Our current efforts reveal the preparation of SiO2@TiO2 nanocomposites having different thicknesses of silica shell and the relationship to photocatalytic activity （PCA） for the photo-oxidation of naph-thalene and a...Our current efforts reveal the preparation of SiO2@TiO2 nanocomposites having different thicknesses of silica shell and the relationship to photocatalytic activity （PCA） for the photo-oxidation of naph-thalene and anthracene. The presence of SiO2 coating over TiO2 surface was demonstrated by FT-IR analysis, with peaks corresponding to Si-O-Si （1081 cm 1） and Si-O-Ti （950 cm-1） bonds observed. High-resolution transmission electron microscopy analysis confirmed the presence of SiO2 in the as- prepared nanocomposites and the amount of Si, Ti, and O was determined by energy dispersive X-ray spectroscopy analysis. Increasing the Si02 shell thickness increases the surface area of the nanocompos- ites （69-235 m2/g）, which enhances naphthalene/anthracene adsorption. However, the observed PCA trend presents an inverse correlation to the adsorption studies, where the as-prepared samples possess- ing the highest surface areas exhibited the least PCA, while catalysts having lower surface areas （among silica coated samples） displayed the highest PCA in the degradation of naphthalene and anthracene to CO2. Despite complete degradation of naphthalene and anthracene, incomplete mineralization occurred, ascribed to the formation of various intermediates, identified by GC-MS analysis.展开更多
文摘Our current efforts reveal the preparation of SiO2@TiO2 nanocomposites having different thicknesses of silica shell and the relationship to photocatalytic activity （PCA） for the photo-oxidation of naph-thalene and anthracene. The presence of SiO2 coating over TiO2 surface was demonstrated by FT-IR analysis, with peaks corresponding to Si-O-Si （1081 cm 1） and Si-O-Ti （950 cm-1） bonds observed. High-resolution transmission electron microscopy analysis confirmed the presence of SiO2 in the as- prepared nanocomposites and the amount of Si, Ti, and O was determined by energy dispersive X-ray spectroscopy analysis. Increasing the Si02 shell thickness increases the surface area of the nanocompos- ites （69-235 m2/g）, which enhances naphthalene/anthracene adsorption. However, the observed PCA trend presents an inverse correlation to the adsorption studies, where the as-prepared samples possess- ing the highest surface areas exhibited the least PCA, while catalysts having lower surface areas （among silica coated samples） displayed the highest PCA in the degradation of naphthalene and anthracene to CO2. Despite complete degradation of naphthalene and anthracene, incomplete mineralization occurred, ascribed to the formation of various intermediates, identified by GC-MS analysis.