Semi-solid squeeze casting（SSSC） and liquid squeeze casting（LSC） processes were used to fabricate a ZL104 connecting rod, and the influences of the process parameters on the microstructures and mechanical properti...Semi-solid squeeze casting（SSSC） and liquid squeeze casting（LSC） processes were used to fabricate a ZL104 connecting rod, and the influences of the process parameters on the microstructures and mechanical properties were investigated. Results showed that the tensile strength and elongation of the SSSC-fabricated rod were improved by 22% and 17%, respectively, compared with those of the LSC-fabricated rod. For SSSC, the average particle size（APS） and the shape factor（SF） increased with the increase of re-melting temperature（Tr）, whereas the tensile strength and elongation increased first and then decreased. The APS increased with increasing the mold temperature（Tm）, whereas the SF increased initially and then decreased, which caused the tensile strength and elongation to increase initially and then decrease. The APS decreased and the SF increased as squeezing pressure（ps） increased, and the mechanical properties were enhanced. Moreover, the optimal Tr, ps and Tm are 848 K, 100 MPa and 523 K, respectively.展开更多
To obtain semi-solid Al alloy billet with high quality, an investigation was carried out by imposing a multiple magnetic field from the outside of a copper mold in the continuous casting. AISi6Mg2 alloy designed for s...To obtain semi-solid Al alloy billet with high quality, an investigation was carried out by imposing a multiple magnetic field from the outside of a copper mold in the continuous casting. AISi6Mg2 alloy designed for semi-solid metal （SSM） processing was continuously cast through a submerged entry nozzle under various conditions. Effects of multiple magnetic field on meniscus motion, temperature distribution and billet quality were examined. The experimental results showed that meniscus disturbance caused by electromagnetic stirring could be controlled effectively and the surface quality of semi-solid AI alloy billet was improved greatly, and an uniformly fine, globular microstructure across the transverse section of the billet was achieved by optimizing the distribution of multiple magnetic field.展开更多
基金Project(51335009)supported by the National Natural Science Foundation of ChinaProject(2014JQ7273)supported by the Natural Science Foundation of Shaanxi Province of ChinaProject(CXY1514(1))supported by the Xi’an Science and Technology Plan Projects,China
文摘Semi-solid squeeze casting（SSSC） and liquid squeeze casting（LSC） processes were used to fabricate a ZL104 connecting rod, and the influences of the process parameters on the microstructures and mechanical properties were investigated. Results showed that the tensile strength and elongation of the SSSC-fabricated rod were improved by 22% and 17%, respectively, compared with those of the LSC-fabricated rod. For SSSC, the average particle size（APS） and the shape factor（SF） increased with the increase of re-melting temperature（Tr）, whereas the tensile strength and elongation increased first and then decreased. The APS increased with increasing the mold temperature（Tm）, whereas the SF increased initially and then decreased, which caused the tensile strength and elongation to increase initially and then decrease. The APS decreased and the SF increased as squeezing pressure（ps） increased, and the mechanical properties were enhanced. Moreover, the optimal Tr, ps and Tm are 848 K, 100 MPa and 523 K, respectively.
文摘To obtain semi-solid Al alloy billet with high quality, an investigation was carried out by imposing a multiple magnetic field from the outside of a copper mold in the continuous casting. AISi6Mg2 alloy designed for semi-solid metal （SSM） processing was continuously cast through a submerged entry nozzle under various conditions. Effects of multiple magnetic field on meniscus motion, temperature distribution and billet quality were examined. The experimental results showed that meniscus disturbance caused by electromagnetic stirring could be controlled effectively and the surface quality of semi-solid AI alloy billet was improved greatly, and an uniformly fine, globular microstructure across the transverse section of the billet was achieved by optimizing the distribution of multiple magnetic field.