Bonding enhancement of cold rolling TA1 P-Ti/AA6061 composite plates via surface oxidation treatment

TA1 P-Ti/AA6061 composite plate was produced by oxidizing the surface of the titanium plate and adopting a cold roll bonding process.The results revealed that the oxide film(Ti6O)prepared on the surface of TA1 pure titanium was easy to crack during the cold roll bonding,thereby promoting the formation of an effective mechanical interlock at the interface,which can effectively reduce the minimum reduction rate of the composite plates produced by cold rolling of titanium and aluminium plates.Moreover,the composite plate subjected to oxidation treatment exhibited high shear strength,particularly at a 43%reduction rate,achieving a commendable value of 117 MPa.Based on oxidation treatment and different reduction rates,the annealed composite plates at temperatures of 400,450,and 500°C displayed favorable resistance to interface delamination,highlighting their remarkable strength-plasticity compatibility as evidenced by a maximum elongation of 31.845%.

ROLES OF ORIENTATION RELATIONSHIP AND RECRYSTALLIZATION IN SUPERPLASTICITY OF SiCw/6061Al COMPOSITE

ＲＯＬＥＳＯＦＯＲＩＥＮＴＡＴＩＯＮＲＥＬＡＴＩＯＮＳＨＩＰＡＮＤＲＥＣＲＹＳＴＡＬＬＩＺＡＴＩＯＮＩＮＳＵＰＥＲＰＬＡＳＴＩＣＩＴＹＯＦＳｉＣｗ／６０６１ＡｌＣＯＭＰＯＳＩＴＥ①ＧｕＷａｎｌｉ，ＰｅｎｇＨｕａｘｉｎ，ＬｉｕＺｏｎｇｒｏｎｇ，Ｗａｎｇ...

EFFECTS OF DIFFUSION WELDING PARAMETERS ON JOINT STRENGTH OF SiCw/6061AI COMPOSITE

Diffusion welding was used to join SiCw/6061AI composites. The effects of welding pammeters on strength Of welded joint were investigated. JOint Of high quality for SiCw/6061Al composites can be obtained with aPPropriate diffesion welding parameters.

Effect of low temperature treatment on tensile yield strength of SiC_w/6061 Al alloy composites

The effect of the low temperature treatment at -78 ℃ and -196 ℃ on the microstructure and properties of 18%SiC w/6061(volume fraction) Al alloy composites of as squeeze casting were studied. The results show that, after the low temperature treatment, the dislocation density in matrix increases, and the residual stress of the matrix decreases, as well as the tensile yield strength of the composites improves. The high residual stress exists in the matrix of the composites of as original squeeze casting. The mismatch degree between the matrix and SiC w phases increases during the low temperature treatment. The matrix undergoes the tensile plastic deformation during the cooling procedure. On the contrary, the matrix encountered an elastic unloading procedure during the heating up process from low temperature to room temperature. The increase of dislocation density and the decrease of residual stress in the matrix are the main reason of the improvement for tensile yield strength of the composites.

反挤压对SiCw/6061力学性能影响的实验研究

以挤压工艺对SiCw/6061复合材料力学性能的影响为研究目标,通过改变挤压温度、挤压比以及凸模中心锥角等工艺参数,系统分析了挤压铸造制备的SiCw/6061复合材料反挤压变形前后强度、塑性及硬度的变化规律。研究表明,挤压变形可以有效地提升复合材料试件的各项力学性能指标;随着挤压温度的升高,试件的屈服强度、抗拉强度均呈现升高的变化趋势,延伸率先显著增大而后略有减小,硬度则呈现下降的趋势;随着挤压比的增加,试件的强度、塑性及硬度均呈现上升趋势;随着凸模中心锥角的增大,试件的屈服强度、抗拉强度均呈现先升高后下降的趋势,延伸率及硬度则随着锥角的增加始终呈上升趋势。

DIFFUSION WELDING FOR 6061 Al REINFORCED WITH SiCw WHISKER

The weldability of SiCw/6061Al -was investigated. From the results of experiments, it is found that the strength of joint is mainly influenced by welding temperature, and high strength of joint is obtained under melding temperature between liquidus and solidus of matrix alloy. Diffusion welding of SiCw/6061Al was successfully realized with appropriate ivelding parameters.

脉冲激光在SiCw/6061A1铝基复合材料焊接中的应用

采用脉冲激光进行诱导焊接SiCw／6061A1铝基复合材料，研究了激光功率、脉冲频率、表面处理状态等工艺参数对接头强度的影响。结果表明：激光功率是影响焊缝质量的主要因素，通过控制激光束输出功率可以有效抑制熔池中SiC晶须与基体铝合金的界面反应，成功地实现SiCw／6061A1铝基复合材料的连接。