(PEO)8LiClO4-SiO2 composite polymer electrolytes(CPEs)were prepared by in-situ reaction,in which ethyl-orthosilicate(TEOS)was catalyzed by HCl and NH3.H2O,respectively.The ionic conductivity,the contact angle and the ...(PEO)8LiClO4-SiO2 composite polymer electrolytes(CPEs)were prepared by in-situ reaction,in which ethyl-orthosilicate(TEOS)was catalyzed by HCl and NH3.H2O,respectively.The ionic conductivity,the contact angle and the morphology of inorganic particles in the CPEs were investigated by AC impedance spectra,contact angle method and TEM.The conductivities of acid-catalyzed CPE and alkali-catalyzed CPE are 2.2×10-5and 1.1×10-5S/cm respectively at 30℃.The results imply that the catalyst plays an important role in the structure of in-situ preparation of SiO2,and influences the surface energy and conductivity of CPE films directly.Meanwhile,the ionic conductivity is related to the surface energy.展开更多
The precursor infiltration and pyrolysis（PIP） method for preparation of BN/SiO2 composites was used to improve mechanical properties, dielectric properties and feasibility of high temperature dielectric parts with l...The precursor infiltration and pyrolysis（PIP） method for preparation of BN/SiO2 composites was used to improve mechanical properties, dielectric properties and feasibility of high temperature dielectric parts with large dimensions and complex shapes. In the processing procedure, the porous BN ceramic matrix was first successfully prepared by compacting the mixed powders of B and BN and then sintering them at a certain temperature under normal pressure of N2.The polycarbosilane（PCS） solution was vacuum infiltrated into porous BN ceramics at the room temperature and then at 800℃ in the air to depolimerize out amorphous SiO2, and sintered further at 1300℃ in N2 to get BN/SiO2 composites. The microstructure of materials was studied by means of X-ray diffraction and electron probe micro （analysis.） The thermo-decomposition mechanism of PCS was investigated by a TG-DTA and infrared （IR） spectrum analysis. The flexural strengths were measured by the three-point bending method. The dielectric constant and the loss tangent were measured by the wave-guide method. The results show BN/SiO2 composites were fabricated. The obtained composites posses a flexural strength of 61.96-93.31MPa, the dielectric constant in the range of 3.50-3.78 and the order of magnitude of the loss tangent at 10-3, which are good for the high temperature dielectric parts with large size and complex shapes.展开更多
The high temperature dielectrics of Quartz fiber-reinforced silicon dioxide ceramic （Si02/SiO2 ） composites were studied both theoretically and experimentally. A multi-scale theoretical model was developed based on ...The high temperature dielectrics of Quartz fiber-reinforced silicon dioxide ceramic （Si02/SiO2 ） composites were studied both theoretically and experimentally. A multi-scale theoretical model was developed based on the theory of dielectrics. It was realized to predict dielectric properties at higher temperature （ 〉 1200 ℃） by experimental data mining for correlative coefficients in model. The results show that the dielectrics of SiO2/SiO2, which were calculated with the theoretical model, were in agreement with experimental measured value.展开更多
基金Supported by the National Natural Science Foundation of China(61674161,61504083)Open Project of State Key Laboratory of Functional Materials for Informatics,Public welfare capacity building in Guangdong Province(2015A010103016)the Science and Technology Foundation of Shenzhen(JCYJ20160226192033020)
文摘(PEO)8LiClO4-SiO2 composite polymer electrolytes(CPEs)were prepared by in-situ reaction,in which ethyl-orthosilicate(TEOS)was catalyzed by HCl and NH3.H2O,respectively.The ionic conductivity,the contact angle and the morphology of inorganic particles in the CPEs were investigated by AC impedance spectra,contact angle method and TEM.The conductivities of acid-catalyzed CPE and alkali-catalyzed CPE are 2.2×10-5and 1.1×10-5S/cm respectively at 30℃.The results imply that the catalyst plays an important role in the structure of in-situ preparation of SiO2,and influences the surface energy and conductivity of CPE films directly.Meanwhile,the ionic conductivity is related to the surface energy.
文摘The precursor infiltration and pyrolysis（PIP） method for preparation of BN/SiO2 composites was used to improve mechanical properties, dielectric properties and feasibility of high temperature dielectric parts with large dimensions and complex shapes. In the processing procedure, the porous BN ceramic matrix was first successfully prepared by compacting the mixed powders of B and BN and then sintering them at a certain temperature under normal pressure of N2.The polycarbosilane（PCS） solution was vacuum infiltrated into porous BN ceramics at the room temperature and then at 800℃ in the air to depolimerize out amorphous SiO2, and sintered further at 1300℃ in N2 to get BN/SiO2 composites. The microstructure of materials was studied by means of X-ray diffraction and electron probe micro （analysis.） The thermo-decomposition mechanism of PCS was investigated by a TG-DTA and infrared （IR） spectrum analysis. The flexural strengths were measured by the three-point bending method. The dielectric constant and the loss tangent were measured by the wave-guide method. The results show BN/SiO2 composites were fabricated. The obtained composites posses a flexural strength of 61.96-93.31MPa, the dielectric constant in the range of 3.50-3.78 and the order of magnitude of the loss tangent at 10-3, which are good for the high temperature dielectric parts with large size and complex shapes.
基金the National Defense 973 (Grant No.513180303) and National Defense Basic Scientific Research (Grant No. A2220061080)the Na-tional Defense Foundation (Grant No. 5142040205BQ0154).
文摘The high temperature dielectrics of Quartz fiber-reinforced silicon dioxide ceramic （Si02/SiO2 ） composites were studied both theoretically and experimentally. A multi-scale theoretical model was developed based on the theory of dielectrics. It was realized to predict dielectric properties at higher temperature （ 〉 1200 ℃） by experimental data mining for correlative coefficients in model. The results show that the dielectrics of SiO2/SiO2, which were calculated with the theoretical model, were in agreement with experimental measured value.
