Angle deviations between the two substrates during transient liquid phase （TLP） bonding single crystal superalloys cannot be avoided. In the present work, specimens have been prepared to investigate the influences o...Angle deviations between the two substrates during transient liquid phase （TLP） bonding single crystal superalloys cannot be avoided. In the present work, specimens have been prepared to investigate the influences of the various substrate orientations. It is found that the width of the non-isothermal solidification zone （NSZ） is linear with the square root of the isothermal solidification time. This suggests that the isothermal solidification process is B-diffusion controlled in different substrate orientation deviations. And also the width of the NSZ increases with increasing angle deviation, indicating that the isothermal solidification time needed in the TLP bonding increases with increasing orientation deviation between the two substrates.展开更多
Transient Liquid Phase Diffusion bonding (TLP bonding) is an effective method to achieve excellent joint of DD6, which is a new generation single crystal superalloy to manufacture aero-engine turbine blades. In this p...Transient Liquid Phase Diffusion bonding (TLP bonding) is an effective method to achieve excellent joint of DD6, which is a new generation single crystal superalloy to manufacture aero-engine turbine blades. In this paper, the interlayer alloys for DD6 TLP bonding were designed. The alloy foils with thickness 40 μm ~ 60 μm, width 4 mm were prepared by using a single roller rapid solidification apparatus and the TLP bonding of DD6 was conducted. Then the joint microstructure and alloying elements diffusion behaviors were analyzed. The results indicate that microstructures of interlayer alloys prepared are fine and homogeneous, the melting point range of alloys from 1070°C to 1074°C and their melting temperature interval is merely 20°C, when the chemical composition of alloys are 1.5 ~ 2.0Cr, 3.2 ~ 4.0W, 3.7 ~ 4.5Co, 2.2 ~ 3.0Al, 0.7 ~ 1.0Mo, 3.2B, remain Ni (wt%). When the welding parameters are bonding temperature 1200?C, holding time 8.0 hour and welding pressure 0.3 MPa, the compacted joints obtained and the microstructure of TLP bonding seams were similar to base metal. The bonding joint is composed of weld center zone, isothermal solidification zone and diffusion-affected zone. Within joint, the elements diffusion is sufficient and borides in the diffusion zone are fewer.展开更多
基金financially supported by the National Basic Research Program (973 Program) of China under Grant Nos. 2010CB631200 and 2010CB631206the National Natural Science Foundation of China (NSFC) under Grant Nos. 50971124, 50904059, 51071165 and 51204156
文摘Angle deviations between the two substrates during transient liquid phase （TLP） bonding single crystal superalloys cannot be avoided. In the present work, specimens have been prepared to investigate the influences of the various substrate orientations. It is found that the width of the non-isothermal solidification zone （NSZ） is linear with the square root of the isothermal solidification time. This suggests that the isothermal solidification process is B-diffusion controlled in different substrate orientation deviations. And also the width of the NSZ increases with increasing angle deviation, indicating that the isothermal solidification time needed in the TLP bonding increases with increasing orientation deviation between the two substrates.
文摘Transient Liquid Phase Diffusion bonding (TLP bonding) is an effective method to achieve excellent joint of DD6, which is a new generation single crystal superalloy to manufacture aero-engine turbine blades. In this paper, the interlayer alloys for DD6 TLP bonding were designed. The alloy foils with thickness 40 μm ~ 60 μm, width 4 mm were prepared by using a single roller rapid solidification apparatus and the TLP bonding of DD6 was conducted. Then the joint microstructure and alloying elements diffusion behaviors were analyzed. The results indicate that microstructures of interlayer alloys prepared are fine and homogeneous, the melting point range of alloys from 1070°C to 1074°C and their melting temperature interval is merely 20°C, when the chemical composition of alloys are 1.5 ~ 2.0Cr, 3.2 ~ 4.0W, 3.7 ~ 4.5Co, 2.2 ~ 3.0Al, 0.7 ~ 1.0Mo, 3.2B, remain Ni (wt%). When the welding parameters are bonding temperature 1200?C, holding time 8.0 hour and welding pressure 0.3 MPa, the compacted joints obtained and the microstructure of TLP bonding seams were similar to base metal. The bonding joint is composed of weld center zone, isothermal solidification zone and diffusion-affected zone. Within joint, the elements diffusion is sufficient and borides in the diffusion zone are fewer.