TA1 P-Ti/AA6061 composite plate was produced by oxidizing the surface of the titanium plate and adopting a cold roll bonding process.The results revealed that the oxide film(Ti6O)prepared on the surface of TA1 pure ti...TA1 P-Ti/AA6061 composite plate was produced by oxidizing the surface of the titanium plate and adopting a cold roll bonding process.The results revealed that the oxide film(Ti6O)prepared on the surface of TA1 pure titanium was easy to crack during the cold roll bonding,thereby promoting the formation of an effective mechanical interlock at the interface,which can effectively reduce the minimum reduction rate of the composite plates produced by cold rolling of titanium and aluminium plates.Moreover,the composite plate subjected to oxidation treatment exhibited high shear strength,particularly at a 43%reduction rate,achieving a commendable value of 117 MPa.Based on oxidation treatment and different reduction rates,the annealed composite plates at temperatures of 400,450,and 500°C displayed favorable resistance to interface delamination,highlighting their remarkable strength-plasticity compatibility as evidenced by a maximum elongation of 31.845%.展开更多
50 vol.% SiCp/Al composites with high thermal and mechanical properties were successfully produced by spark plasma sintering technique. The influences of sintering temperature on the thermal conductivity, coefficient ...50 vol.% SiCp/Al composites with high thermal and mechanical properties were successfully produced by spark plasma sintering technique. The influences of sintering temperature on the thermal conductivity, coefficient of thermal expansion and bending strength of the SiCp/Al composites were carefully investigated. The results show that the SiCp/Al composites sintered at 520℃ exhibits a thermal conductivity of 189 W/(m·K), a coefficient of thermal expansion (50.200℃) of 10.03×10^-6 K^-1 and a bending strength of 649 MPa. The high thermal and mechanical properties can be ascribed to the nearly full density and the well interfacial bonding between the alloy matrix and the SiC particles. This work provides a promising pathway for producing materials to meet the needs of high performance electronic packaging.展开更多
A double layer Rare Earth Metal (REM) conversion coating process of Al 6061/SiCp metal matrix composites (MMC) was studied.The corrosion resistance of REM conversion coating was examined by electrochemical impedance s...A double layer Rare Earth Metal (REM) conversion coating process of Al 6061/SiCp metal matrix composites (MMC) was studied.The corrosion resistance of REM conversion coating was examined by electrochemical impedance spectroscopy (EIS).REM conversion coating produced very corrosion resistant surface of Al 6061/SiCp MMC.The X ray diffraction (XRD) analysis revealed that REM conversion coatings exhibited non crystalline structure.The composition of REM conversion coating was studied by X ray photoelectron spectroscopy (XPS).The coatings consisted of cerium oxide and hydrated cerium oxide.Some of Ce3+were oxidized to Ce4+during the formation of the first layer coating in the solution containing Ce3+.During the course of exposing the specimens in open air,some of the residual Ce3+were oxidized to Ce4+.REM conversion coating formed in the solution containing Ce4+consisted entirely of Ce4+compounds.展开更多
Silicon carbide particulate (SiCp) reinforced cast aluminium (A1) based metal matrix composites (MMCs) have gained wide acceptance in the fabrication of light weight structures requiring high specific strength, ...Silicon carbide particulate (SiCp) reinforced cast aluminium (A1) based metal matrix composites (MMCs) have gained wide acceptance in the fabrication of light weight structures requiring high specific strength, high temperature capability and good wear resistance. Friction stir welding (FSW) process parameters play major role in deciding the performance of welded joints. The ultimate tensile strength, notch tensile strength and weld nugget hardness of friction stir butt welded joints of cast A1/SiCp MMCs (AA6061 with 20% (volume fraction) of SiCp) were investigated. The relationships between the FSW process parameters (rotational speed, welding speed and axial force) and the responses (ultimate tensile strength, notch tensile strength and weld nugget hardness) were established. The optimal welding parameters to maximize the mechanical properties were identified by using desirability approach. From this investigation, it is found that the joints fabricated with the tool rotational speed of 1370 r/min, welding speed of 88.9 mm/min, and axial force of 9.6 kN yield the maximum ultimate tensile strength, notch tensile strength and hardness of 265 MPa, 201 MPa and HV 114, respectively.展开更多
Based on theories of heat transfer, physical metallurgy and hydro-mechanical, in order to analyze the effect of welding parameters on species and distribution of reinforcing phases visually and legibly,finite element ...Based on theories of heat transfer, physical metallurgy and hydro-mechanical, in order to analyze the effect of welding parameters on species and distribution of reinforcing phases visually and legibly,finite element software ANSYS was used to simulate transient temperature field for SiCp/AI in "in-situ" weld-alloying/plasma arc welding. The results show that the calculated results approximately agreed with the experimental measured results. So the model is basically correct and credible., Based on the numerical solutions and experimental results, effect of temperature field in different welding process parameters(welding current, welding velocity) on species and distribution of reinforcing phases is analyzed. The results show that adjusting and optimizing temperature field appropriately is an effective method to obtain welded joint with better microstructure and property.展开更多
基金supports from the National Natural Science Foundation of China(Nos.52075472,52004242)the National Key Research and Development Program of China(No.2018YFA0707300)the Natural Science Foundation of Hebei Province,China(No.E2020203001)。
文摘TA1 P-Ti/AA6061 composite plate was produced by oxidizing the surface of the titanium plate and adopting a cold roll bonding process.The results revealed that the oxide film(Ti6O)prepared on the surface of TA1 pure titanium was easy to crack during the cold roll bonding,thereby promoting the formation of an effective mechanical interlock at the interface,which can effectively reduce the minimum reduction rate of the composite plates produced by cold rolling of titanium and aluminium plates.Moreover,the composite plate subjected to oxidation treatment exhibited high shear strength,particularly at a 43%reduction rate,achieving a commendable value of 117 MPa.Based on oxidation treatment and different reduction rates,the annealed composite plates at temperatures of 400,450,and 500°C displayed favorable resistance to interface delamination,highlighting their remarkable strength-plasticity compatibility as evidenced by a maximum elongation of 31.845%.
基金Project(2014DFA50860) supported by the International Science & Technology Cooperation Program of Ministry of Science and Technology of China
文摘50 vol.% SiCp/Al composites with high thermal and mechanical properties were successfully produced by spark plasma sintering technique. The influences of sintering temperature on the thermal conductivity, coefficient of thermal expansion and bending strength of the SiCp/Al composites were carefully investigated. The results show that the SiCp/Al composites sintered at 520℃ exhibits a thermal conductivity of 189 W/(m·K), a coefficient of thermal expansion (50.200℃) of 10.03×10^-6 K^-1 and a bending strength of 649 MPa. The high thermal and mechanical properties can be ascribed to the nearly full density and the well interfacial bonding between the alloy matrix and the SiC particles. This work provides a promising pathway for producing materials to meet the needs of high performance electronic packaging.
文摘A double layer Rare Earth Metal (REM) conversion coating process of Al 6061/SiCp metal matrix composites (MMC) was studied.The corrosion resistance of REM conversion coating was examined by electrochemical impedance spectroscopy (EIS).REM conversion coating produced very corrosion resistant surface of Al 6061/SiCp MMC.The X ray diffraction (XRD) analysis revealed that REM conversion coatings exhibited non crystalline structure.The composition of REM conversion coating was studied by X ray photoelectron spectroscopy (XPS).The coatings consisted of cerium oxide and hydrated cerium oxide.Some of Ce3+were oxidized to Ce4+during the formation of the first layer coating in the solution containing Ce3+.During the course of exposing the specimens in open air,some of the residual Ce3+were oxidized to Ce4+.REM conversion coating formed in the solution containing Ce4+consisted entirely of Ce4+compounds.
文摘Silicon carbide particulate (SiCp) reinforced cast aluminium (A1) based metal matrix composites (MMCs) have gained wide acceptance in the fabrication of light weight structures requiring high specific strength, high temperature capability and good wear resistance. Friction stir welding (FSW) process parameters play major role in deciding the performance of welded joints. The ultimate tensile strength, notch tensile strength and weld nugget hardness of friction stir butt welded joints of cast A1/SiCp MMCs (AA6061 with 20% (volume fraction) of SiCp) were investigated. The relationships between the FSW process parameters (rotational speed, welding speed and axial force) and the responses (ultimate tensile strength, notch tensile strength and weld nugget hardness) were established. The optimal welding parameters to maximize the mechanical properties were identified by using desirability approach. From this investigation, it is found that the joints fabricated with the tool rotational speed of 1370 r/min, welding speed of 88.9 mm/min, and axial force of 9.6 kN yield the maximum ultimate tensile strength, notch tensile strength and hardness of 265 MPa, 201 MPa and HV 114, respectively.
基金The research was supported by the National Natural Science Foundation of China(50475126) the province graduate student innovation plan of Jiangsu(xm04-27).
文摘Based on theories of heat transfer, physical metallurgy and hydro-mechanical, in order to analyze the effect of welding parameters on species and distribution of reinforcing phases visually and legibly,finite element software ANSYS was used to simulate transient temperature field for SiCp/AI in "in-situ" weld-alloying/plasma arc welding. The results show that the calculated results approximately agreed with the experimental measured results. So the model is basically correct and credible., Based on the numerical solutions and experimental results, effect of temperature field in different welding process parameters(welding current, welding velocity) on species and distribution of reinforcing phases is analyzed. The results show that adjusting and optimizing temperature field appropriately is an effective method to obtain welded joint with better microstructure and property.