NH_(3) selective catalytic reduction(SCR) has been widely recognized as a promising technique for reducing nitrogen oxides from diesel vehicle exhausts. High-efficiency SCR catalysts that could perform at low temperat...NH_(3) selective catalytic reduction(SCR) has been widely recognized as a promising technique for reducing nitrogen oxides from diesel vehicle exhausts. High-efficiency SCR catalysts that could perform at low temperatures are essential to denitration. In this work, a series of bimetallic CeCu-SAPO-34 molecular sieves were synthesized by one-step hydrothermal method. The Ce Cu-SAPO-34 maintained good crystallinity and a regular hexahedron appearance of Cu-SAPO-34 after introducing Ce species, while exhibiting a higher specific surface area and pore volume. The as-prepared CeCu-SAPO-34 with 0.02%(mass) Ce constituent exhibited the best catalytic activity below 300℃ and a maximum NO_(x) conversion of 99% was attained;the NO_(x) removal rates of more than 68% and 94% were achieved at 150℃ and 200℃, respectively. And the introduction of cerium species in Cu-SAPO-34 improves the low-temperature hydrothermal stability of the catalyst towards NH_(3)-SCR reaction. Additionally, the introduced Ce species could enhance the formation of abundant weak Br?nsted acid centers and promote the synergistic effect between CuO grains and isolated Cu^(2+) to enhance the redox cycle, which benefit the NH_(3)-SCR reaction.This work provides a facile synthesis method of high-efficiency SCR denitration catalysts towards diesel vehicles exhaust treatment under low temperature.展开更多
Waste selective catalytic reduction(SCR)catalyst as a hazardous waste has a significant impact on the environment and human health.In present study,a novel technology for thermal treatment of waste SCR catalyst was pr...Waste selective catalytic reduction(SCR)catalyst as a hazardous waste has a significant impact on the environment and human health.In present study,a novel technology for thermal treatment of waste SCR catalyst was proposed by adding it to sinter mix for iron ore sintering.The influences of coke rate on the flame front propagation,sinter microstructure,and sinter quality during sintering co-processing the waste SCR catalyst process were studied.In situ tests results indicated the maximum sintering bed temperature increased at higher coke rate,indicating more liquid phase generated and higher airflow resistance.The sintering time was longer and the calculated flame front speed dropped at higher coke rate.Sinter microstructure results found the coalescence and reshaping of bubbles were more fully with increasing coke rate.The porosity dropped from 35.28%to 25.66%,the pore average diameter of large pores decreased from 383.76μm to 311.43μm.With increasing coke rate,the sinter indexes of tumbler index,productivity,and yield,increased from 33.2%,9.2 t·m^(-2)·d^(-1),28.9%to 58.0%,36.0 t·m^(-2)·d^(-1),68.9%,respectively.Finally,a comprehensive index was introduced to systematically assess the influence of coke rate on sinter quality,which rose from 100 to 200 when coke rate was increased from 3.5%(mass)to 5.5%(mass).展开更多
The catalyst of Fe-Mo/ZSM-5 has been found to be more active than Fe-ZSM-5 and Mo/ZSM-5 separately for selective catalytic reduction （SCR） of nitric oxide （NO） with NH3. The kinetics of the SCR reaction in the pre...The catalyst of Fe-Mo/ZSM-5 has been found to be more active than Fe-ZSM-5 and Mo/ZSM-5 separately for selective catalytic reduction （SCR） of nitric oxide （NO） with NH3. The kinetics of the SCR reaction in the presence of O2 was studied in this work. The results showed that the observed reaction orders were 0.74-0.99, 0.01-0.13, and 0 for NO, O2 and NH3 at 350-450℃, respectively. And the apparent activation energy of the SCR was 65 kJ/mol on the Fe-Mo/ZSM-5 catalyst. The SCR mechanism was also deduced. Adsorbed NO species can react directly with adsorbed ammonia species on the active sites to form N2 and H2O. Gaseous O2 might serve as a reoxidizing agent for the active sites that have undergone reduction in the SCR process. It is also important to note that a certain amount of NO was decomposed directly over the Fe-Mo/ZSM-5 catalyst in the absence of NH3.展开更多
Granular CuO-CeO2-MnOx/γ-Al2O3 catalysts were synthesized by the sol-gel method. The performance of the CuO-CeO2-MnOx/γ-Al2O3 catalysts for the selective catalytic reduction (SCR) was studied in a fixed bed system. ...Granular CuO-CeO2-MnOx/γ-Al2O3 catalysts were synthesized by the sol-gel method. The performance of the CuO-CeO2-MnOx/γ-Al2O3 catalysts for the selective catalytic reduction (SCR) was studied in a fixed bed system. Preliminary tests were carried out to analyze the behavior of NH3 and NO over catalyst in the presence of oxygen. The optimum temperature range for SCR over the CuO-CeO2-MnOx/γ-Al2O3 catalysts is 300-400 ℃ . The catalysts maintain nearly 100% NO conversion at 350 ℃. The NH3 oxidation experiments show that both NO and N2O are produced gradually with the increase of temperature. The catalysts in this experiment have a stronger oxidation property on NH3, which improves the denitrification activity at low temperature. The over-oxidation of NH3 at high temperature is the main cause leading to a decrease in the NO conversion. The NH3 and NO desorption experiments show that NH3 and NO can be adsorbed on CuO-CeO2-MnOx/γ-Al2O3 granular catalysts. The transient response of NH3 and NO indicates that the SCR reaction proceeds in accordance with the Eley-Rideal mechanism. The adsorbed NO has little influence on the denitrification activity in SCR process.展开更多
The selective catalytic reduction （SCR） of NOx with NH3 has been proven to be an efficient technology for NOx conversion to N2. However, the catalysts used for SCR usually suffer from the problem of sulfur poisoning...The selective catalytic reduction （SCR） of NOx with NH3 has been proven to be an efficient technology for NOx conversion to N2. However, the catalysts used for SCR usually suffer from the problem of sulfur poisoning which seriously limits their practical application. This review summarized sulfur poisoning mechanisms of various SCR deNG catalysts and strategies to reduce deactivation caused by SO2 such as doping metals, controlling the structures and morphologies of the catalysts, and selecting appropriate supports. The methods and procedures of catalysts preparation and the reaction conditions also have effect on SO2-resistance of the catalysts. Several novel catalyst systems that exhibited good SO2 resistance are also introduced. This paper could provide guidance for the development of highly efficient sulfur-tolerant deNOx catalysts.展开更多
This study was aimed to investigate the effects of hydrothermal aging, propene and SO<sub>2</sub> poisoning on the ammonia-selective catalytic reduction (NH<sub>3</sub>-SCR) performance of both...This study was aimed to investigate the effects of hydrothermal aging, propene and SO<sub>2</sub> poisoning on the ammonia-selective catalytic reduction (NH<sub>3</sub>-SCR) performance of both Cu-SAPO-34 and Cu-ZSM-5. The catalytic activities of fresh, aged and poisoned samples were tested in ammonia-selective catalytic reduction (NH<sub>3</sub>-SCR) of NO<sub>x</sub> conditions. The XRD, TG and N<sub>2</sub>-desorption results showed that the structures of the Cu-SAPO-34 and Cu-ZSM-5 remained intact after 750˚C hydrothermally aged, SO<sub>2</sub> and propene poisoned. After hydrothermal aging at 750˚C for 12 h, the NO reduction performance of Cu-ZSM-5 was significantly reduced at lower temperatures, while that of Cu-SAPO-34 was less affected. Moreover, Cu-SAPO-34 catalyst showed high NO conversion with SO<sub>2</sub> or propene compared to Cu-ZSM-5. However, Cu-ZSM-5 showed a larger drop in catalytic activity with SO<sub>2</sub> or propene compared to Cu-SAPO-34 catalyst. The H<sub>2</sub>-TPR results showed that Cu<sup>2 </sup> ions could be reduced to Cu<sup> </sup> and Cu<sup>0</sup> for Cu-ZSM-5, while no significant transformation of copper species was observed for Cu-SAPO-34. Meanwhile, the UV-vis DRS results showed that CuO species were formed in Cu-ZSM-5, while little changes were observed for the Cu-SAPO-34. Cu-SAPO-34 showed high sulfur and hydrocarbon poison resistance compared to Cu-ZSM-5. In summary, Cu-SAPO-34 with small-pore zeolite showed higher hydrothermal stability and better hydrocarbon and sulfur poison resistant than Cu-ZSM-5 with medium-pore.展开更多
基金supported by Project of Central Government for Local Science and Technology Development of China (2022JH6/100100050)the National Natural Science Foundation of China (21776028)Liaoning Key Laboratory of Chemical Additive Synthesis and Separation (ZJKF2001)。
文摘NH_(3) selective catalytic reduction(SCR) has been widely recognized as a promising technique for reducing nitrogen oxides from diesel vehicle exhausts. High-efficiency SCR catalysts that could perform at low temperatures are essential to denitration. In this work, a series of bimetallic CeCu-SAPO-34 molecular sieves were synthesized by one-step hydrothermal method. The Ce Cu-SAPO-34 maintained good crystallinity and a regular hexahedron appearance of Cu-SAPO-34 after introducing Ce species, while exhibiting a higher specific surface area and pore volume. The as-prepared CeCu-SAPO-34 with 0.02%(mass) Ce constituent exhibited the best catalytic activity below 300℃ and a maximum NO_(x) conversion of 99% was attained;the NO_(x) removal rates of more than 68% and 94% were achieved at 150℃ and 200℃, respectively. And the introduction of cerium species in Cu-SAPO-34 improves the low-temperature hydrothermal stability of the catalyst towards NH_(3)-SCR reaction. Additionally, the introduced Ce species could enhance the formation of abundant weak Br?nsted acid centers and promote the synergistic effect between CuO grains and isolated Cu^(2+) to enhance the redox cycle, which benefit the NH_(3)-SCR reaction.This work provides a facile synthesis method of high-efficiency SCR denitration catalysts towards diesel vehicles exhaust treatment under low temperature.
基金supported by the National Natural Science Foundation of China(52036008).
文摘Waste selective catalytic reduction(SCR)catalyst as a hazardous waste has a significant impact on the environment and human health.In present study,a novel technology for thermal treatment of waste SCR catalyst was proposed by adding it to sinter mix for iron ore sintering.The influences of coke rate on the flame front propagation,sinter microstructure,and sinter quality during sintering co-processing the waste SCR catalyst process were studied.In situ tests results indicated the maximum sintering bed temperature increased at higher coke rate,indicating more liquid phase generated and higher airflow resistance.The sintering time was longer and the calculated flame front speed dropped at higher coke rate.Sinter microstructure results found the coalescence and reshaping of bubbles were more fully with increasing coke rate.The porosity dropped from 35.28%to 25.66%,the pore average diameter of large pores decreased from 383.76μm to 311.43μm.With increasing coke rate,the sinter indexes of tumbler index,productivity,and yield,increased from 33.2%,9.2 t·m^(-2)·d^(-1),28.9%to 58.0%,36.0 t·m^(-2)·d^(-1),68.9%,respectively.Finally,a comprehensive index was introduced to systematically assess the influence of coke rate on sinter quality,which rose from 100 to 200 when coke rate was increased from 3.5%(mass)to 5.5%(mass).
基金Project supported by the CCSS of Shanxi Provincial Government of China(No.200032,200516)
文摘The catalyst of Fe-Mo/ZSM-5 has been found to be more active than Fe-ZSM-5 and Mo/ZSM-5 separately for selective catalytic reduction （SCR） of nitric oxide （NO） with NH3. The kinetics of the SCR reaction in the presence of O2 was studied in this work. The results showed that the observed reaction orders were 0.74-0.99, 0.01-0.13, and 0 for NO, O2 and NH3 at 350-450℃, respectively. And the apparent activation energy of the SCR was 65 kJ/mol on the Fe-Mo/ZSM-5 catalyst. The SCR mechanism was also deduced. Adsorbed NO species can react directly with adsorbed ammonia species on the active sites to form N2 and H2O. Gaseous O2 might serve as a reoxidizing agent for the active sites that have undergone reduction in the SCR process. It is also important to note that a certain amount of NO was decomposed directly over the Fe-Mo/ZSM-5 catalyst in the absence of NH3.
基金Projects (50776037,50721005) supported by the National Natural Science Foundation of China
文摘Granular CuO-CeO2-MnOx/γ-Al2O3 catalysts were synthesized by the sol-gel method. The performance of the CuO-CeO2-MnOx/γ-Al2O3 catalysts for the selective catalytic reduction (SCR) was studied in a fixed bed system. Preliminary tests were carried out to analyze the behavior of NH3 and NO over catalyst in the presence of oxygen. The optimum temperature range for SCR over the CuO-CeO2-MnOx/γ-Al2O3 catalysts is 300-400 ℃ . The catalysts maintain nearly 100% NO conversion at 350 ℃. The NH3 oxidation experiments show that both NO and N2O are produced gradually with the increase of temperature. The catalysts in this experiment have a stronger oxidation property on NH3, which improves the denitrification activity at low temperature. The over-oxidation of NH3 at high temperature is the main cause leading to a decrease in the NO conversion. The NH3 and NO desorption experiments show that NH3 and NO can be adsorbed on CuO-CeO2-MnOx/γ-Al2O3 granular catalysts. The transient response of NH3 and NO indicates that the SCR reaction proceeds in accordance with the Eley-Rideal mechanism. The adsorbed NO has little influence on the denitrification activity in SCR process.
基金Supported by the Scientific Research Foundation for the Returned Overseas Chinese Scholars,State Education Ministrythe National Natural Science Foundation of China(21506150)
文摘The selective catalytic reduction （SCR） of NOx with NH3 has been proven to be an efficient technology for NOx conversion to N2. However, the catalysts used for SCR usually suffer from the problem of sulfur poisoning which seriously limits their practical application. This review summarized sulfur poisoning mechanisms of various SCR deNG catalysts and strategies to reduce deactivation caused by SO2 such as doping metals, controlling the structures and morphologies of the catalysts, and selecting appropriate supports. The methods and procedures of catalysts preparation and the reaction conditions also have effect on SO2-resistance of the catalysts. Several novel catalyst systems that exhibited good SO2 resistance are also introduced. This paper could provide guidance for the development of highly efficient sulfur-tolerant deNOx catalysts.
文摘This study was aimed to investigate the effects of hydrothermal aging, propene and SO<sub>2</sub> poisoning on the ammonia-selective catalytic reduction (NH<sub>3</sub>-SCR) performance of both Cu-SAPO-34 and Cu-ZSM-5. The catalytic activities of fresh, aged and poisoned samples were tested in ammonia-selective catalytic reduction (NH<sub>3</sub>-SCR) of NO<sub>x</sub> conditions. The XRD, TG and N<sub>2</sub>-desorption results showed that the structures of the Cu-SAPO-34 and Cu-ZSM-5 remained intact after 750˚C hydrothermally aged, SO<sub>2</sub> and propene poisoned. After hydrothermal aging at 750˚C for 12 h, the NO reduction performance of Cu-ZSM-5 was significantly reduced at lower temperatures, while that of Cu-SAPO-34 was less affected. Moreover, Cu-SAPO-34 catalyst showed high NO conversion with SO<sub>2</sub> or propene compared to Cu-ZSM-5. However, Cu-ZSM-5 showed a larger drop in catalytic activity with SO<sub>2</sub> or propene compared to Cu-SAPO-34 catalyst. The H<sub>2</sub>-TPR results showed that Cu<sup>2 </sup> ions could be reduced to Cu<sup> </sup> and Cu<sup>0</sup> for Cu-ZSM-5, while no significant transformation of copper species was observed for Cu-SAPO-34. Meanwhile, the UV-vis DRS results showed that CuO species were formed in Cu-ZSM-5, while little changes were observed for the Cu-SAPO-34. Cu-SAPO-34 showed high sulfur and hydrocarbon poison resistance compared to Cu-ZSM-5. In summary, Cu-SAPO-34 with small-pore zeolite showed higher hydrothermal stability and better hydrocarbon and sulfur poison resistant than Cu-ZSM-5 with medium-pore.