A kind of undercoat for resistor with high temperature and humidity resistance was obtained by modifying epoxy resin with proper nano-SiO2 added at 80℃. The structure, thermal stability, humidity resistance, and morp...A kind of undercoat for resistor with high temperature and humidity resistance was obtained by modifying epoxy resin with proper nano-SiO2 added at 80℃. The structure, thermal stability, humidity resistance, and morphological characteristics of the modified epoxy resin undercoat were studied by electrical tests, infrared spectra （IR） analysis, and scanning electron microscopy （SEM）. The results show that more compact and steady inter-crosslinked network structures are formed in the modified epoxy resin undercoat added with nano-SiO2, which greatly improves the performance of modified epoxy resin undercoat. The undercoat with nano-SiO2 of about 2. 71%, kept for six months at room temperature without flocculating and aggregating, is of good stability, and the surface of painted resistor is uniform, tight and without air holes on it. The varying ratio of resistance with such undercoat painted is less than one in a thousand after high temperature and humidity resistance tests.展开更多
A kind of modified epoxy resins was obtained by condensation of epoxy resin with silicic acid tetraethyl ester（TEOS） and nano-SiO2. The reactions were performed with hydrochloric acid as a catalyst at 63 ℃. The str...A kind of modified epoxy resins was obtained by condensation of epoxy resin with silicic acid tetraethyl ester（TEOS） and nano-SiO2. The reactions were performed with hydrochloric acid as a catalyst at 63 ℃. The structure, thermal stability and morphological characteristics of the modified epoxy resins were studied through infrared spectra（FT-IR） analysis, thermogravimetric（TG） analysis and scanning electron microscopy respectively. It has been found from the IR and TG study that modified epoxy resins have greater thermal stability than epoxy resins, and its thermal stability has been improved by the formation of inter-crosslinked network structure. The modified epoxy resins exhibit heterogeneous morphology and heterogeneity increases with more TEOS feeding, which in turn confirms the formation of inter-crosslinked network structure in modified epoxy resins.展开更多
文摘A kind of undercoat for resistor with high temperature and humidity resistance was obtained by modifying epoxy resin with proper nano-SiO2 added at 80℃. The structure, thermal stability, humidity resistance, and morphological characteristics of the modified epoxy resin undercoat were studied by electrical tests, infrared spectra （IR） analysis, and scanning electron microscopy （SEM）. The results show that more compact and steady inter-crosslinked network structures are formed in the modified epoxy resin undercoat added with nano-SiO2, which greatly improves the performance of modified epoxy resin undercoat. The undercoat with nano-SiO2 of about 2. 71%, kept for six months at room temperature without flocculating and aggregating, is of good stability, and the surface of painted resistor is uniform, tight and without air holes on it. The varying ratio of resistance with such undercoat painted is less than one in a thousand after high temperature and humidity resistance tests.
文摘A kind of modified epoxy resins was obtained by condensation of epoxy resin with silicic acid tetraethyl ester（TEOS） and nano-SiO2. The reactions were performed with hydrochloric acid as a catalyst at 63 ℃. The structure, thermal stability and morphological characteristics of the modified epoxy resins were studied through infrared spectra（FT-IR） analysis, thermogravimetric（TG） analysis and scanning electron microscopy respectively. It has been found from the IR and TG study that modified epoxy resins have greater thermal stability than epoxy resins, and its thermal stability has been improved by the formation of inter-crosslinked network structure. The modified epoxy resins exhibit heterogeneous morphology and heterogeneity increases with more TEOS feeding, which in turn confirms the formation of inter-crosslinked network structure in modified epoxy resins.
