Experimental study and numerical analysis on dry friction and wear performance of co-continuous SiC/Fe-40Cr against SiC/2618 Al alloy composites

The dry friction and wear behaviors of co-continuous composites SiC/Fe–40Cr against SiC/Al 2618 alloy were investigated on a ring-on-ring friction and wear tester at sliding speed of 30-105 m/s under the load of 1.0-2.5 MPa. The experimental result reveals that the characteristic of two body abrasive wear and oxidation wear mechanisms are present for SiCn/2618 Al composite under higher load and sliding speed. SiC ceramic continuous network as the reinforcement can avoid composite from the third body wear that usually occurs in traditional particle reinforced composite. The mechanically mixed layer (MML) controls greatly the wear rate and friction coefficient of the composites. The composites tested at higher sliding speed exhibit higher value of friction coefficient and fluctuation, which is associated with the intermittent formation and removal of the MML. The wear and stress—strain behaviors of SiCn/Fe–40Cr against SiCn/Al 2168 at 30-105 m/s under 1.0-2.5 MPa were analyzed by finite element method with the software Solidwork2012 Simulation, respectively. The wear and stress–strain behavior of the composite predicted by the FEM correlated well with the experimental results.

Multi-scale Modeling and Finite Element Analyses of Thermal Conductivity of 3D C/SiC Composites Fabricating by Flexible-Oriented Woven Process

Thermal conductivity is one of the most significant criterion of three-dimensional carbon fiber-reinforced SiC matrix composites(3D C/SiC).Represent volume element(RVE)models of microscale,void/matrix and mesoscale proposed in this work are used to simulate the thermal conductivity behaviors of the 3D C/SiC composites.An entirely new process is introduced to weave the preform with three-dimensional orthogonal architecture.The 3D steady-state analysis step is created for assessing the thermal conductivity behaviors of the composites by applying periodic temperature boundary conditions.Three RVE models of cuboid,hexagonal and fiber random distribution are respectively developed to comparatively study the influence of fiber package pattern on the thermal conductivities at the microscale.Besides,the effect of void morphology on the thermal conductivity of the matrix is analyzed by the void/matrix models.The prediction results at the mesoscale correspond closely to the experimental values.The effect of the porosities and fiber volume fractions on the thermal conductivities is also taken into consideration.The multi-scale models mentioned in this paper can be used to predict the thermal conductivity behaviors of other composites with complex structures.

Tensile Mechanical Behavior and Failure Mechanism of a Plain-Woven SiCf/SiC Composites at Room and Elevated Temperatures

Ceramic matrix composites (CMCs) are the preferred materials for solving advanced aerospace high-temperature structural components;it has the comprehensive advantages of higher temperature (~1500˚C) and low density. In service environments, CMCs exhibit complex damage mechanisms and failure modes, which are affected by constituent materials, meso-architecture and inhere defects. In this paper, the in-plane tensile mechanical behavior of a plain-woven SiCf/SiC composite at room and elevated temperatures was investigated, and the factors affecting the tensile strength of the material were discussed in depth. The results show that the tensile modulus and strength of SiCf/SiC composites at high temperature are lower, but the fracture strain increases and the toughness of the composites is enhanced;the stitching holes significantly weaken the tensile strength of the material, resulting in the material is easy to break at the cross-section with stitching holes.

FORMING PROCESS OF HOT-EXTRUDED SiCw/6061Al COMPOSITES(Ⅰ)

１ＩＮＴＲＯＤＵＣＴＩＯＮＩｎｒｅｃｅｎｔｙｅａｒｓ，ｍｏｒｅａｎｄｍｏｒｅｃｏｎｔｉｎｕｏｕｓｌｙｏｒｄｉｓｃｏｎｔｉｎｕｏｕｓｌｙｒｅｉｎｆｏｒｃｅｄｍｅｔａｌｍａｔｒｉｘｃｏｍｐｏｓｉｔｅｓ（ＭＭＣｓ）ｈａｖｅｂｅｅｎｕｓｅｄｔｏｍａｋｅｓｔ...

Role of particle stimulated nucleation in recrystallization of hot extruded Al 6061/SiC_p composites

Studies on texture and microstructure evolution in hot extruded Al 6061 aluminium alloy reinforced with uncoated and nickel coated SiC p were carried out by electron backscattered diffraction technique.Textures of both the alloy and its composite with nickel coated SiC p do exhibit strong β fiber with its axis parallel to the direction of extrusion.In addition to the dominant cube texture（001） 100,fully recrystallized grains with partially equiaxed structure have been observed in the alloy reinforced with uncoated SiC p.The recrystallization texture of this composite can be attributed to the particle stimulated nucleation（PSN） due to the presence of SiC p with size less than 5 μm.Under these conditions,the low value of Zener-Hollomon,Z（～1012s-1） confirms that PSN is one of the dominant mechanisms for recrystallization and is governed by formation of deformation zone rather than stored energy.

Tensile behavior of SiC_p/2124Al composites with various SiC particle sizes at room temperature

The tensile properties of 2124Al alloy composites reinforced with various sizes of SiC particles were investigated at room temperature. The size of SiC p was changed from 0.2 μm to 48.0 μm with an identical volume fraction of 20%. The results show that the relative density of the composite decreased with increase of the SiC p size from 3.0 μm to 48.0 μm, whereas 0.2 μm SiC p reinforced composite has the lowest relative density. The pore density, interparticle spacing, SiC particle cracking, SiC p/Al interfacial debonding, the distribution of SiC particles, in the composites are considered as factors to determine the failure behavior of the composites. [

Microstructure and Mechanical Behavior of Squeeze Cast SiC_w/AZ91 Magnesium Matrix Composites

The interfacial microstructure and tensile properties of the squeeze cast SiCw/AZ91 Mg composites were characterized. There exist uniform, line and discrete MgO particles at the interface between SiC whisker and magnesium in the composites using acid aluminum phosphate binder. The interfacial reaction products MgO are beneficial to interfacial bonding between SiCw and the Mg matrix. resulting in an improvement of the mechanical properties of the composite.

Oxidation behavior of oxidation protective coatings for C/C-SiC composites at 1500 ℃

Porous carbon/carbon preforms were infiltrated with melted silicon to form C/C-SiC composites. Three-layer Si-Mo coating prepared by slurry painting and SiC/Si-Mo multilayer coating prepared by chemical vapor deposition(CVD) alternated with slurry painting were applied on C/C-SiC composites, respectively. The oxidation of three samples at 1 500 ℃ was compared. The results show that the C/C-SiC substrate is distorted quickly. Three-layer Si-Mo coating is out of service soon due to the formation of many bubbles on surface. The mass loss of coated sample is 0.76% after 1 h oxidation. The sample with SiC/Si-Mo multilayer coating gains mass even after 105 h oxidation. SiC/Si-Mo multilayer coating can provide longtime protection for C/C-SiC composites and has excellent thermal shock resistance. This is attributed to the combination of dense SiC layer and porous Si-Mo layer. Dense SiC layer plays the dual role of physical and chemical barrier, and resists the oxidation of porous Si-Mo layer. Porous Si-Mo layer improves the thermal shock resistance of the coating.

Thixotropic compression deformation behavior of SiC_p/AZ61 magnesium matrix composites

Compression tests on semi-solid SiCp/AZ61 magnesium matrix composites were carried out using Thermecmastor-Z dynamic material testing machine.Influences of strain-rate,strain,temperature and volume fraction of SiC particles on flow stress were analyzed.The results show that the flow stress of semi-solid SiCp/AZ61 composites is sensitive to temperature and strain rate.The lower the temperature and the larger the strain rate,the higher the flow stress.Meanwhile the flow stress increases with the increase of the volume fraction of SiC particles.This study helps establish the constitutive model of magnesium matrix composites and offers theoretic and experimental references for its thixoforming.

Interfacial reaction in squeeze cast SiC_w/AZ91 composites with different binders

The whisker/matrix interfaces in squeeze cast SiC w/AZ91 composites with different binders (silica binder, acid aluminum phosphate binder and without binder), were studied by transmission electron microscopy (TEM) and high resolution electron microscopy (HREM). The SiC w/AZ91 interface is very clean in the composites with no binders. For the composites with acid aluminum phosphate binders or silica binders, there exists fine discrete interfacial reaction products MgO at the interface, and a definite orientation relationship between MgO and SiC w. The interfacial reaction products MgO is unevenly distributed at different parts of the composite ingot with silica binder, and mainly distributed to the interface at the side part of the composite cylinder. While in the SiC w/AZ91 composite with acid aluminum phosphate binder, MgO particles are distributed evenly at the interface in almost all the parts of the composite ingot. [

Elastic modulus of SiC_w/6061Al alloy composites as-squeeze-cast

By using the system of image analyzer connected with scanning electron microscope, the whisker orientation in the SiC w/6061Al alloy composite as squeeze cast was measured. According to the shear lag model and the actual distribution function of whisker in composite, the inhomogeneity of elastic modulus in composite was analyzed. With the method of ultrasonic velocity, the elastic modulus of composite was measured. The results showed that, the whiskers of composite are preferred in an orientation normal to the direction of squeeze cast. The higher the volume fraction of whisker, the more extent of preferred orientation of it, and the inhomogeneity of elastic modulus is mainly due to the differences of whisker distribution in composite.

Mixed rare earth metal conversion coatings on 2024 alloy and Al6061/SiC_p metal matrix composites

The processes of mixed rare earth metal (REM) conversion coatings on 2024 alloy and Al6061/SiC p metal matrix composites (MMC) were introduced. The coatings were examined to be honeycomb like feature by scanning electron microscope. X ray diffraction analysis revealed that the coatings are amorphous structure. The results of X ray photoelectron spectroscopy indicated that the mixed REM conversion coatings consist predominantly of Ce and O, the contents of other rare earth elements (such as La, Pr) are relatively low, the coatings are about 2～4 μm thickness with excellent adhesion and wearability. The results of mass loss test showed that the mixed REM conversion coatings produce corrosion resistant surface of 2024 alloy and Al6061/SiC p. [

Processing and mechanical properties of SiC particulate reinforced AZ91 composites fabricated by stir casting

The influence of stirring parameters (stirring temperature, stirring speed and stirring time) on the particle distribution of 10%(volume fraction) SiC particulate reinforced AZ91 composites (SiCp/AZ91) was studied. It is found that it is necessary for 10μm SiC particulate reinforced AZ91 composites to stir the molten composites in semi-solid condition with vortex formation, or else the cluster of the reinforcements would not be eliminated. Compared with the monolithic alloy, the SiCp/AZ91 composite has higher strength, especially for yield strength, but the elongation is reduced. For the as-cast composite, the particles often segregate within the grain boundary regions. Extrusion can effectively reduce the segregation of SiC particles and improve the mechanical properties of the composite. The extrusion-induced reduction in particle size varies with extrusion temperatures and extrusion ratios. The effect of extrusion-induced reduction in particle size on the mechanical properties of the composites is not always beneficial.

Preparation and oxidation property of ZrB_2-MoSi_2/SiC coating on carbon/carbon composites

To improve the oxidation resistance of carbon/carbon composites,ZrB2-MoSi2/SiC coating on the carbon/carbon substrate was prepared.The inner coating of SiC was prepared by pack cementation and the outer coating of ZrB2-MoSi2 was prepared by slurry painting.The phase compositions and microstructures of the coating were characterized by XRD and SEM,respectively.The preparation and the high temperature oxidation property of the coated composites were investigated.The results show that the outer coating of carbon/carbon composites is composed of ZrB2,MoSi2 and SiC phases.The mass losses of the ZrB2-MoSi2/SiC coated samples with SiC nano-whiskers after 30 h and 10 h of oxidation at 1 273 K and 1 773 K were,respectively,5.3% and 3.0%.The ZrB2-MoSi2/SiC coated samples exhibit self-sealing performance and good oxidation resistance at high temperature.

C/SiC/MoSi_2-SiC-Si multilayer coating for oxidation protection of carbon/carbon composites

C/SiC/MoSi2-SiC-Si oxidation protective multilayer coating for carbon/carbon （C/C） composites was prepared by pack cementation and slurry method. The microstructure, element distribution and phase composition of the as-received coating were analyzed by scanning electron microscopy （SEM）, energy dispersive X-ray spectroscopy （EDS） and X-ray diffraction （XRD）. The results show that the multilayer coating was composed of MoSi2, SiC and Si. It could effectively protect C/C composites against oxidation for 200 h with the mass loss of 3.25% at 1873 K in static air. The mass loss of the coated C/C composites results from the volatilization of SiO2 and the formation of cracks and bubble holes in the coating.

Double SiC coating on carbon/carbon composites against oxidation by a two-step method

To improve the oxidation resistance of C/C composites, a double SiC protective coating was prepared by a two-step technique. Firstly, the inner SiC layer was prepared by a pack cementation technique, and then an outer uniform and compact SiC coating was obtained by low pressure chemical vapor deposition. The microstructures and phase compositions of the coatings were characterized by SEM, EDS and XRD analyses. Oxidation behaviour of the SiC coated C/C composites was also investigated. It was found that the double SiC coating could protect C/C composites against oxidation at 1773 K in air for 178 h with a mass loss of 1.25%. The coated samples also underwent thermal shocks between 1773 K and room temperature 16 times. The mass loss of the coated C/C composites was only 2.74%. Double SiC layer structures were uniform and dense, and can suppress the generation of thermal stresses, facilitating an excellent anti-oxidation coating.

Thermal analysis for brake disks of SiC/6061 Al alloy co-continuous composite for CRH3 during emergency braking considering airflow cooling

The mass of high-speed trains can be reduced using the brake disk prepared with SiC network ceramic frame reinforced 6061 aluminum alloy composite （SiCn/Al）. The thermal and stress analyses of SiCn/Al brake disk during emergency braking at a speed of 300 km/h considering airflow cooling were investigated using finite element （FE） and computational fluid dynamics （CFD） methods. All three modes of heat transfer （conduction, convection and radiation） were analyzed along with the design features of the brake assembly and their interfaces. The results suggested that the higher convection coefficients achieved with airflow cooling will not only reduce the maximum temperature in the braking but also reduce the thermal gradients, since heat will be removed faster from hotter parts of the disk. Airflow cooling should be effective to reduce the risk of hot spot formation and disc thermal distortion. The highest temperature after emergency braking was 461 °C and 359 °C without and with considering airflow cooling, respectively. The equivalent stress could reach 269 MPa and 164 MPa without and with considering airflow cooling, respectively. However, the maximum surface stress may exceed the material yield strength during an emergency braking, which may cause a plastic damage accumulation in a brake disk without cooling. The simulation results are consistent with the experimental results well.

Microstructures and properties of Al-50%SiC composites for electronic packaging applications

Al？50%SiC （volume fraction） composites containing different sizesofSiC particles （average sizesof 23, 38 and 75 μm） were prepared by powder metallurgy. The influences of SiC particle sizes and annealing on the propertiesof the compositeswere investigated. The results show that SiC particles are distributed uniformly in the Al matrix. The coarse SiC particles result in higher coefficient of thermal expansion （CTE） and higher thermal conductivity （TC）, while fine SiC particles decrease CTE and improve flexural strength of the composites. The morphology and size of SiC particles in the composite are not influenced by the annealing treatment at 400℃for 6h. However, the CTE and the flexural strength of annealed composites are decreased slightly, and the TCis improved. The TC, CTE and flexural strength of the Al/SiC composite with averageSiC particlesize of75 μm are 156 W/（m·K）, 11.6×10^-6K^-1 and 229 MPa, respectively.

Effect of ZrC-SiC content on microstructure and ablation properties of C/C composites

C/C-ZrC-SiC composites with different ZrC-SiC contents were fabricated by precursor infiltration and pyrolysis. The effect of ceramic content on the microstructure and ablation resistance was investigated. Both the C/C-SiC and C/C-ZrC-SiC composites exhibited good ablation resistance under the plasma flame above 2300℃. Withtheincreaseof ZrC content, a continuous oxide layer and a solid Zr-Si-O mesophase were formed during the ablation. And the structure of the formed oxides layer closely linked with the contents of ZrC-SiC ceramics. The solid ZrO2-ZrC and Zr-Si-O mesophase could increase the viscosity of SiO2 moderately and improve the anti-scouring ability. The continuous SiO2-ZrO2-ZrC-SiC layer would serve as a thermal and oxygen barrier for preventing the substratefrom further ablation. The C/C-ZrC-SiC composites with 27.2%ZrC and 7.56%SiC shows superior ablation resistance, and the mass and linear ablation rates are-3.51 mg/s and-1.88 μm/s, respectively.

Microstructure and interface thermal stability of C/Mo double-coated SiC fiber reinforced γ-TiAl matrix composites

C/Mo duplex coating interfacially modified SiC fiber-reinforced γ-TiAl matrix composite （SiCf/C/Mo/γ-TiA1） was prepared by foil-fiber-foil method to investigate its interfacial modification effect. SiCf/C/TiAl composites were also prepared under the same processing condition for comparision. Both kinds of the composites were thermally exposed in vacuum at 800 and 900℃ for different durations in order to study thermal stability of the interfacial zone. With the aids of scanning electron microscope （SEM） and energy dispersive spectrometer （EDS）, the interracial microstructures of the composites were investigated. The results reveal that, although adding the Mo coating, the interfacial reaction product of the SiCf/C/Mo/TiAl composite is the same with that of the SiCf/C/TiA1 composite, which is TiC/Ti2AlC between the coating and the matrix. However, C/Mo duplex coating is more efficient in hindering interfacial reaction than C single coating at 900 ℃ and below. In addition, a new layer of interfacial reaction product was found between Ti2AlC and the matrix after 900 ℃, 200 h thermal exposure, which is rich in V and close to the chemical composition of B2 phase.