An antireflection （AR） coating is fabricated by applying an optimal spin-coating method and a pH-modified SiO2 nanoparticle solution on a cover glass. Because the pH value of the solution will affect the aggregation...An antireflection （AR） coating is fabricated by applying an optimal spin-coating method and a pH-modified SiO2 nanoparticle solution on a cover glass. Because the pH value of the solution will affect the aggregation and dispersion of the SiO2 particles, the transmittance of the AR-treated cover glass will be enhanced under optimal fabricated conditions. The experimental results show that an AR coating fabricated by an SiO2 nano- particle solution of pH 11 enhances the transmittance approximately by 3% and 5% under normal and oblique incident conditions, respectively. Furthermore, the AR-treated cover glass exhibits hydrophobicity and shows a 65% enhancement at a contact angle to bare glass.展开更多
A white substance was got by directly heating TiSi powder on Ti foil, under Ar+O2 atmosphere. ED, EDX, SEM and HRTEM studies reveal that the white substance consists of amorphous SiO2nanowires of smooth surface and un...A white substance was got by directly heating TiSi powder on Ti foil, under Ar+O2 atmosphere. ED, EDX, SEM and HRTEM studies reveal that the white substance consists of amorphous SiO2nanowires of smooth surface and uniform diameter (40-90 nm). X-ray-induced luminescent emission experiment shows that two broad peaks are at 430 and 570 nm. A one-dimensional growth mechanism, on the basis of the one-dimensional thermal flow during nanowire formation, is discussed.展开更多
基金financially supporting this research under Contract No. NSC 102-2221-E-155-076-MY3
文摘An antireflection （AR） coating is fabricated by applying an optimal spin-coating method and a pH-modified SiO2 nanoparticle solution on a cover glass. Because the pH value of the solution will affect the aggregation and dispersion of the SiO2 particles, the transmittance of the AR-treated cover glass will be enhanced under optimal fabricated conditions. The experimental results show that an AR coating fabricated by an SiO2 nano- particle solution of pH 11 enhances the transmittance approximately by 3% and 5% under normal and oblique incident conditions, respectively. Furthermore, the AR-treated cover glass exhibits hydrophobicity and shows a 65% enhancement at a contact angle to bare glass.
基金This work was supported by the Committee of Education of Hubei Province (Grant No.2000A09011).
文摘A white substance was got by directly heating TiSi powder on Ti foil, under Ar+O2 atmosphere. ED, EDX, SEM and HRTEM studies reveal that the white substance consists of amorphous SiO2nanowires of smooth surface and uniform diameter (40-90 nm). X-ray-induced luminescent emission experiment shows that two broad peaks are at 430 and 570 nm. A one-dimensional growth mechanism, on the basis of the one-dimensional thermal flow during nanowire formation, is discussed.