped tin hydroxide colloid precipitates were prepared by hydrolysis of SnCl4·5H2O and SbCl3 ethanol solutions. Isoamyl acetate was selected as azeotropic drying solvent and was compared with the most commonly used n-butanol solvent on treating precipitate for low hard agglomeration precursor powders. The FT-IR, BET, XRD, and TEM results of the precursor powders and calcinated antimony-doped tin oxide powders were recorded. The results demonstrate that isoamyl acetate is an excellent azeotropic drying solvent that can effectively prevent the agglomeration of particles and greatly improve the fluffiness of the obtained dried powders. After these precursor powders are calcined, antimony-doped tin oxide nanopowders with tetragonal rutile structure and high dispersivity can be obtained.展开更多
Tin-doped Indium Oxide （ITO） has been successfully prepared via solvothermal method with a mixture of Indium（Ill） acetylacetonate and Tin（IV） bis（acetylacetonate）dichioride in oleyamine solvent under the condi...Tin-doped Indium Oxide （ITO） has been successfully prepared via solvothermal method with a mixture of Indium（Ill） acetylacetonate and Tin（IV） bis（acetylacetonate）dichioride in oleyamine solvent under the condition of the different reaction time from 12 h to 48 h for the first time. The morphology, phase composition and particle size of the ITO powder were characterized by TEM and XRD. Two significant properties required for ITO samples to become noncarbon support for Pt in PEMFCs including specific surface area and electrical conductivity were studied.展开更多
This paper reports that highly transparent and low resistance tantalum-doped indium tin oxide （Ta-doped ITO） films contacted to p-type GaN have been prepared by the electron-beam evaporation technique. The Ta-doped ...This paper reports that highly transparent and low resistance tantalum-doped indium tin oxide （Ta-doped ITO） films contacted to p-type GaN have been prepared by the electron-beam evaporation technique. The Ta-doped ITO contacts become Ohmic with a specific contact resistance of $／sim 5.65／times 10^{ - 5}$$／Omega ／cdot$cm$^{2}$ and show the transmittance of $／sim $98% at a wavelength of 440nm when annealed at 500／du. Blue light emitting diodes （LEDs） fabricated with Ta-doped ITO p-type Ohmic contact layers give a forward-bias voltage of 3.21V at an injection current of 20mA. It further shows that the output power of LEDs with Ta-doped ITO contacts is enhanced 62% at 20mA in comparison with that of LEDs with conventional Ni/Au contacts展开更多
Proton exchange membrane(PEM)water electrolysis represents a promising technology for green hydrogen production,but its widespread deployment is greatly hindered by the indispensable usage of platinum group metal cata...Proton exchange membrane(PEM)water electrolysis represents a promising technology for green hydrogen production,but its widespread deployment is greatly hindered by the indispensable usage of platinum group metal catalysts,especially iridium(Ir)based materials for the energy-demanding oxygen evolution reaction(OER).Herein,we report a new sequential precipitation approach to the synthesis of mixed Ir-nickel(Ni)oxy-hydroxide supported on antimony-doped tin oxide(ATO)nanoparticles(IrNiyO_(x)/ATO,20 wt.%(Ir+Ni),y=0,1,2,and 3),aiming to reduce the utilisation of scarce and precious Ir while maintaining its good acidic OER performance.When tested in strongly acidic electrolyte(0.1 M HClO_(4)),the optimised IrNi1Ox/ATO shows a mass activity of 1.0 mAµgIr^(−1) and a large turnover frequency of 123 s^(−1) at an overpotential of 350 mV,as well as a comparatively small Tafel slope of 50 mV dec^(−1),better than the IrOx/ATO control,particularly with a markedly reduced Ir loading of only 19.7µgIr cm^(−2).Importantly,IrNi1O_(x)/ATO also exhibits substantially better catalytic stability than other reference catalysts,able to continuously catalyse acidic OER at 10 mA cm^(−2) for 15 h without obvious degradation.Our in-situ synchrotron-based x-ray absorption spectroscopy confirmed that the Ir^(3+)/Ir^(4+)species are the active sites for the acidic OER.Furthermore,the performance of IrNi1Ox/ATO was also preliminarily evaluated in a membrane electrode assembly,which shows better activity and stability than other reference catalysts.The IrNi1Ox/ATO reported in this work is a promising alternative to commercial IrO_(2) based catalysts for PEM electrolysis.展开更多
A series of nanocrystalline SnO2 powders, doped with different Sb contents, were synthesized by route of alkoxides hydrolysis using SnCl4·5H2O and SbCl3 as starting materials and calcined at different temperature...A series of nanocrystalline SnO2 powders, doped with different Sb contents, were synthesized by route of alkoxides hydrolysis using SnCl4·5H2O and SbCl3 as starting materials and calcined at different temperatures. The microstructure and morphology of samples are investigated by XRD and TEM, the valence state changes of Sb in SnO2 crystal lattice is detected by Mssbauer spectroscopy and XPS.The resistivity of powders is examined with a mould of inside diameter d=10mm at a constant pressure. The results show that lightly-doping Sb is effective means of semiconducting of nanocrystalline SnO2. The ratio of Sb5+ to Sb3+ decreases with increasing Sb content in SnO2 crystal lattices and calcination temperature. The XPS diffraction confirms the same result as Mssbauer spectroscopy.展开更多
Antimony-doped tin oxide(ATO) nanoparticles were prepared by the mild hydrothermal method at 200 ℃ using sodium stannate, antimony oxide, sodium hydroxide and sulfuric acid as the starting materials. The doped powder...Antimony-doped tin oxide(ATO) nanoparticles were prepared by the mild hydrothermal method at 200 ℃ using sodium stannate, antimony oxide, sodium hydroxide and sulfuric acid as the starting materials. The doped powders were examined by differential thermal analysis(DTA), X-ray diffractometry(XRD) and transmission electron microscopy(TEM). The doping levels of antimony were determined by volumetric method and iodimetry.The results show that antimony is incorporated into the crystal lattice of tin oxide and the doping levels of antimony in the resulting powders are 2.4%, 4.3 % and 5.1 % (molar fraction). The mean particle size of ATO nanoparticles is in the range of 25 - 30 nm. The effects of antimony doping level on the crystalline size and crystallinity were also discussed.展开更多
1 INTRODUCTIONStannic oxide as a wide-band gap semiconductor（Eg≈3.5eV）,has high transparency in thevisible spectral region（index of refraction,n≈1.9）and resistance to acids and bases at roomtemperature.The SnO&l...1 INTRODUCTIONStannic oxide as a wide-band gap semiconductor（Eg≈3.5eV）,has high transparency in thevisible spectral region（index of refraction,n≈1.9）and resistance to acids and bases at roomtemperature.The SnO<sub>2</sub> thin film.the most useful form in application,has been prepared by avariety of physical and chemical deposition processes.It has been found that undoped SnO<sub>2</sub>films have high resistivity(about 10<sup>8--15</sup>Ω·cm)at room temperature[1].For manyapplications requiring not too low sheet resistance。展开更多
Antimony-doped tin oxide(ATO) nanoparticles with an average size of ～ 6 nm were prepared by co-precipitation and subsequent heat treatment. Graphitic carbon nitride(g-CN)/ATO hybrid nanocomposite was designed by the ...Antimony-doped tin oxide(ATO) nanoparticles with an average size of ～ 6 nm were prepared by co-precipitation and subsequent heat treatment. Graphitic carbon nitride(g-CN)/ATO hybrid nanocomposite was designed by the combination of thermally synthesized g-CN and ATO nanoparticles by ultrasonication. The materials were characterized using N2 adsorption/desorption(BET), X-ray diffraction(XRD), scanning electron microscopy(SEM), energy dispersive spectroscopy(EDS), transmission electron microscopy(TEM) and Fourier transform infrared spectroscopy(FTIR). A mixture of five volatile organic compounds(VOCs, chloroform, benzene, toluene, xylene and styrene) was used to compare the adsorption capacity of the samples. The adsorption capacity of ATO nanoparticles was improved by the addition of g-CN. Experimental data showed that, among the five VOCs,chloroform was the least adsorbed, regardless of the samples. The g-CN/ATO showed nearly three times greater adsorption capacity for the VOC mixture than pure ATO. The unchanged efficiency of VOC adsorption during cyclic use demonstrated the completely reversible adsorption and desorption behavior of the nanocomposite at room conditions. This economically and environmentally friendly material can be a practical solution for outdoor and indoor VOC removal.展开更多
近年来,钙钛矿太阳能电池(Perovskite solar cells,PSCs)由于具有光伏性能优异、材料成本低、制造工艺简单等优势,引起了科研工作者广泛的研究兴趣。在PSCs中,电子传输层(Electron transport layer,ETL)在提取和传输光生电子方面起着至...近年来,钙钛矿太阳能电池(Perovskite solar cells,PSCs)由于具有光伏性能优异、材料成本低、制造工艺简单等优势,引起了科研工作者广泛的研究兴趣。在PSCs中,电子传输层(Electron transport layer,ETL)在提取和传输光生电子方面起着至关重要的作用。氧化锡(SnO_(2))由于具有高光学透过率、高电子迁移率、良好的化学稳定性、合理的能级结构和可低温制备等优异性能,成为PSCs器件中理想的ETL。本文围绕SnO_(2) ETL在正置PSCs中的研究进展进行综述,首先介绍了SnO_(2)的结构与光电特性,并归纳了SnO_(2)的制备方法,随后对有机无机杂化PSCs及全无机PSCs中SnO_(2) ETL的改性进行了详细的阐述和总结,包括掺杂及界面修饰处理,最后总结全文,对SnO_(2) ETL的发展进行展望。展开更多
基金financially supported by Key Research Program of the Chinese Academy of Sciences (ZDRW-ZS-2016-3)the National Key Research and Development Program of China (2016YFB0600901)the Instrument Developing Project of the Chinese Academy of Sciences
文摘Tin/tin oxide materials are key electrocatalysts for selective conversion of CO;to formate/formic acid.Herein we report a tin oxide material with nitrogen doping by using ammonia treatment at elevated temperature. The N doped material demonstrated enhanced electrocatalytic CO;reduction activity, showing high Faradaic efficiency（90%） for formate at -0.65 V vs. RHE with partial current density of 4 mA/cm;.The catalysis was contributed to increased electron negativity of N atom compared to O atom. Additionally, the N-doped catalyst demonstrates sulfur tolerance with retained formate selectivity. The analysis after electrolysis shows that the catalyst structure partially converts to metallic Sn, and thus the combined Sn/N-SnO;is the key for the active CO;catalysis.
文摘Tin oxide（SnO2） and fluorine doped tin oxide（FTO） films were prepared on glass substrates by sol-gel spin-coating using SnCl4 and NH4F precursors.Fluorine doping concentration was fixed at 4 at%and 20 at%by controlling precursor sol composition.Films exhibited the tetragonal rutile-type crystal structure regardless of fluorine concentration.Uniform and highly transparent FTO films,with more than 85%of optical transmittance,were obtained by annealing at 600℃.Florine doping of films was verified by analyzing the valence band region obtained by XPS.It was found that the fluorine doping affects the shape of valence band of SnO2 films.In addition,it was observed that the band gap of SnO2 is reduced as well as the Fermi level is upward shifted by the effect of fluorine doping.
基金Funded by the Program for Changjiang Scholars and Innovative Research Team in University, Ministry of Education, China (No.IRT0547)
文摘High transparent and conductive thin films of zinc doped tin oxide （ZTO） were deposited on quartz substrates by the radio-frequency （RF） magnetron sputtering using a 12 wt% ZnO doped with 88 wt% SnO2 ceramic target.The effect of substrate temperature on the structural,electrical and optical performances of ZTO films has been studied.X-ray diffraction （XRD） results show that ZTO films possess tetragonal rutile structure with the preferred orientation of （101）.The surface morphology and roughness of the films was investigated by the atomic force microscope （AFM）.The electrical characteristic （including carrier concentration,Hall mobility and resistivity） and optical transmittance were studied by the Hall tester and UV- VIS,respectively.The highest carrier concentration of -1.144×1020 cm-3 and the Hall mobility of 7.018 cm2（V ·sec）-1 for the film with an average transmittance of about 80.0% in the visible region and the lowest resistivity of 1.116×10-2 Ω·cm were obtained when the ZTO films deposited at 250 oC.
基金Project(50471027) supported by the National Natural Science Foundation of China
文摘Antimony-doped tin hydroxide colloid precipitates were prepared by hydrolysis of SnCl4·5H2O and SbCl3 ethanol solutions. Isoamyl acetate was selected as azeotropic drying solvent and was compared with the most commonly used n-butanol solvent on treating precipitate for low hard agglomeration precursor powders. The FT-IR, BET, XRD, and TEM results of the precursor powders and calcinated antimony-doped tin oxide powders were recorded. The results demonstrate that isoamyl acetate is an excellent azeotropic drying solvent that can effectively prevent the agglomeration of particles and greatly improve the fluffiness of the obtained dried powders. After these precursor powders are calcined, antimony-doped tin oxide nanopowders with tetragonal rutile structure and high dispersivity can be obtained.
文摘Tin-doped Indium Oxide （ITO） has been successfully prepared via solvothermal method with a mixture of Indium（Ill） acetylacetonate and Tin（IV） bis（acetylacetonate）dichioride in oleyamine solvent under the condition of the different reaction time from 12 h to 48 h for the first time. The morphology, phase composition and particle size of the ITO powder were characterized by TEM and XRD. Two significant properties required for ITO samples to become noncarbon support for Pt in PEMFCs including specific surface area and electrical conductivity were studied.
基金Project supported by Science and Technology Planning Project of Guangdong Province (Grant No. 2007A010501008)the Production and Research Project of Guangdong Province and the Ministry of Education (Grant No. 2009B090300338)
文摘This paper reports that highly transparent and low resistance tantalum-doped indium tin oxide （Ta-doped ITO） films contacted to p-type GaN have been prepared by the electron-beam evaporation technique. The Ta-doped ITO contacts become Ohmic with a specific contact resistance of $／sim 5.65／times 10^{ - 5}$$／Omega ／cdot$cm$^{2}$ and show the transmittance of $／sim $98% at a wavelength of 440nm when annealed at 500／du. Blue light emitting diodes （LEDs） fabricated with Ta-doped ITO p-type Ohmic contact layers give a forward-bias voltage of 3.21V at an injection current of 20mA. It further shows that the output power of LEDs with Ta-doped ITO contacts is enhanced 62% at 20mA in comparison with that of LEDs with conventional Ni/Au contacts
基金supported by the National Innovation Agency of Portugal through the project Baterias 2030(Grant No.POCI-01-0247-FEDER-046109)J R E would like to acknowledge the Fundación General CSIC’s ComFuturo programme which has received funding from the European Union’s Horizon 2020 research and innovation programme under the Marie Sklodowska-Curie grant agreement No.101034263+2 种基金The authors appreciate Dr Laura Simonelli and Dr Vlad Martin Diaconescu for their assistance in XAS measurements at the beamline BL22-CLÆSS,ALBA synchrotron(experiment AV-2022025706)R M is grateful to the Portuguese Foundation for Science and Technology(FCT)for the doctoral grant(Grant No.2021.06496.BD)R M and A M are grateful for the financial support from:LA/P/0045/2020,UIDB/00511/2020 and UIDP/00511/2020,funded by the national funds through FCT/MCTES(PIDDAC)。
文摘Proton exchange membrane(PEM)water electrolysis represents a promising technology for green hydrogen production,but its widespread deployment is greatly hindered by the indispensable usage of platinum group metal catalysts,especially iridium(Ir)based materials for the energy-demanding oxygen evolution reaction(OER).Herein,we report a new sequential precipitation approach to the synthesis of mixed Ir-nickel(Ni)oxy-hydroxide supported on antimony-doped tin oxide(ATO)nanoparticles(IrNiyO_(x)/ATO,20 wt.%(Ir+Ni),y=0,1,2,and 3),aiming to reduce the utilisation of scarce and precious Ir while maintaining its good acidic OER performance.When tested in strongly acidic electrolyte(0.1 M HClO_(4)),the optimised IrNi1Ox/ATO shows a mass activity of 1.0 mAµgIr^(−1) and a large turnover frequency of 123 s^(−1) at an overpotential of 350 mV,as well as a comparatively small Tafel slope of 50 mV dec^(−1),better than the IrOx/ATO control,particularly with a markedly reduced Ir loading of only 19.7µgIr cm^(−2).Importantly,IrNi1O_(x)/ATO also exhibits substantially better catalytic stability than other reference catalysts,able to continuously catalyse acidic OER at 10 mA cm^(−2) for 15 h without obvious degradation.Our in-situ synchrotron-based x-ray absorption spectroscopy confirmed that the Ir^(3+)/Ir^(4+)species are the active sites for the acidic OER.Furthermore,the performance of IrNi1Ox/ATO was also preliminarily evaluated in a membrane electrode assembly,which shows better activity and stability than other reference catalysts.The IrNi1Ox/ATO reported in this work is a promising alternative to commercial IrO_(2) based catalysts for PEM electrolysis.
文摘A series of nanocrystalline SnO2 powders, doped with different Sb contents, were synthesized by route of alkoxides hydrolysis using SnCl4·5H2O and SbCl3 as starting materials and calcined at different temperatures. The microstructure and morphology of samples are investigated by XRD and TEM, the valence state changes of Sb in SnO2 crystal lattice is detected by Mssbauer spectroscopy and XPS.The resistivity of powders is examined with a mould of inside diameter d=10mm at a constant pressure. The results show that lightly-doping Sb is effective means of semiconducting of nanocrystalline SnO2. The ratio of Sb5+ to Sb3+ decreases with increasing Sb content in SnO2 crystal lattices and calcination temperature. The XPS diffraction confirms the same result as Mssbauer spectroscopy.
文摘Antimony-doped tin oxide(ATO) nanoparticles were prepared by the mild hydrothermal method at 200 ℃ using sodium stannate, antimony oxide, sodium hydroxide and sulfuric acid as the starting materials. The doped powders were examined by differential thermal analysis(DTA), X-ray diffractometry(XRD) and transmission electron microscopy(TEM). The doping levels of antimony were determined by volumetric method and iodimetry.The results show that antimony is incorporated into the crystal lattice of tin oxide and the doping levels of antimony in the resulting powders are 2.4%, 4.3 % and 5.1 % (molar fraction). The mean particle size of ATO nanoparticles is in the range of 25 - 30 nm. The effects of antimony doping level on the crystalline size and crystallinity were also discussed.
基金Supported by the National Natural Science Foundation of China
文摘1 INTRODUCTIONStannic oxide as a wide-band gap semiconductor（Eg≈3.5eV）,has high transparency in thevisible spectral region（index of refraction,n≈1.9）and resistance to acids and bases at roomtemperature.The SnO<sub>2</sub> thin film.the most useful form in application,has been prepared by avariety of physical and chemical deposition processes.It has been found that undoped SnO<sub>2</sub>films have high resistivity(about 10<sup>8--15</sup>Ω·cm)at room temperature[1].For manyapplications requiring not too low sheet resistance。
基金supported by a grant from the Korean Ministry of Education, Science, and Technology (MEST)Republic of Korea through the National Research Foundation (NRF) (No. 2017-R1C1B2011968)
文摘Antimony-doped tin oxide(ATO) nanoparticles with an average size of ～ 6 nm were prepared by co-precipitation and subsequent heat treatment. Graphitic carbon nitride(g-CN)/ATO hybrid nanocomposite was designed by the combination of thermally synthesized g-CN and ATO nanoparticles by ultrasonication. The materials were characterized using N2 adsorption/desorption(BET), X-ray diffraction(XRD), scanning electron microscopy(SEM), energy dispersive spectroscopy(EDS), transmission electron microscopy(TEM) and Fourier transform infrared spectroscopy(FTIR). A mixture of five volatile organic compounds(VOCs, chloroform, benzene, toluene, xylene and styrene) was used to compare the adsorption capacity of the samples. The adsorption capacity of ATO nanoparticles was improved by the addition of g-CN. Experimental data showed that, among the five VOCs,chloroform was the least adsorbed, regardless of the samples. The g-CN/ATO showed nearly three times greater adsorption capacity for the VOC mixture than pure ATO. The unchanged efficiency of VOC adsorption during cyclic use demonstrated the completely reversible adsorption and desorption behavior of the nanocomposite at room conditions. This economically and environmentally friendly material can be a practical solution for outdoor and indoor VOC removal.
文摘近年来,钙钛矿太阳能电池(Perovskite solar cells,PSCs)由于具有光伏性能优异、材料成本低、制造工艺简单等优势,引起了科研工作者广泛的研究兴趣。在PSCs中,电子传输层(Electron transport layer,ETL)在提取和传输光生电子方面起着至关重要的作用。氧化锡(SnO_(2))由于具有高光学透过率、高电子迁移率、良好的化学稳定性、合理的能级结构和可低温制备等优异性能,成为PSCs器件中理想的ETL。本文围绕SnO_(2) ETL在正置PSCs中的研究进展进行综述,首先介绍了SnO_(2)的结构与光电特性,并归纳了SnO_(2)的制备方法,随后对有机无机杂化PSCs及全无机PSCs中SnO_(2) ETL的改性进行了详细的阐述和总结,包括掺杂及界面修饰处理,最后总结全文,对SnO_(2) ETL的发展进行展望。