The dissolution of alumina-based refractory ceramics in CaO-Al2O3-SiO_(2)slag melts was performed based on the in-situ observation system of an ultra-high-temperature laser confocal microscope,and the effect of the Ca...The dissolution of alumina-based refractory ceramics in CaO-Al2O3-SiO_(2)slag melts was performed based on the in-situ observation system of an ultra-high-temperature laser confocal microscope,and the effect of the CaO/SiO_(2)slag mass ratio(C/S ratio)on the dissolution rate of alumina-based refractory ceramics was investigated.The results indicate that the dissolution rate increases with an increase of the C/S ratio and is mainly controlled by diffusion.During the early stage of dissolution,for all C/S ratios,the dissolution process conforms to the classical invariant interface approximation model.During the later stage of dissolution,when the C/S ratio is≥6,the dissolution process is significantly different from the model above because of the formation of a thick interfacial layer,which can be explained by dissolution kinetics.展开更多
以几种不同的2.5D衍生结构织物为增强体,制备了法向增强、经向增强及经法向增强2.5D Si O2f/Si O2复合材料,比较了上述材料与现有2.5D Si O2f/Si O2复合材料的经向力学性能,并研究了经法向增强2.5D结构复合材料中增强纱比例、纤维体积...以几种不同的2.5D衍生结构织物为增强体,制备了法向增强、经向增强及经法向增强2.5D Si O2f/Si O2复合材料,比较了上述材料与现有2.5D Si O2f/Si O2复合材料的经向力学性能,并研究了经法向增强2.5D结构复合材料中增强纱比例、纤维体积分数与材料性能之间的关系,对织物结构进行了优化。结果表明,经法向增强2.5D Si O2f/Si O2复合材料的经向力学性能较现有2.5D复合材料有显著提高,该材料在较低密度下(1.6 g/cm3),经向拉伸强度与现有材料(1.65 g/cm3)持平,且经向压缩强度接近现有材料的4.3倍。展开更多
基金supported by the National Natural Science Foundation of China(52272022)the Special Project of Central Government for Local Science and Technology Development of Hubei Province(2019ZYYD076)the Innovation and Entrepreneurship Fund of Wuhan University of Science and Technology(D202202171045002669).
文摘The dissolution of alumina-based refractory ceramics in CaO-Al2O3-SiO_(2)slag melts was performed based on the in-situ observation system of an ultra-high-temperature laser confocal microscope,and the effect of the CaO/SiO_(2)slag mass ratio(C/S ratio)on the dissolution rate of alumina-based refractory ceramics was investigated.The results indicate that the dissolution rate increases with an increase of the C/S ratio and is mainly controlled by diffusion.During the early stage of dissolution,for all C/S ratios,the dissolution process conforms to the classical invariant interface approximation model.During the later stage of dissolution,when the C/S ratio is≥6,the dissolution process is significantly different from the model above because of the formation of a thick interfacial layer,which can be explained by dissolution kinetics.
文摘以几种不同的2.5D衍生结构织物为增强体,制备了法向增强、经向增强及经法向增强2.5D Si O2f/Si O2复合材料,比较了上述材料与现有2.5D Si O2f/Si O2复合材料的经向力学性能,并研究了经法向增强2.5D结构复合材料中增强纱比例、纤维体积分数与材料性能之间的关系,对织物结构进行了优化。结果表明,经法向增强2.5D Si O2f/Si O2复合材料的经向力学性能较现有2.5D复合材料有显著提高,该材料在较低密度下(1.6 g/cm3),经向拉伸强度与现有材料(1.65 g/cm3)持平,且经向压缩强度接近现有材料的4.3倍。