We investigate the molecular-beam-epitaxy growth of highly relaxed Si0.45 Ge0.55 films with very low dislocation densities. By using the Si3N4 film as the mask material, the Si0.45Ge0.55 film can be grown on a composi...We investigate the molecular-beam-epitaxy growth of highly relaxed Si0.45 Ge0.55 films with very low dislocation densities. By using the Si3N4 film as the mask material, the Si0.45Ge0.55 film can be grown on a compositionally stepwise graded SiGe buffer layer in 3 μm× 3 μm windows on a Si （001） substrate. Raman scattering spectroscopy measurement shows that more than 90% strain of the Si0.45Ge0.55 film is relaxed, and almost neither misfit dislocation lines nor etch pits of thread dislocations could be observed when the sample is etched by the modified Schimmel etchant. We suggest that the results can be explained by influence of the edge-induced strain relaxation of the epitaxial film and the edge-induced stress of the mask material.展开更多
基金Supported by the National Natural Science Foundation of China under Grant No 60376012, and the State Key Laboratory of Functional Materials of Informatics, Chinese Academy of Sciences.
文摘We investigate the molecular-beam-epitaxy growth of highly relaxed Si0.45 Ge0.55 films with very low dislocation densities. By using the Si3N4 film as the mask material, the Si0.45Ge0.55 film can be grown on a compositionally stepwise graded SiGe buffer layer in 3 μm× 3 μm windows on a Si （001） substrate. Raman scattering spectroscopy measurement shows that more than 90% strain of the Si0.45Ge0.55 film is relaxed, and almost neither misfit dislocation lines nor etch pits of thread dislocations could be observed when the sample is etched by the modified Schimmel etchant. We suggest that the results can be explained by influence of the edge-induced strain relaxation of the epitaxial film and the edge-induced stress of the mask material.