The effects of the Cr3C2 content and wheel speed on the amorphization behavior of the melt-spun SmCo7-x（Cr3C2）x （x=0.10-0.25） alloys were studied systematically by X-ray diffraction analysis （XRD）, differential ...The effects of the Cr3C2 content and wheel speed on the amorphization behavior of the melt-spun SmCo7-x（Cr3C2）x （x=0.10-0.25） alloys were studied systematically by X-ray diffraction analysis （XRD）, differential scanning calorimetry （DSC） and magnetic measurements. The ribbon melt-spun at lower wheel speed （20 m/s） has composite structure composed of mostly SmCo7 and a small amount of Sm2Co17R. The grain size of SmCo7 phase decreases with the increase of Cr3C2 content. With the increase of wheel speed, the XRD peaks become lower and accompanied with a broad increase in backgrounds, indicating a considerable decrease in the grain size of the SmCo7 phase. When the wheel speed increases to 40 m/s, SmCo7-x（Cr3C2）x alloys can be obtained in the amorphous state for 0.15≤x≤0.25 with intrinsic coercive Hci of 0.004-0.007 T. The DSC analysis reveals that SmCo7 phase firstly precipitates from the amorphous matrix at 650 °C, followed by the crystallization of Sm2Co17 phase at 770 °C.展开更多
基金Project (51104188) supported by the National Natural Science Foundation for Young Scholars of China
文摘The effects of the Cr3C2 content and wheel speed on the amorphization behavior of the melt-spun SmCo7-x（Cr3C2）x （x=0.10-0.25） alloys were studied systematically by X-ray diffraction analysis （XRD）, differential scanning calorimetry （DSC） and magnetic measurements. The ribbon melt-spun at lower wheel speed （20 m/s） has composite structure composed of mostly SmCo7 and a small amount of Sm2Co17R. The grain size of SmCo7 phase decreases with the increase of Cr3C2 content. With the increase of wheel speed, the XRD peaks become lower and accompanied with a broad increase in backgrounds, indicating a considerable decrease in the grain size of the SmCo7 phase. When the wheel speed increases to 40 m/s, SmCo7-x（Cr3C2）x alloys can be obtained in the amorphous state for 0.15≤x≤0.25 with intrinsic coercive Hci of 0.004-0.007 T. The DSC analysis reveals that SmCo7 phase firstly precipitates from the amorphous matrix at 650 °C, followed by the crystallization of Sm2Co17 phase at 770 °C.