Sr2Al2SiO7：Ce^3＋, Tb^3＋ white emitting phosphors were fabricated using the sol-gel method. X-Ray Powder Diffraction （XRD） analysis confirmed the formation of Sr2Al2SiO7：Ce^3＋, Tb^3＋. Scanning Electron Microsco...Sr2Al2SiO7：Ce^3＋, Tb^3＋ white emitting phosphors were fabricated using the sol-gel method. X-Ray Powder Diffraction （XRD） analysis confirmed the formation of Sr2Al2SiO7：Ce^3＋, Tb^3＋. Scanning Electron Microscopy （SEM） observation indicated that the microstructure of the phosphor consisted of regular fine grains with an average size of about 0.5-1 μm. Luminescence properties were analyzed by measuring the photoluminescence spectra. The Ce^3＋, Tb^3＋-codoped Sr2Al2SiO7 phosphors showed four main emission peaks： one at 414 nm for Ce^3＋ and three at 482, 543, and 588 nm for Tb^3＋. The emission spectra of the samples with different doping concentrations showed that the Tb^3＋ emission was dominant because of the persistent energy transfer from Ce^3＋. The decay characteristic was better than that prepared by the solid-state process in the comparable condition. The codoped phosphor displayed long persistent white phosphorescence.展开更多
YAl3 （BO3）4： Eu^3＋ phosphors were prepared by the conventional solid state reaction. The phase structure and morphology were investigated by X-ray diffraction （XRD） and scanning electron microscope （SEM）. Dopi...YAl3 （BO3）4： Eu^3＋ phosphors were prepared by the conventional solid state reaction. The phase structure and morphology were investigated by X-ray diffraction （XRD） and scanning electron microscope （SEM）. Doping YAl3（BO3）4： Eu^3＋ phosphors with concentration of Eu^3＋ ions of 0, 2, 5, 8 and 10 mol% were studied and their luminescent properties at room temperature were discussed. The excitation spectrum of Y0.95Eu0.05Al3（BO3）4 was composed of a broad band centered at about 252 nm and a group of lines in the longer wavelength region. In the emission spectra, the peak wavelength was about 614 nm under a 252 nm UV excitation. The optimal doping concentration of Eu^3＋ ions in YAl3（BO3）4： Eu^3＋ phosphors was 8 mol%.展开更多
基金the National Natural Science Foundation of China (20376009)the Liaoning Natural Science Foundation (20032129) of China
文摘Sr2Al2SiO7：Ce^3＋, Tb^3＋ white emitting phosphors were fabricated using the sol-gel method. X-Ray Powder Diffraction （XRD） analysis confirmed the formation of Sr2Al2SiO7：Ce^3＋, Tb^3＋. Scanning Electron Microscopy （SEM） observation indicated that the microstructure of the phosphor consisted of regular fine grains with an average size of about 0.5-1 μm. Luminescence properties were analyzed by measuring the photoluminescence spectra. The Ce^3＋, Tb^3＋-codoped Sr2Al2SiO7 phosphors showed four main emission peaks： one at 414 nm for Ce^3＋ and three at 482, 543, and 588 nm for Tb^3＋. The emission spectra of the samples with different doping concentrations showed that the Tb^3＋ emission was dominant because of the persistent energy transfer from Ce^3＋. The decay characteristic was better than that prepared by the solid-state process in the comparable condition. The codoped phosphor displayed long persistent white phosphorescence.
文摘YAl3 （BO3）4： Eu^3＋ phosphors were prepared by the conventional solid state reaction. The phase structure and morphology were investigated by X-ray diffraction （XRD） and scanning electron microscope （SEM）. Doping YAl3（BO3）4： Eu^3＋ phosphors with concentration of Eu^3＋ ions of 0, 2, 5, 8 and 10 mol% were studied and their luminescent properties at room temperature were discussed. The excitation spectrum of Y0.95Eu0.05Al3（BO3）4 was composed of a broad band centered at about 252 nm and a group of lines in the longer wavelength region. In the emission spectra, the peak wavelength was about 614 nm under a 252 nm UV excitation. The optimal doping concentration of Eu^3＋ ions in YAl3（BO3）4： Eu^3＋ phosphors was 8 mol%.