To improve the wear resistance and corrosion resistance of magnesium alloys, a 5 kW continuous wave CO2 laser was used to investigate the laser surface cladding on AZ31 B magnesium alloys with Al-Si/Al2O3-TiO2 composi...To improve the wear resistance and corrosion resistance of magnesium alloys, a 5 kW continuous wave CO2 laser was used to investigate the laser surface cladding on AZ31 B magnesium alloys with Al-Si/Al2O3-TiO2 composite powders. A detailed microstructure, chemical composition, and phase analysis of the composite coatings were studied by scanning electron microscopy （SEM）, energy dispersive spectroscopy （EDS）, and X-ray diffraction （XRD）. The laser cladding shows good metallurgical bonding with the substrate. The composite coatings are composed of Mgl7Al12, Al3Mg2, Mg2Si, Al2O3, and TiO2 phases. Compared to the average microhardness （50HV0.05） of the AZ3 1 B substrate, that of the composite coatings （230HV0.05） is improved significantly. The wear resistances of the surface layers were evaluated in detail. The results demonstrate that the wear resistances of the laser surface-modified samples are considerably improved compared to the substrate. It also show that the composite coatings exhibit better corrosion resistance than that of the substrate in 3.5wt% NaCI solution.展开更多
The wetting of molten Sn-3.5Ag-0.5Cu alloy on the Ni-P(-SiC)coated SiCp/Al substrates was investigated by electroless Ni plating process,and the microstructures of the coating and the interfacial behavior of wetting s...The wetting of molten Sn-3.5Ag-0.5Cu alloy on the Ni-P(-SiC)coated SiCp/Al substrates was investigated by electroless Ni plating process,and the microstructures of the coating and the interfacial behavior of wetting systems were analyzed.The SiC particles are evenly distributed in the coating and enveloped with Ni.No reaction layer is observed at the coating/SiCp/Al composite interfaces.The contact angle increases from^19°with the Ni-P coating to 29°,43°and 113°with the corresponding Ni-P-3SiC,Ni-P-6SiC and Ni-P-9SiC coatings,respectively.An interaction layer containing Cu,Ni,Sn and P forms at the Sn-Ag-Cu/Ni-P-(0,3,6)SiC coated SiCp/Al interfaces,and the Cu-Ni-Sn and Ni-Sn-P phases are detected in the interaction layer.Moreover,the molten Sn-Ag-Cu can penetrate into the Ni-P(-SiC)coatings through the Ni-P/SiC interface and dissolve them to contact the SiCp/Al substrate.展开更多
SiCp/Cu composites with a compact microstructure were successfully fabricated by vacuum hot-pressing method. In order to suppress the detrimental interfacial reactions and ameliorate the interfacial bonding between co...SiCp/Cu composites with a compact microstructure were successfully fabricated by vacuum hot-pressing method. In order to suppress the detrimental interfacial reactions and ameliorate the interfacial bonding between copper and silicon carbide, molybdenum coating was deposited on the surface of silicon carbide by magnetron sputtering method and crystallized heat-treatment. The effects of the interfacial design on the thermo-physical properties of Si Cp/Cu composites were studied in detail. Thermal conductivity and expansion test results showed that silicon carbide particles coated with uniform and compact molybdenum coating have improved the comprehensive thermal properties of the Si Cp/Cu composites. Furthermore, the adhesion of the interface between silicon carbide and copper was significantly strengthened after molybdenum coating. Si Cp/Cu composites with a maximum thermal conductivity of 274.056 W/（m·K） and a coefficient of thermal expansion of 9 ppm/K were successfully prepared when the volume of silicon carbide was about 50%, and these Si Cp/Cu composites have potential applications for the electronic packageing of the high integration electronic devices.展开更多
The processes of mixed rare earth metal (REM) conversion coatings on 2024 alloy and Al6061/SiC p metal matrix composites (MMC) were introduced. The coatings were examined to be honeycomb like feature by scanning elect...The processes of mixed rare earth metal (REM) conversion coatings on 2024 alloy and Al6061/SiC p metal matrix composites (MMC) were introduced. The coatings were examined to be honeycomb like feature by scanning electron microscope. X ray diffraction analysis revealed that the coatings are amorphous structure. The results of X ray photoelectron spectroscopy indicated that the mixed REM conversion coatings consist predominantly of Ce and O, the contents of other rare earth elements (such as La, Pr) are relatively low, the coatings are about 2～4 μm thickness with excellent adhesion and wearability. The results of mass loss test showed that the mixed REM conversion coatings produce corrosion resistant surface of 2024 alloy and Al6061/SiC p. [展开更多
The SiCp(20 %)reinforced cobalt-based alloy composite coatings deposited by laser cladding on IF steel were introduced.The microstructure across the whole section of such coatings was examined using optical microscope...The SiCp(20 %)reinforced cobalt-based alloy composite coatings deposited by laser cladding on IF steel were introduced.The microstructure across the whole section of such coatings was examined using optical microscope,scanning electron microscope(SEM)and X-ray diffractometer(XRD),and the wear resistance of the coatings was measured by MM-200 type wear testing machine.The results show that the SiCpis completely dissolved during laser cladding and the primary phase in the coatings isγ-Co.The other phases,such as Si2 W,CoWSi,Cr3 Si and CoSi2,are formed by carbon,silicon reacting with other elements existing in the melting pool.There are various crystallization morphologies in different zones,such as planar crystallization at the interface,followed by cellular and dendrite crystallization from interface to the surface.The direction of solidification changes from one direction perpendicular to interface to multi-directions at the central and upper regions of the clad.The wear resistance of the clad is improved by adding SiCp.展开更多
This paper evaluated the protection effect of the cerium conversion coatings on the SiCp/5A06 Al composite and the 5A06 Al alloy.Electrochemical impedance spectroscopy(EIS) was employed to examine the variation of the...This paper evaluated the protection effect of the cerium conversion coatings on the SiCp/5A06 Al composite and the 5A06 Al alloy.Electrochemical impedance spectroscopy(EIS) was employed to examine the variation of the electrochemical variables of the samples treated and immersed in 3.5% NaCl solution at 35 °C for 1 h,which showed the enhancement of charge transfer resistance(Rt) and coating film resistance(Rc),i.e.,the corrosion resistance of the conversion coated samples was improved.The best protection ef...展开更多
The reactive process for Al/SiC P composite was studied. SiC particles were in situ coated by the exothermal reaction of SiC Ti powder compact in Al melt bath, and easily incorporated into Al melt. The detailed study ...The reactive process for Al/SiC P composite was studied. SiC particles were in situ coated by the exothermal reaction of SiC Ti powder compact in Al melt bath, and easily incorporated into Al melt. The detailed study was carried out to understand the microstructures of the reacted SiC particles. During the reaction and consequent mixing, the successive processes include in situ coating on the reacted SiC particles, coat dissolution and SiC P splitting. The tensile mechanical properties of 6013Al/SiC P composite processed by the present technology showed that the reacted SiC P considerably reinforced the 6013 matrix.展开更多
This article studies the effects of the CeCl3 concentrations in conversion solutions with and without addition of NaCl, pH-values of conversion solution, drying temperature, time and temperature of immersion on the Ce...This article studies the effects of the CeCl3 concentrations in conversion solutions with and without addition of NaCl, pH-values of conversion solution, drying temperature, time and temperature of immersion on the Ce-conversion coatings for corrosion protection of the SiCp/5A06 Al-MMC and 5A06 Al-alloy in the 3.5% NaCl aqueous solution at room temperature. Potentiodynamic polarization tests reveal that the Ce-conversion treatment could markedly improve the pitting corrosion resistance of the composite and the matrix alloy in chloride containing environment. The best corrosion resistance effects are obtained for the samples treatment in 1% CeCl3.7H2O/3.5% NaCl solution at 45℃ for 60 min, followed by drying at 100 ℃ for 30 min. Examinations by means of scanning electron microscopy （SEM）, energy dispersion spectroscopy （EDS） and X-ray photoelectron spectroscopy （XPS） indicate that this behavior is due to the precipitation of Ce-oxides/hydroxides on the cathodic intermetallics and the Al-oxide film on the rest of the metal matrix.展开更多
基金Funded by the national Natural Science Foundation of China (No. 51075293)the Foundation for Development of Science and Technology of Taiyuan University of Technology,China(No.K201014)
文摘To improve the wear resistance and corrosion resistance of magnesium alloys, a 5 kW continuous wave CO2 laser was used to investigate the laser surface cladding on AZ31 B magnesium alloys with Al-Si/Al2O3-TiO2 composite powders. A detailed microstructure, chemical composition, and phase analysis of the composite coatings were studied by scanning electron microscopy （SEM）, energy dispersive spectroscopy （EDS）, and X-ray diffraction （XRD）. The laser cladding shows good metallurgical bonding with the substrate. The composite coatings are composed of Mgl7Al12, Al3Mg2, Mg2Si, Al2O3, and TiO2 phases. Compared to the average microhardness （50HV0.05） of the AZ3 1 B substrate, that of the composite coatings （230HV0.05） is improved significantly. The wear resistances of the surface layers were evaluated in detail. The results demonstrate that the wear resistances of the laser surface-modified samples are considerably improved compared to the substrate. It also show that the composite coatings exhibit better corrosion resistance than that of the substrate in 3.5wt% NaCI solution.
基金Projects(51572112,51401034)supported by the National Natural Science Foundation of ChinaProject(BK20151340)supported by the Natural Science Foundation of Jiangsu Province,China+3 种基金Projects(2014-XCL-002,TD-XCL-004)supported by the Six Talent Peaks Project of Jiangsu Province,ChinaProject(BRA2017387)supported by the 333 Talents Project of Jiangsu Province,ChinaProject([2015]26)supported by the Innovation/Entrepreneurship Program of Jiangsu Province,ChinaProject([2016]15)supported by the Qing Lan Project,China
文摘The wetting of molten Sn-3.5Ag-0.5Cu alloy on the Ni-P(-SiC)coated SiCp/Al substrates was investigated by electroless Ni plating process,and the microstructures of the coating and the interfacial behavior of wetting systems were analyzed.The SiC particles are evenly distributed in the coating and enveloped with Ni.No reaction layer is observed at the coating/SiCp/Al composite interfaces.The contact angle increases from^19°with the Ni-P coating to 29°,43°and 113°with the corresponding Ni-P-3SiC,Ni-P-6SiC and Ni-P-9SiC coatings,respectively.An interaction layer containing Cu,Ni,Sn and P forms at the Sn-Ag-Cu/Ni-P-(0,3,6)SiC coated SiCp/Al interfaces,and the Cu-Ni-Sn and Ni-Sn-P phases are detected in the interaction layer.Moreover,the molten Sn-Ag-Cu can penetrate into the Ni-P(-SiC)coatings through the Ni-P/SiC interface and dissolve them to contact the SiCp/Al substrate.
基金Funded by the China Aerospace Science&Industry Corp
文摘SiCp/Cu composites with a compact microstructure were successfully fabricated by vacuum hot-pressing method. In order to suppress the detrimental interfacial reactions and ameliorate the interfacial bonding between copper and silicon carbide, molybdenum coating was deposited on the surface of silicon carbide by magnetron sputtering method and crystallized heat-treatment. The effects of the interfacial design on the thermo-physical properties of Si Cp/Cu composites were studied in detail. Thermal conductivity and expansion test results showed that silicon carbide particles coated with uniform and compact molybdenum coating have improved the comprehensive thermal properties of the Si Cp/Cu composites. Furthermore, the adhesion of the interface between silicon carbide and copper was significantly strengthened after molybdenum coating. Si Cp/Cu composites with a maximum thermal conductivity of 274.056 W/（m·K） and a coefficient of thermal expansion of 9 ppm/K were successfully prepared when the volume of silicon carbide was about 50%, and these Si Cp/Cu composites have potential applications for the electronic packageing of the high integration electronic devices.
文摘The processes of mixed rare earth metal (REM) conversion coatings on 2024 alloy and Al6061/SiC p metal matrix composites (MMC) were introduced. The coatings were examined to be honeycomb like feature by scanning electron microscope. X ray diffraction analysis revealed that the coatings are amorphous structure. The results of X ray photoelectron spectroscopy indicated that the mixed REM conversion coatings consist predominantly of Ce and O, the contents of other rare earth elements (such as La, Pr) are relatively low, the coatings are about 2～4 μm thickness with excellent adhesion and wearability. The results of mass loss test showed that the mixed REM conversion coatings produce corrosion resistant surface of 2024 alloy and Al6061/SiC p. [
基金Item Sponsored by International Government Cooperation Projects of Sino-Korea(2002009)and Sino-America(01088013)
文摘The SiCp(20 %)reinforced cobalt-based alloy composite coatings deposited by laser cladding on IF steel were introduced.The microstructure across the whole section of such coatings was examined using optical microscope,scanning electron microscope(SEM)and X-ray diffractometer(XRD),and the wear resistance of the coatings was measured by MM-200 type wear testing machine.The results show that the SiCpis completely dissolved during laser cladding and the primary phase in the coatings isγ-Co.The other phases,such as Si2 W,CoWSi,Cr3 Si and CoSi2,are formed by carbon,silicon reacting with other elements existing in the melting pool.There are various crystallization morphologies in different zones,such as planar crystallization at the interface,followed by cellular and dendrite crystallization from interface to the surface.The direction of solidification changes from one direction perpendicular to interface to multi-directions at the central and upper regions of the clad.The wear resistance of the clad is improved by adding SiCp.
基金supported by Higher Education Commission of Pakistan
文摘This paper evaluated the protection effect of the cerium conversion coatings on the SiCp/5A06 Al composite and the 5A06 Al alloy.Electrochemical impedance spectroscopy(EIS) was employed to examine the variation of the electrochemical variables of the samples treated and immersed in 3.5% NaCl solution at 35 °C for 1 h,which showed the enhancement of charge transfer resistance(Rt) and coating film resistance(Rc),i.e.,the corrosion resistance of the conversion coated samples was improved.The best protection ef...
文摘The reactive process for Al/SiC P composite was studied. SiC particles were in situ coated by the exothermal reaction of SiC Ti powder compact in Al melt bath, and easily incorporated into Al melt. The detailed study was carried out to understand the microstructures of the reacted SiC particles. During the reaction and consequent mixing, the successive processes include in situ coating on the reacted SiC particles, coat dissolution and SiC P splitting. The tensile mechanical properties of 6013Al/SiC P composite processed by the present technology showed that the reacted SiC P considerably reinforced the 6013 matrix.
文摘This article studies the effects of the CeCl3 concentrations in conversion solutions with and without addition of NaCl, pH-values of conversion solution, drying temperature, time and temperature of immersion on the Ce-conversion coatings for corrosion protection of the SiCp/5A06 Al-MMC and 5A06 Al-alloy in the 3.5% NaCl aqueous solution at room temperature. Potentiodynamic polarization tests reveal that the Ce-conversion treatment could markedly improve the pitting corrosion resistance of the composite and the matrix alloy in chloride containing environment. The best corrosion resistance effects are obtained for the samples treatment in 1% CeCl3.7H2O/3.5% NaCl solution at 45℃ for 60 min, followed by drying at 100 ℃ for 30 min. Examinations by means of scanning electron microscopy （SEM）, energy dispersion spectroscopy （EDS） and X-ray photoelectron spectroscopy （XPS） indicate that this behavior is due to the precipitation of Ce-oxides/hydroxides on the cathodic intermetallics and the Al-oxide film on the rest of the metal matrix.