热变形温度对SmCo/FeCo纳米复合磁体磁性能的影响

采用热变形技术,制备了SmCo/FeCo纳米复合磁体,研究了热变形温度对磁体磁性能的影响规律。通过X射线衍射、热重分析、扫描电子显微镜和透射电子显微镜研究了磁体的相组成和微观结构。研究结果表明:随着热变形温度从600℃升高到1000℃,Sm_(2)Co_(17)硬磁相的含量不断增加,FeCo软磁相的含量不断减少,SmCo/FeCo纳米复合磁体的矫顽力从1.54 kOe提升到5.04 kOe;饱和磁化强度先增加后降低,剩余磁化强度呈“先升高、后降低、再升高”的趋势。相对于含有部分非晶相的600℃热变形磁体,700℃热变形磁体的晶化程度更高,饱和磁化强度和剩余磁化强度在700℃达到最大值。

Temperature Dependence of Magnetic Properties of SmCo/FeCo Multilayer Films

Sm22Co78/Fe65Co35/Sm22Co78/Fe35 multilaver films were prepared by magnetron sputtering. The temperature dependence of coercivity （Hc）, remanence （Mr） and reduced remanence （Mr/Ms） has been measured. The coercivity decreases with increasing of temperature. The remanence decreases with increasing the temperature from 26 to 100℃, and then increases with continuously increasing the temperature from 100 to 150℃. The reduced remanence increases with increasing the temperature.

SmCo/FeCo双层薄膜性能的温度稳定性

用磁控溅射方法制备了Ｓｍ２２Ｃｏ７８／Ｆｅ６５Ｃｏ３５双层膜，并对其在２６℃（室温）≤Ｔ≤１５０℃范围内的磁性进行了研究。从各个温度下磁化曲线的单一性可以看到： ＳｍＣｏ硬磁层和ＦｅＣｏ软磁层两相之间存在着很强的交换耦合。矫顽力随温度的提高是单调减小的，相对变化率为４．７×１０－３；剩磁及饱和磁化强度随着温度的提高基本上是减小的；而剩磁比随温度的提高，则是单调上升的，这说明软、硬磁相之间的交换相互作用随温度的提高是单调增加的。